Optical properties of sol-gel fabricated Mn/SiO2 nanocomposites: Observation of surface plasmon resonance in Mn nanoparticles |
|
| Authors: | Oleg A Yeshchenko Igor M Dmitruk Andriy M Dmytruk |
| Institution: | a Physics Department, National Taras Shevchenko Kyiv University, 2/1 Akademik Glushkov prosp., 03127 Kyiv, Ukraine b Laboratory of Technical Ceramics and Silicates, Gomel State Technical University, 48 October prosp., 246746 Gomel, Belarus c Center for Interdisciplinary Research, Tohoku University, Aoba-ku, Aramaki Aza Aoba, 980-8578 Sendai, Japan |
| Abstract: | Manganese nanoparticles were grown in silica glass and silica film on silicon substrate by annealing of the sol-gel prepared porous silicate matrices doped with manganese nitrate. Annealing of doped porous silicate matrices was performed at various conditions that allowed to obtain the nanocomposite glasses with various content of metallic Mn. TEM of Mn/SiO2 glass indicates the bimodal size distribution of Mn nanoparticles with mean sizes of 10.5 nm and 21 nm. The absorption and photoluminescence spectra of Mn/SiO2 glasses were measured. In the absorption spectra at 300 nm (4.13 eV) we observed the band attributed to the surface plasmon resonance in Mn nanoparticles. The spectra proved the creation of Mn2+ and Mn3+ ions in silica glass as well. The absorption spectra of Mn/SiO2 glasses annealed in air prove the creation of manganese oxide Mn2O3. The measured reflection spectra of Mn/SiO2 film manifest at 240-310 nm the peculiarity attributed to surface plasmons in Mn nanoparticles. |
| Keywords: | 73 20 Mf 78 66 Sq 78 67 Bf |
| 本文献已被 ScienceDirect 等数据库收录！ | |