Electrochemical Preparation of WO_3 Nanowire Arrays

1 Results Ordered WO3 nanowires arrays have been fabricated by electrochemical deposition with anodic aluminum oxide (AAO) templates and annealing the W nanowire arrays in air at 400 ℃. The morphology and the chemical composition of WO3 nanowires arrays were characterized by Scanning Electron Microscopy (SEM),Transmission Electron Microscopy (TEM), X-ray Photoelectron Spectroscopy (XPS), and X-ray diffraction (XRD). The results show that the diameters of the WO3 nanowires are about 90 nm, which is in go...     

具有平整表面的定向纳米碳管膜的制备

为了获得表面平整的定向纳米碳管，通过化学及物理的方法将纳米碳管膜进行反转，使其原来的AAO模板底面成为新的表面，用溶液逐步去除表面的铝和氧化铝后，获得了平整的定向纳米碳管膜表面，从而可将其作为工作面使用. 还比较了5％NaOH和6%H₃PO₄＋1.8%H₂CrO₄溶液去除氧化铝的效果.     

Y2O3:Eu3+纳米线阵列的制备与表征

Y2O3:Eu3+红色荧光粉由于色纯度高、化学性质稳定和量子效率接近100%而广泛用于荧光灯和投影电视等方面.近年来,Y2O3:Eu3+的大量研究工作主要集中于纳米粉末的制备方法及其与体相材料不同的发光特性[1～3].最近,有关Y2O3:Eu3+及其稀土化合物的纳米管、纳米线和纳米带一维材料的制备成为研究热点.Wu Changfeng等[4,5]利用表面活性剂合成了Y2O3 : Eu3+纳米管.激光格位选择激发测试结果表明,Eu3+在纳米管中占据3个不同的格位,其611 nm处的红色发光峰出现了宽化.He Yu等[6]采用水热法及退火处理制备出了Y2O3:Eu3+纳米带,发现Eu3+的发射峰不仅宽化,而且出现了625 nm的新峰.Li Yadong等[7～9]采用水热法制备了稀土氧化物、硫氧化物和氢氧化物等的纳米线和纳米管,并探索了其形成机理,同时发现Y2O3S : yb3+,Er3+具有上转换的性质.     

贫水电解质体系制备多孔阳极氧化铝模板的研究

在有机溶剂为主的含草酸电解质中,研究了大孔径有序度高的阳极氧化铝(AAO)的一步法电化学制备.实验证实,电解质中水含量的降低能够有效抑制铝的电氧化速率和溶解速率,使得其氧化膜孔道的生长能够稳定进行,所得到的六方孔道排列有序度明显高于纯水溶剂制备的电解质体系下的产物.考察了水含量、有机溶剂种类以及电解质浓度对AAO模板孔道形貌的影响.结果表明,有机溶剂贫水电解质体系使得电氧化电压的选取范围比水溶液电解质体系更宽,孔径连续可调,反应条件温和.该方法适合于制备均匀大孔径的AAO模板.     

纳米级铝阳极氧化膜的形成机理及结构调整

从纳米级阳极氧化铝(AAO)膜对应用的重要性入手，主要简述AAO膜的制备、形成机理、自结构特点及结构调整方法。     

Molecular Dynamics in 1- and 2-D Confinement as Studied for the Case of Poly(Cis-1,4-Isoprene)

Broadband Dielectric Spectroscopy (BDS) is used to probe the molecular dynamics of Type A polymer, poly(cis-1,4-isoprene), when confined in the 1-dimensional (1D) exploring space of thin layers and the 2-dimensional (2D) constraining geometry of unidirectional anodic aluminum oxide (AAO) nanopores. For both cases, it was observed that the structural relaxation remains bulk-like in its mean relaxation rate, although the distribution of its relaxation times is broadened in 2D confinement. Furthermore, the fluctuation of the end-to-end vector is interrupted, with the 1D case being relatively less pronounced. By this clear-cut comparison, it is demonstrated that the effects of confinement on molecular dynamics depend, inter alia, on the dimensionality of the restricting space.     

多孔氧化铝模板催化制备定向碳纳米管阵列

Well-aligned open-ended multi-walled carbon nanotube (MWCNT) arrays were prepared via chemical vapor deposition (CVD) method in porous anodic aluminum oxide (AAO) templates without depositing any transition metals as catalyst. Effects of the CVD temperature and heat treatment were studied in detail.Well-aligned open-ended MWCNT arrays were obtained at the CVD temperature above 600 ℃; when CVD temperature is reduced to around 550 ℃, CNTs, CNFs and other structures existed at the same time; no CNTs or carbon nanofibres (CNFs) could be found as the CVD temperature is below 500 ℃, and only amorphous carbon in the porous AAO template was found. Experimental results showed that the AAO template is catalytic during the CVD process, and it has the following two effects: to catalyze thermal decomposition of acetylene and to catalyze conversion of carbon decomposed from acetylene into CNTs or CNFs. Heat treatment could improve the graphitization degree, but it might also introduce new defects.     

Fabrication and magnetic properties of Co nanowire arrays of different crystal structures

It is important to find some developing high-density magnetic recording materials in magnetic recording field with the development of information and technique, in which vertical magnetic recording is a very important way and has received considerable attention[1—3]. The vertical magnetic recording materials require high squareness, suitable coercivity, and small size of storage element[4]. Someone used nanoporous anodic aluminum oxide as templates to fabricate uniform arrays of multi magneti…     

圆盘状a-Co(OH)2的控制合成及其电化学性能

采用AAO模板及后处理方法合成了圆盘状a-Co(OH)2并研究了其电化学电容性能.在该合成方法中,先采用阳极氧化铝模板结合交流电沉积的方法获得钴纳米线,而后将其在碱液中通过溶解氧氧化生成终端产物.用红外光谱(FT-IR),X射线衍射(XRD)和场发射扫描电子显微镜(FE-SEM)表征了产物的结构和形貌;用循环伏安、恒电流充放电测试方法对其电化学性能进行了测试.此外,对圆盘状Co(OH)2的形成机理进行了初步探讨.结果表明,用此方法合成的Co(OH)2具有圆盘状形貌,属a相态,且表现出较好的电容特性.     

AAO辅助三唑亚铁纳米材料:一维限制生长和二维表面成膜及自旋转换性能

通过连续多步自组装的方式分别将三唑亚铁（SCO1）和氨基三唑亚铁（SCO2）自旋转换纳米材料生长于氧化铝模板（AAO）的孔道内和表面上。利用扫描电镜（SEM）、红外光谱（IR）、粉末X射线衍射（PXRD）、拉曼光谱（Raman）等手段对SCO1-1D+2D和SCO2-1D+2D纳米材料进行表征,SEM表明随着自组装时间的增加,球状的SCO纳米颗粒生长于AAO孔道内,并逐渐形成1D的纳米结构,而在AAO表面则形成致密均匀的SCO-2D薄膜。两种SCO-1D+2D纳米粒子都具有两步自旋行为（SCO1-1D+2D：T_c1↑=319 K,T_c1↓=313 K,T_c2↑=381 K,T_c2↓=340 K;SCO2-1D+2D：T_c1↑=181 K,T_c1↓=155 K,T_c2↑=246 K,T_c2↓=233 K）。对相应的SCO-1D和SCO-2D磁性结果表明,两步自旋转换行为的产生是由于SCO组装体形貌的差异。其中,低温区的自旋转换行为是由生长于AAO表面的SCO-2D自旋转换性能所致,而发生在更高温度的第二阶段的自旋转换行为则归因于生长于AAO孔道内的SCO-1D的自旋转换性能。