Preparation of composite hollow fiber membranes of poly(ethylene oxide)-containing polyimide and their CO2/N2 separation properties

Composite hollow fiber membranes were prepared by a dry-jet wet spinning process using a double layer spinneret. These membranes were composed of a thin and dense outer-layer of poly(ethylene oxide)-containing polyimide and a sponge-like inner layer of other polyimide. The outer layer was responsible for the separation and fabricated as thin as 1 μm. The permeation flux of CO₂, R_CO2, and the CO₂/N₂ selectivity decreased 40% and 10–20%, respectively, in a month after the membrane preparation. The steady performance was still high; for example, R_CO2=69×10⁻⁶cm³ (STP)/(cm² s cm Hg) and the selectivity of 33 at 323 K.