Determination of thermodynamic properties of Na2S using solid-state EMF measurements

To obtain reliable thermodynamic data for Na₂S(s), solid-state EMF measurements of the cell Pd(s)|O₂(g)|Na₂S(s), Na₂SO₄(s)|YSZ| Fe(s), FeO(s)|O₂(g)_ref| Pd(s) were carried out in the temperature range 870 < T/K < 1000 with yttria stabilized zirconia as the solid electrolyte. The measured EMF values were fitted according to the equation E_fit/V (±0.00047) = 0.63650 − 0.00584732(T/K) + 0.00073190(T/K) ln (T/K). From the experimental results and the available literature data on Na₂SO₄(s), the equilibrium constant of formation for Na₂S(s) was determined to be lg K_f(Na₂S(s)) (±0.05) = 216.28 − 4750(T/K)⁻¹ − 28.28878 ln (T/K). Gibbs energy of formation for Na₂S(s) was obtained as Δ_fG^∘(Na₂S(s))/(kJ · mol⁻¹) (±1.0) = 90.9 − 4.1407(T/K) + 0.5415849(T/K) ln (T/K). By applying third law analysis of the experimental data, the standard enthalpy of formation of Na₂S(s) was evaluated to be Δ_fH^∘(Na₂S(s), 298.15 K)/(kJ · mol⁻¹) (±1.0) = −369.0. Using the literature data for C_p and the calculated Δ_fH^∘, the standard entropy was evaluated to S^∘(Na₂S(s), 298.15 K)/(J · mol⁻¹ · K⁻¹) (±2.0) = 97.0.