改性中孔分子筛SBA-16薄膜的合成及表征
引用本文:史克英,池玉娟,金效齐,徐敏,袁福龙,付宏刚. 改性中孔分子筛SBA-16薄膜的合成及表征[J]. 化学学报, 2005, 63(10): 885-890
作者姓名:史克英  池玉娟  金效齐  徐敏  袁福龙  付宏刚
作者单位:(1黑龙江大学化学化工与材料学院 物理化学实验室 哈尔滨 150080)(2哈尔滨师范大学化学系 哈尔滨 150080)
基金项目:国家自然科学基金重点项目(No.20431013),国家自然科学基金项目(No.20271019),黑龙江省博士后基金资助项目.
摘    要:在酸性条件下, 以导电玻璃(ITO)为基底合成了SBA-16分子筛膜. 所制备的SBA-16膜孔径均匀, 具有体心立方结构(属于Im3m空间群), SBA-16膜的晶胞参数为18.6 nm. TEM, SEM和XRD等技术研究表明, 加入少量的AlCl3盐于形成膜的母液并且采用RSiX3对导电玻璃基底进行处理, 能够明显改善SBA-16膜的连续性而不影响孔结构. 红外(FTIR)研究结果表明, SBA-16膜的表面硅羟基和结晶水很少, 膜很稳定. XPS研究表明, 加入少量MnCl2对SBA-16膜进行改性, 可以提高膜的导电性.

关 键 词:中孔硅  改性SBA-16薄膜  孔结构  
收稿时间:2004-07-17
修稿时间:2005-02-04

Synthesis and Characterization of Modified Mesoporous Silica SBA-16 Film
SHI, Ke-Ying,CHI, Yu-Juan,JIN, Xiao-Qi,XU, Min,YUAN, Fu-Long,FU, Hong-Gang. Synthesis and Characterization of Modified Mesoporous Silica SBA-16 Film[J]. Acta Chimica Sinica, 2005, 63(10): 885-890
Authors:SHI   Ke-Ying  CHI   Yu-Juan  JIN   Xiao-Qi  XU   Min  YUAN   Fu-Long  FU   Hong-Gang
Affiliation:(1 School of Chemistry and Materials Science, Physical Chemistry Laboratory, Heilongjiang University, Harbin 150080)(2 Department of Chemistry, Harbin Normal University, Harbin 150080)
Abstract:Continuous mesoporous silica thin films with three-dimensional (3D) accessible pore structures have been prepared by a dip-coating technique using F-127 surfactants in nonaqueous media under acidic conditions, and can be grown on ITO. Films are shown to be crystalline. XRD study displays that the mesoporous film is SBA-16 with Im3m space group symmetry, and SBA-16 film with unit cell parameter a of 18.6 nm for calcined SBA-16 film, and the mesoporous openings about 7~8 nm. Adding a little of AlCl3 into mother liquor of SBA-16, or the surface of ITO with RSiX3, would enhance the integrity of SBA-16 film but did not change the structure of SBA-16 film. The results of FTIR indicate that there was a little —OH or crystal H2O on the surface of SBA-16 film, the stability of SBA-16 film was good. The result of XPS demonstrates that, adding a little of MnCl2 into SBA-16 film, the electricity of modified SBA-16 was improved.
Keywords:mesoporous silica  modified SBA-16 film  pore structure  