Synthesis of ultrahigh molecular weight poly(N‐vinylcarbazole) with a high yield using low‐temperature heterogeneous‐solution polymerization

To prepare ultrahigh molecular weight (UHMW) poly(N‐vinylcarbazole) (PVCZ) with a high conversion, I heterogeneous‐solution‐polymerized N‐vinylcarbazole (VCZ) in methanol/tertiary butyl alcohol (TBA) at 25, 35, and 45 °C with a low‐temperature initiator, 2,2′‐azobis(2,4‐dimethylvaleronitrile) (ADMVN), and I investigated the effects of the polymerization conditions on the polymerization behavior and molecular parameters of PVCZ. A low‐polymerization temperature with ADMVN, a heterogeneous system with methanol, and a low chain transfer with TBA proved to be successful in obtaining PVCZ of UHMW [weight‐average molecular weight (M_w) > 3,000,000] and high conversion (>80%) with a smaller temperature rise during polymerization but still of free‐radical polymerization by an azoinitiator. The polymerization rate of VCZ in methanol/TBA at 25 °C was proportional to the 0.97 power of the ADMVN concentration, indicating a heterogeneous nature for the polymerization. The molecular weight was higher and the molecular weight distribution was narrower with PVCZ polymerized at lower temperatures. For PVCZ produced in methanol/TBA at 25 °C with an ADMVN concentration of 0.0001 mol/mol of VCZ, an M_w of 3,230,000 was obtained, with a polydispersity index of 2.4. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 539–545, 2001