NLO‐active maleimide copolymers with ­high glass transition temperatures

We synthesized some novel rigid NLO‐active maleimide copolymers bearing DR‐1 moieties ( PMPD , PHSD and PHND ). All copolymers exhibited high T_g's (190～197 °C), good solubilities for common solvents and excellent film‐forming properties. Dependence of film thickness on the d₃₃ value for the poled copolymer films induced by corona poling was investigated and it was demonstrated that in less than thickness of 0.3 µm decrease of the thickness gives rise to remarkable increase in the d₃₃ value. The poled copolymer films exhibited large d₃₃ values (270 × 10^?9 esu (film thickness 0.13 µm) for PMPD , 290 × 10^?9 esu (0.12 µm) for PHSD and 350 × 10^?9 esu (0.08 µm) for PHND ) as well as large r₃₃ values (51.0 pmV^?1 for PMPD and 60.4 pmV^?1 for PHND ) which are significantly large compared to the value of LiNbO₃ (31 pmV^?1) as a typical EO material. The d₃₃ values of the poled copolymers were kept constant even after standing 1000h at 80 °C, although a small decrease was observed at an initial stage. Further, the d₃₃ values did not change up to ca. 123 °C upon heating at the rate of 10 °C/min in all cases. Copyright © 2002 John Wiley & Sons, Ltd.