Porous MoO3@SiC hallow nanosphere composite as an efficient oxidative desulfurization catalyst

A novel N‐doped MoO ₃ @SiC hollow nanosphere has been synthesized through two steps. Due to the first step, N‐doped MoO₂@C nanosphere was synthesized using the hydrothermal method and in the second step, Si‐C bonds were formed through the low‐temperature magnesiothermic method and MoO ₃ @SiC hollow nanosphere was produced. The prepared nanostructures were identified by various techniques such as IR, XRD, XPS, BET/BJH, SEM/EDS, and Raman spectroscopy. Results show that converting of C to SiC increase the surface area from 17 to 241 m²/g with remarkably decrease in pore diameter. Also, molybdenum is present in the form of MoO₂ in carbon catalyst while during magnesiothermic process, it transfers to MoO₃ form in the SiC catalyst. The synthesized products were employed as catalysts in oxidative desulfurization of model fuel. The results displayed that MoO ₃ @SiC hollow nanostructure shows a superior catalytic activity (99.9%, 40 min) compared to C support (56%, 60 min). Furthermore, the recycling of MoO₂@C catalyst shows a dramatic decrease even after the first run, while, SiC support exhibit higher stability during the stronger interaction between molybdenum catalyst and SiC support.