Self-Compacting Alkali-Activated Materials: Progress and Perspectives

Alkali-activated materials (AAMs) are considered to be alternative cementitious materials for civil infrastructures. Nowadays, efforts have been made in developing AAMs with self-compacting ability. The obtained self-compacting AAMs (SCAAMs) accomplish superior passing and filling properties as well as excellent mechanical and environmental advantages. This work critically revisits recent progresses in SCAAMs including mixture proportions, fresh properties, mechanical strength, microstructure, acid and sulfate resistance, high temperature behaviors, impact resistance and interface shear strength. To facilitate direct comparison and interpretation of data from different publications, mixture proportions were normalized in terms of the content of key reactive components from precursors and activators, and correlation with mechanical behaviors was made. Moreover, special attention was paid to current research challenges and perspectives to promote further investigation and field application of SCAAMs as advanced construction material.     

高性能混凝土的强度影响因素的探讨

讨论了混凝土的骨料级配对混凝土强度的影响，认为优良的骨料级配可以配制出工作性较好、强度较高的高性能混凝土。通过混凝土受压试件的尺寸效应，讨论了高性能混凝土需重点解决的力学性能，探讨了混凝土坍落度与流动度的关系。     

机制砂自密实混凝土研制

研制中对混凝土原材料配合比进行了优选,将优选出的混凝土进行了下述试验:坍落度、扩展度、间隙通过性、抗分离性及抗压强度等测试,用较多的数据,说明了贵州地区人工机制砂、人工碎石尽管自身条件差,但经过适当的配比,是能够配制出满足工程需要的自密实混凝土。     

泵送减水剂对尾砂-棒磨砂膏体料浆和易性与充填体强度影响研究

针对金川镍矿尾砂-棒磨砂膏体在充填管道输送中存在的堵管问题,开展了泵送减水剂对膏体的和易性与充填体强度影响试验研究.首先分析了膏体物料的物化特性和颗粒级配;然后采用金川镍矿尾砂-棒磨砂膏体充填系统工业生产中的技术参数,开展了添加不同泵送减水剂添加量的充填体强度、膏体和易性以及流变特性参数测试研究.研究结果显示,当添加1%~2%的泵送减水剂,3、7和28 d强度均有显著提高.膏体的和易性随泵送减水剂添加量的增加而提高,且浓度越高,效果越显著.当膏体浓度(质量浓度)在78%~80%的范围,膏体初始剪切应力和粘滞系数均随着泵送减水剂的增加而线性减小.结合泵送减水剂对充填体强度、膏体和易性以及流变特性影响分析,并考虑膏体充填成本与采矿经济效益,确定1%的泵送减水剂为比较合理的添加量.研究结果为金川镍矿膏体充填系统料浆制备提供重要依据,已经应用于金川矿山膏体充填的工业化生产.     

乳化沥青配方对冷再生混合料路用性能的影响

为提高乳化沥青冷再生混合料的和易性及早期强度,结合实际工程,对乳化沥青配方进行专项设计。并用现有的规范方法验证了设计配方的乳化沥青冷再生混合料的路用性能。结果表明,所设计的乳化沥青配方能够有效提高混合料和易性与早期强度。实体工程的成功应用充分说明了设计乳化沥青配方对提高冷再生混合料路用性能的重要性。     

自密实轻骨料混凝土抗离析性控制与试验方法

轻骨料混凝土容易出现因轻骨料上浮而导致的混凝土离析现象,严重影响混凝土质量.通过对混凝土基体中骨料的受力和运动状态进行分析,研究了影响混凝土骨料上浮和下沉的主要因素.并在此基础上,结合普通自密实混凝土和轻骨料混凝土的配合比设计方法,设计了2种28d抗压强度分别为42.6MPa和50.1MPa的自密实轻骨料混凝土,通过湿筛试验、粗骨料分层试验、试件断面切片试验以及观察的方法验证了所设计的自密实轻骨料混凝土具有良好的抗离析性能.     

粗磷尾矿胶结充填级配及料浆和易性规律研究

利用粗骨料进行高浓度胶结充填是矿业工程中的研究难点,也是前沿性研究课题。为高效利用粗磷尾矿以消除环境污染、土地占用以及采空区诱发的地质灾害等问题,以粗磷尾矿和粉煤灰为主要材料,首先通过SEM、ICP-MSICP-OES、XRD、激光粒度分析及其他标准测试手段对主要充填材料的物理特性、化学成分和矿物成分进行分析;然后利用Füller和Talbol最大密实度曲线理论对粗磷尾矿自然级配和不同破碎粒度磷尾矿级配进行研究;最后采用正交试验设计法及多元非线性回归法对充填料浆和易性规律进行研究。结果表明,粗磷尾矿和粉煤灰物理性能较差,但前者化学特性稳定,后者具有较强火山灰特性;-5 mm粒度破碎磷尾矿具有较优密实度;充填料浆坍落度均随胶砂比、质量浓度和水泥/粉煤灰增大而先增后减,其中胶砂比的影响程度最大;坍落扩散度均随胶砂比、水泥/粉煤灰增大而增大,随质量浓度增大而先增后减,其中质量浓度的影响程度最大;稠度均随胶砂比、质量浓度增大而减小,随水泥/粉煤灰增大而先增后减,其中质量浓度的影响程度最大,且坍落度、坍落扩散度和稠度与各因子之间存在显著非线性关系。     

A new method for circular grid analysis in the sheet metal forming test

Computer vision systems are employed to determine the major and minor lengths of deformed elliptic grids while determining a sheet metal's workability. The existing method identifies the ellipse using the least squares analysis. It suffers two drawbacks: assumptions in direct conflict with the observed real-world processes and an undesirable property of orientation dependence. For the remedy, this paper presents a new method that, in addition to achieving the desired property of orientation invariance, discards assumptions that conflict with real-world processes. The proposed method is implemented and tested using simulated and real-world data. Results are reported and compared with those obtained by the existing method.     

膨胀剂对免振捣自密实混凝土性能的影响

研究了膨胀剂掺量对自密实混凝土工作性、力学性能及体积稳定性能的影响;研究了养护制度,不同约束条件对膨胀剂在自密实混凝土中作用效果的影响。研究结果表明,无约束条件下所得到的掺膨胀剂的标养混凝土试块不能正确指导有钢筋约束的实际构件混凝土强度;无论是在干燥环境下,还是在潮湿环境下使用膨胀剂,都应通过试验慎重选择合适掺量。掺量过低,起不到补偿收缩作用,掺量过大,反而会产生负面效应。     

索塔锚固区钢纤维混凝土的工艺试验

首先通过室内试验优选出索塔锚固区纤维混凝土配合比,然后在现场泵送浇注2.44 m×1.22 m×1.22 m长方体试验块和3.4 m×1.0 m×2.3 m剪力钉试验块,最后浇注节段足尺模型.采用合理的振捣工艺,避免振捣过程中砂浆上浮和纤维外漏,从而试验块未出现开裂,外观质量良好.对优选的钢纤维混凝土进行了120 m和216 m泵送试验,系统泵压都在20 MPa左右;停机0.5h后泵压约为22 MPa,并且混凝土土出机坍落度大、和易性良好.通过泵送阻力计算,预测优选的钢纤维混凝土能达到306 m的泵送高度.