| Abstract: | Electron microscope studies are reported for crystals of linear polyethylene formed in dilute solution from very sharp low molecular weight fractions. Emphasis is placed on molecular weights in the range of 1.1 × 103 to 15.1 × 103. The dependence of the crystal habit on the crystallization temperature is very similar to that which has been found for the higher molecular weight species. However, the demarcation temperature for the crystallization of the different morphological forms is very molecular weight-dependent. The conditions under which interfacial dislocation networks form can be clearly defined. The molecular weight must be less than 3000, so that these structures are restricted to very small chain lengths. However, not all crystallization conditions within this allowable molecular weight range yield such dislocations. The formation of interfacial dislocation networks are shown to occur only under very special circumstances. Their occurrence clearly cannot be offered as evidence, as has been done in the past, for a regular, chain-folded interfacial structure. |