Etude du polymorphisme des orthophosphates de lithium et de zinc |
| |
| Authors: | A Elfakir M Quarton B Monnaye R Bouaziz |
| |
| Institution: | (1) Laboratoire de Cristallochimie du Solide, Cnrs-Ura 1388, Tour 54, Universite P. et M. Curie, 4 Place Jussieu, 75252 Paris Cedex 05, France;(2) Laboratoire de Chimie Minerale Structurale, Universite de Rouen, BP 118, 76134 Mont-Saint-Aignan, France |
| |
| Abstract: | A partial study of the Li2O-P2O5 and ZnO-P2O5 binary diagrams led to establishment of the polymorphism of Li3PO4 and of Zn3(PO4)2. Three crystalline forms were found for Li3PO4, differring from one another only on the cation distribution at the tetrahedral sites of the almost hexagonal compact arrangement of the anions. Li3PO4 differs from the isostructural compounds Li3VO4 and Li3AsO4 in its irreversible transformation at low temperature. Zn3(PO4)2 is dimorphic, with a reversible transformation. It displays a slight non-stoichiometry through a ZnO deficiency.
Zusammenfassung Aufgrund einer teilweisen Untersuchung der binären Diagramme von Li2O-P2O5 und ZnO-P2O5 konnte der Polymorphismus der Verbindungen Li3PO4 und Zn3(PO4)2 näher beschrieben werden. Für Lithiumorthophosphat wurden drei kristalline Formen gefunden. Sie unterscheiden sich voneinander nur in der Kationenverteilung in den tetraedrischen Gebilden der fast hexagonal kompakten Anordnung der Anionen. Li3PO4 unterscheidet sich von den isostrukturellen Verbindungen Li3VO4 und Li3AsO4 durch seinen irreversiblen Übergang bei niedriger Temperatur. Zinkorthophosphat ist dimorph und zeigt eine reversiblen Umwandlung. Es weist wegen ZnO-Mangels eine geringe Abweichung von der stöchiometrischen Zusammensetzung auf.
                          —   — .   ,    .  . .  , , .
|
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|