Microwave absorption properties of composite powders with low density

The composites of barium ferrite coated on hollow ceramic microspheres were prepared using sol-gel technique. The crystal structure, morphology and microwave absorption properties of composite powders with different weight ratio of microspheres were studied with XRD, EDS, FESEM and vector network analyzer. The results show that the microwave absorption properties of composite powders are greatly improved. The maximum microwave loss of composite powders reaches 31 dB with an amount of 50 wt.% microspheres, and its density is only about 1.80 g/cm³. The effect of hollow ceramic microspheres on the microwave absorption property is also discussed.     

尖晶石型软磁铁氧体纳米材料的制备研究进展

介绍了软磁铁氧体纳米材料的特性,综述了近年来具有尖晶石结构的软磁铁氧体纳米材料的制备方法。其中包括:化学共沉淀法,水热法,溶胶-凝胶法,喷雾热解法,微乳液法,相转化法,超临界法,冲击波合成法,微波场下湿法合成,爆炸法,高能球磨法,自蔓延高温合成法等。详细介绍了各种制备方法的特点,研究进展及其发展趋势。     

Preparation and microwave absorption properties of electroless Co-Ni-P coated strontium ferrite powder

A new type of Co-Ni-P coated strontium ferrite nanocomposite was prepared with electroless plating enhanced by ultrasonic wave at room temperature. The plating process was studied carefully. The morphology, crystal structure and microwave absorption properties of the Co-Ni-P coated powder were studied with field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), energy dispersive analysis of X-rays (EDX) and vector network analyzer. The results show that the strontium ferrite powder was successfully coated with Co-Ni-P alloy and possesses excellent microwave absorption properties. The maximum microwave loss of the composite powder reaches −44.12 dB. The bandwidth with the loss above −10 dB exceeds 13.8 GHz.     

NiCuZn铁氧体和银内电极的共烧行为

NiCuZn铁氧体正作为磁介质广泛地应用于低烧多层片式电感，因此有必要对其与银内电极的共烧行为进行研究。该文主要介绍NiCuZn铁氧体／银内电极多层复合体共烧过程中的烧结收缩、界面反应、扩散对介质性能的影响。尖晶石结构中存在相当数量的空位，这为银离子提供了一定的溶解度，因此在共烧过程中银对铁氧体的相组成影响较小。银对铁氧体性能的影响体现在两个方面。一方面是由于银具有相对低的烧结温度，从而在烧结过程中起到助烧剂的作用，促进致密化过程，提高烧结体的密度和磁导率；另一方面，银促使铁氧体中的铜在晶界处析出，导致晶界处应力，使磁导率降低，晶粒生长也被一定程度地抑制。     

高功率双工旋转场移相器

旋转场移相器具有移相精度高(均方根误差可小于1°)和温度稳定性好等特点,通过改进射频传输结构,可大大提高他的功率容量。利用旋转场移相器的互易特性和铁氧体圆极化器的非互易特性,设计出高功率双工旋转场移相器。其双工特性可将收/发信号分开,实现移相器和环行器的双重功能,用于天线的收发通道等场合时,可省去一个高功率环行器,结构紧凑。分析了双工旋转场移相器的工作原理,阐述了高功率应用下的设计方法,推导出了管状铁氧体的相移量计算公式,按此方法设计了实用的器件,并给出了试验数据。     

Effect of Additives on Magnetic Properties of High Frequency MnZn Power Ferrite

In keeping with the advance of more compact and more power-saving electronic equipment, the demand is increasing for smaller and more efficient switching power supply. Therefore, it is necessary to provide the adequate magnetic power ferrite materials to satisfy the demand. Such ferrite materials have to meet the following main requirement: 1) high initial permeability (μ i ); 2) high saturation magnetic induction (Bs); 3) high Curie temperature (Tc); 4) high electrical resistivity (ρ ); 5)…     

复合型铁氧体全极化器

应用耦合波理论 ,对有两组NS/N′S′四磁极磁化铁氧体中极化传输进行了分析 .在X、S波段对多种椭圆极化进行了测试 ,还完成了 0°～ 180°范围内多种线极化波测试 .最后对全极化器应用作了简单介绍 .     

ST－4型节能全自动辊道双推板窑

ＳＴ－４型全自动辊道双推板窑是为永磁铁氧体规模生产而研制的一种节能型空气烧结窑。它根据永磁铁氧体烧结的工艺要求，设计了合理的温区，使规模生产烧结成品率达９５％以上；采用辊道推板相结合的窑床形式与复合保温结构，达到了永磁铁氧体能耗１．２ｋｗｈ／ｋｇ；采用优化设计，使设备性能先进，稳定可靠。     

Mössbauer study of nanodimensional nickel ferrite – mechanochemical synthesis and catalytic properties

Iron–nickel spinel oxide NiFe₂O₄ nanoparticles have been prepared by the combination of chemical precipitation and subsequent mechanical milling. For comparison, their analogue obtained by thermal synthesis is also studied. Phase composition and structural properties of iron–nickel oxides are investigated by X-ray diffraction and Mössbauer spectroscopy. Their catalytic behavior in methanol decomposition to CO and methane is tested. An influence of the preparation method on the reduction and catalytic properties of iron–nickel samples is established.     

Effects of pH and citric acid contents on characteristics of ester-derived BaFe12O19 powder

The single domain size of BaFe₁₂O₁₉ powder with crystallite sizes less than 200 nm was produced using a citric acid precursor method. Fe³⁺ and Ba²⁺, in a molar ratio of 12, were chelated by COOH⁻ in an aqueous solution. After ethylene glycol additions, esterification, dehydration, and calcination led to the formation of ester-derived BaFe₁₂O₁₉ powder. High pH and/or high citric acid contents in the starting solution are required to complete chelate metallic ions in the solution and to form pure barium ferrite powder at 1073 K. Pure single magnetic domain BaFe₁₂O₁₉ particles of M(30 kOe)≈54 emu/g, M_r≈28 emu/g, and H_c≈3.7 kOe were produced using [citric acid]/[metallic ions]=1.5 and pH7.