| Abstract: | A series of copolymers of N,N‐dialkyl‐N‐2‐(methoxycarbonyl)allyl allyl ammonium chloride, N,N‐dialkyl‐N‐2‐(ethoxycarbonyl)allyl allyl ammonium chloride, and N,N‐dialkyl‐N‐2‐(t‐butoxycarbonyl)allyl allyl ammonium bromide with diallyldimethylammonium chloride (DADMAC) were prepared in water at 60 °C with 2,2′‐azo‐bis(2‐amidinopropane)dihydrochloride. A strong effect of ester substituents on cyclopolymerization was observed. The methyl and ethyl ester monomers showed high cyclization efficiencies during homopolymerizations and copolymerizations. Unexpectedly, the t‐butyl ester derivatives showed high crosslinking tendencies. Water‐soluble copolymers were obtained only with a decrease in the molar fraction of t‐butyl ester monomer below 30%. Relative reactivities of the allyl‐acrylate monomers in photopolymerizations were compared with the relative reactivity of DADMAC. Allyl‐acrylate monomers were much more reactive than DADMAC; the photopolymerization rate decreased in the following order: N,N‐morpholine‐N‐2‐(t‐butoxycarbonyl)allyl allyl ammonium bromide > N,N‐piperidyl‐N‐2‐(t‐butoxycarbonyl)allyl allyl ammonium bromide > N,N‐dibutyl‐N‐2‐(ethoxycarbonyl)allyl allyl ammonium chloride > N,N‐piperidyl‐N‐2‐(ethoxycarbonyl)allyl allyl ammonium chloride ～ N,N‐morpholine‐N‐2‐(ethoxycarbonyl)allyl allyl ammonium chloride ～ N,N‐piperidyl‐N‐2‐(methoxycarbonyl)allyl allyl ammonium chloride > N‐methyl‐N‐butyl‐N‐2‐(ethoxycarbonyl)allyl allyl ammonium chloride. Intrinsic viscosities of the polymers measured in 0.09 M NaCl ranged from 1.06 to 3.20 dL/g. The highest viscosities were obtained for copolymers of the t‐butyl ester monomers with piperidine and morpholine substituents. The copolymer of the t‐butyl ester with piperidine substituent and DADMAC was hydrolyzed in acid to give a polymer with zwitterionic character. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 640–649, 2001 |