Preparation, Curing Reactivity and Thermal Properties of Titanium-doped Silicone Resins |
| |
Authors: | WANG Xue-mei WU Ya-hong HAO Zhi-feng YU Jian YU Lin |
| |
Affiliation: | Faculty of Chemical Engineering and Light Industry, Guangdong University of Technology, Guangzhou 510006, P. R. China |
| |
Abstract: | Novel titanium-doped silicone resins were synthesized from low-cost silane monomers and tetrabutyl titanate as raw materials and hydrochloric acid as catalyst, with titanium element as dopant into principal chain of Si-O-Si. The resins were characterized by means of FTIR, 1H NMR and 13C NMR spectra, their thermal properties and curing properties were investigated and their corresponding films were determined. The results show that the thermal stability and storage stability of the resins were influenced by the types of silane monomers containing different carbon atomicities of organic group. The thermal stability of the titanium-doped silicone resin with a molar ratio of silane monomer B(n-propyl triethoxysilane) to silane monomer C(n-octyl triethoxysilane) being 1:1 is superior to that of the resin with a molar ratio of silane monomer B to silane monomer C being 1:3. However, the storage stability of the former is inferior to that of the latter.This work also showed that the synthesized titanium-doped silicone resins have the highest thermal stability up to 450―500 °C with an atomicity molar ratio of 1:4 of titanium to silicon in the reactants. But the best storage stability of the resin prepared from the reactants with an atomicity molar ratio of 1:6[n(Ti):n(Si)] was obtained. The effect of the type and content of curing agent on the curing properties of the resin was also studied. Moreover, thermal mechanism and curing mechanism were proposed in this work. |
| |
Keywords: | Titanium-doped silicone resin Synthesis Thermal stability Curing Mechanism |
本文献已被 CNKI 万方数据 等数据库收录! |
| 点击此处可从《高等学校化学研究》浏览原始摘要信息 |
|
点击此处可从《高等学校化学研究》下载全文 |
|