Fabrication of Dendrimer－like PAMAM Based on Silica Nanoparticles

A G 4.0 dendrimer-like poly (amido amine) (PAMAM) based on silica nanoparticles was fabricated via a divergent approach.It was built from γ-aminopropyi silica nanoparfides (APSN) core via repetitive addition of acrylate (MA) and hexylenediamine (HDA). FT-IR and EA were used to monitor the progress of dendrimer during each step. The amino group content of the resulting product increased from 0.49 to 3.72 mmol/g after the 4th generation. In addition, the percentage of grafting increased with increasing generation and reached to 65.9% after 4th generation. It was found that the resulting silica nanoparticles could be dispersed in methanol with a mean hydrodynamic particle diameter of 152.7 nm although the silica nanoparticles had agglomerated during the storage period.     

温度及pH敏感的树枝状高分子衍生物合成及药物控制释放研究

对合成的系列聚酰胺-胺型(PAMAM)树枝状高分子进行端基的羟基化和氯乙酰化两步修饰,使PAMAM最外层接上烷基氯.以修饰产物为引发剂,通过原子转移自由基引发甲基丙烯酸N,N-二甲氨基乙酯(DMAEMA)聚合得到树枝状PAMAM高分子衍生物,并对其结构用FTIR、1H-NMR和粒径分析进行了表征.紫外可见分光光度仪测定证实此高分子具有温度及pH敏感性.通过对小分子药物控制释放研究表明,此树枝状高分子衍生物通过环境pH值可有效地控制小分子药物的释放.     

小肽修饰的PAMAM树枝状化合物的生物活性

合成了甘氨酸 (Gly) 天冬氨酸 (Asp)组成的肽链Gly Asp、Gly Asp Gly Asp、Gly Asp (Gly Asp) 2 .分别将天冬氨酸及上述合成的肽链引入到聚酰胺 胺型树枝状化合物 (PAMAM)的表面 .对所得化合物进行了分子模拟 ,结果表明Gly Asp (Gly Asp) 2 肽链在PAMAM表面可形成接近于 β sheet的构象 .由实验得知 ,经Asp、Gly Asp、Gly Asp Gly Asp、Gly Asp (Gly Asp) 2 修饰的PAMAM树枝状化合物对抗坏血酸还原FeⅢ 细胞色素C(cytc)的反应有干扰作用 ,导致该反应速率下降 .这说明所合成的化合物与cytc有较好的结合能力 .特别是Gly Asp (Gly Asp) 2 修饰的PAMAM ,其与cytc的结合常数为 1 6ⅹ 1 0 5.     

PAMAM树形分子对CaCO3结晶影响的研究

研究了不同端基的聚酰胺胺(PAMAM)树形分子对CaCO₃在水溶液中结晶的影响。分别利用傅立叶变换红外光谱(FTIR)、X-射线衍射(XRD)、扫描电镜(SEM)等测试手段对样品进行了分析。结果表明:没有树形分子存在时CaCO₃是粒径为10μm的菱形方解石晶体;端基为-COONa的树形分子存在时CaCO₃则是粒径为1～2μm的球形球霰石晶体;-COOCH₃端基PAMAM树形分子存在时得到的CaCO_{3相似文献}   

Dendrimers as potential drug carriers; encapsulation of acidic hydrophobes within water soluble PAMAM derivatives

This paper describes the synthesis of three neutral water soluble poly(amidoamine) (PAMAM) dendrimer derivatives. The ability of the two larger dendrimers to bind small acidic hydrophobic molecules is reported. Spectroscopic data and pH behaviour suggested that the acidic hydrophobes were forming stable ion pairs with the dendrimer's internal, basic tertiary nitrogens. With respect to forming 1:1 and 2:1 substrate/dendrimer complexes, both of the larger dendrimers were equally efficient at binding. All dendrimer/substrate complexes were completely miscible with water in all proportions (i.e. infinitely water soluble). When the bound substrates are drug moieties, then the resulting complexes could be considered as potential drug delivery systems. Flow calorimetry demonstrated that the dendrimers were able to release their hydrophobic guests when in contact with a biological cell.     

