NOVEL TRIMETHACRYLATES: SYNTHESIS,CHARACTERIZATION, AND EVALUATION OF NEW MONOMERS FOR IMPROVED DENTAL RESTORATIVES

ABSTRACT

Two novel trimethacrylates, i.e., 1,1,1-tri-[4-(methacryloxyethoxy)-phenyl] ethane (TMPE) and 1,1,1-tri-[4-(2-methyl-2-methacryloxyethoxy)-phenyl]ethane (TMMPE), have been synthesized by reacting methacryloyl chloride with the corresponding hydroxyl intermediates. Both trimethacrylate monomers, having a low viscosity of 11.5 and 13.1 Pa.S, respectively, were blended with TEGDMA at three different weight ratios, i.e., 90/10, 70/30, and 50/50. The mixtures were made visible light-curable (VLC) by the addition of camphorquinone (0.5 wt%) and N,N-dimethyl-aminoethyl methacrylate (1.0 wt%). In addition to evaluation as cured neat resins, VLC formulations with 70% by wt. of silanated microfiller were also prepared and evaluated. The control in both cases was a VLC formulation of BisGMA/TEGDMA (70/30 and 50/50 wt/wt). These new, formulated resins have both improved physical properties and higher double bond conversion than the BisGMA control, as well as decreased linear polymerization shrinkage (LPS). The neat resin having 70/30 (wt/wt) ratio of TMPE/TEGDMA (T7T3, Table 2) exhibited a compressive strength (CS) of 496 (±51) MPa compared to the 70/30 (wt/wt) ratio of BisGMA/-TEGDMA control having 425(±27) MPa. A filled resin having a 90/10 (wt/wt) ratio of TMPE/TEGDMA exhibited a flexural strength (FS) of 122.6(±23) MPa, compared with a similar filled BisGMA/TEGDMA (70/30, wt/wt) resin exhibiting 112.7(±19) MPa. These and other results suggest that these new trimethacrylates have potential application in formulating dental composites with improved performance.