Microcontact printed poly(amidoamine) dendrimer monolayers on silicon oxide surface

Patterning of silicon substrates with poly(amidoamine) generation 5 (PAMAM-G5) dendrimers using soft lithographic microcontact printing (μCP) is presented. μCP is shown to yield monolayers of dendrimers patterned with high level of definition over μm² to mm² areas. The patterns are stable over a period of weeks, which is attributed to the suppressed diffusion of partially charged G5 PAMAM on oxidized silicon. However, the dendrimers studied were shown to be relatively weakly bound to the substrate when subjected to lateral stresses. In aqueous conditions most of the dendrimers desorbed from the substrate.     

Convergent synthesis of PAMAM dendrimers using click chemistry of azide-functionalized PAMAM dendrons

Azide-functionalized PAMAM dendrons containing an azidopropylamine focal point were synthesized by the divergent method and applied for the construction of symmetric PAMAM-like dendrimers containing 1,2,3-triazole rings as connectors via stitching with two different multi-terminal alkynes. The stitching method was based on the click chemistry protocol, i.e., the copper-catalyzed cycloaddition reaction between an alkyne and an azide.     

PAMAM体型缩聚物的制备及其性能研究

以分子末端带有多官能度活泼端基的PAMAM等为原料 ,通过缩聚反应制备了一类新型体型缩聚物 .借助X射线光电子能谱仪 (XPS)对制备的体型缩聚物进行分析 ,利用其化学分析电子光谱 (ESCA)中碳元素价态的拟合数据判断体型缩聚反应进行的程度 ,数据表明酯基碳 (—COO)拟合峰已基本消失 ,说明其与氨基缩合反应转化为酰胺基 (—CON) ,且反应进行的比较彻底 .通过体型缩聚物在乙醇、正己烷、甲苯、氯仿、异丙醇、乙酸、甲酸、去离子水中进行溶胀试验 ,发现其在甲酸作为溶剂体系中的溶胀比出现最大值 ,根据溶度参数的意义估测体型缩聚物的溶度参数约为δ2 =2 7 6 (MJ m3) 1 2 (即甲酸的溶度参数 ) .对原料PAMAM以及制备的体型缩聚物进行DSC分析 ,发现制备体型缩聚物的玻璃化转变温度 (Tg)有了较大提高 ,从初始原料PAMAM的负值提高到 4 8℃左右 .     

新型高分子絮凝剂处理含油废水的研究

利用新型高分子絮凝剂聚酰胺胺类 (polyam idoam ine PAMAM)树形分子对油田含油废水处理进行研究 .研究表明 :该絮凝剂在用量非常低的情况下 (15～ 2 0 m g· L- 1 ) ,除油效果明显 ,废水含油量从处理前 32 0 m g· L- 1降至处理后 1mg· L- 1 ;该絮凝剂与天然高分子助凝剂 (可溶性淀粉、羧甲基纤维素等 )配合使用效果更好 ,用量可降低到 5 mg· L- 1 .     

不同代数PAMAM树形分子对CaCO3晶体的影响

以端基为-COONa的聚酰胺胺(PAMAM)树形分子为基础,研究不同代数PAMAM树形分子对CaCO3晶体的影响.分别合成了0.5代、1.5代、2.5代、3.5代、4.5代-COONa端基的PAMAM树形分子,制备了不同代数树形分子存在下的CaCO3晶体,并用IR,XRD,SEM等方法对其进行了表征.结果表明,随着树形分子代数的增加,生成趋于完善的球霰石CaCO3晶体,且CaCO3晶体颗粒的粒径呈减小趋势,由0.5代PAMAM的(6.0±0.5) μm降至4.5代PAMAM的(0.7±0.5) μm.说明端基为-COONa的PAMAM树形分子对CaCO3是一种很好的晶体改性剂和结晶抑制剂.