Viscoelastic properties of ultrathin polycarbonate films by liquid dewetting

A liquid dewetting method for the determination of the viscoelastic properties of ultrathin polymer films has been extended to study thickness effects on the properties of ultrathin polycarbonate (PC) films. PC films with film thicknesses ranging from 4 to 299 nm were placed on glycerol at temperatures from below the macroscopic glass transition temperature (T_g) to above it with the dewetting responses being monitored. It is found that the isothermal creep results for films of the same thickness, but dewetted at different temperatures can be superposed into one master curve, which is consistent with the fact of PC being a thermorheologically simple material. Furthermore, the results show that the T_g of PC thin films is thickness dependent, but the dependence is weaker than the results for freely standing films and similar to literature data for PC films supported on rigid substrates. It was also found that the rubbery plateau region for the PC films stiffens dramatically, but still less than what has been observed for freely standing polycarbonate films. The rubbery stiffening is discussed in terms of a recently reported model that relates macroscopic segmental dynamics with the stiffening. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1559–1566     

One-pot Synthesis,Crystal Structures and Antimicrobial Activities of Two New 1,4-Disubstituted 1,2,3-Triazole-4-Carboxylates

Two new 1,4-disubstituted 1,2,3-triazoles-4-carboxylates were synthesized via click reaction. Compound 1a was synthesized by the interaction of 6-nitro-tetrazolo[1.5-a]-pyridine with ethyl propynoate at room temperature in the presence of Cu(OAc)2 as a catalyst and THF as solvent. Compound 1b was also synthesized by the same manner except that tert-butyl propionate, instead of ethyl propynoate, was used. The compounds were characterized by IR, 1H-NMR, 13C-NMR and single-crystal X-ray diffraction analysis. Compound 1a(C10H9N5O4) crystallizes in the triclinic system, space group P1 with a = 5.0894(9), b = 8.9834(13), c = 13.089(2) ?, α= 83.041(7), β= 80.256(7), γ=87.296(8)°, V = 585.24(16)?3, Z = 2, Mr = 263.22, crystal size(mm) = 0.37 × 0.20 ×0.18,(I 2σ(I)) = 8557, 2493, 1229, Rint = 0.057. Compound 1b(C12H13N5O4) crystallizes in the monoclinic system, space group P21/c with a = 6.8854(5), b = 21.783(2), c = 9.3986(8) ?,β = 93.239(4)°, V = 1407.4(2)?3, Z = 4, Mr = 291.27, crystal size(mm) = 0.38 × 0.22 × 0.20,(I 2σ(I)) = 11842, 3172, 1866, Rint = 0.047. Antimicrobial assay results showed that the title compounds display excellent activities to different bacterial and fungal strains.     

Achieving Rich and Active Alkaline Hydrogen Evolution Heterostructures via Interface Engineering on 2D 1T‐MoS2 Quantum Sheets

Large‐scale production of hydrogen from water‐alkali electrolyzers is impeded by the sluggish kinetics of hydrogen evolution reaction (HER) electrocatalysts. The hybridization of an acid‐active HER catalyst with a cocatalyst at the nanoscale helps boost HER kinetics in alkaline media. Here, it is demonstrated that 1T–MoS₂ nanosheet edges (instead of basal planes) decorated by metal hydroxides form highly active ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ heterostructures, which significantly enhance HER performance in alkaline media. Featured with rich ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ sites, the fabricated 1T–MoS₂ QS/Ni(OH)₂ hybrid (quantum sized 1T–MoS₂ sheets decorated with Ni(OH)₂ via interface engineering) only requires overpotentials of 57 and 112 mV to drive HER current densities of 10 and 100 mA cm^?2, respectively, and has a low Tafel slope of 30 mV dec^?1 in 1 m KOH. So far, this is the best performance for MoS₂‐based electrocatalysts and the 1T–MoS₂ QS/Ni(OH)₂ hybrid is among the best‐performing non‐Pt alkaline HER electrocatalysts known. The HER process is durable for 100 h at current densities up to 500 mA cm^?2. This work not only provides an active, cost‐effective, and robust alkaline HER electrocatalyst, but also demonstrates a design strategy for preparing high‐performance catalysts based on edge‐rich 2D quantum sheets for other catalytic reactions.     

Unsymmetrical Pyrene‐Fused Phthalocyanine Derivatives: Synthesis,Structure, and Properties

Novel pyrene‐fused unsymmetrical phthalocyanine derivatives 2,3,9,10,16,17‐hexakis(2,6‐dimethylphenoxy)‐22,25‐diaza(2,7‐di‐tert‐butylpyrene)[4,5]phthalocyaninato zinc complex Zn[Pc(Pz‐pyrene)(OC₈H₉)₆] ( 1 ) and 2,3,9,10‐tra(2,6‐dimethylphenoxy)‐15,18,22,25‐traza(2,7‐di‐tert‐butylpyrene)[4,5]phthalocyaninato zinc compound Zn[Pc(Pz‐pyrene)₂(OC₈H₉)₄] ( 2 ) were isolated for the first time. These unsymmetrical pyrene‐fused phthalocyanine derivatives have been characterized by a wide range of spectroscopic and electrochemical methods. In particular, the pyrene‐fused phthalocyanine structure was unambiguously revealed on the basis of single crystal X‐ray diffraction analysis of 1 , representing the first structurally characterized phthalocyanine derivative fused with an aromatic moiety larger than benzene.     

Structural and optical properties of CdTe-nanocrystals thin films grown by chemical synthesis

By mans of a chemical synthesis technique stoichiometric CdTe-nanocrystals thin films were prepared on glass substrates at 70 °C. First, Cd(OH)₂ films were deposited on glass substrates, then these films were immersed in a growing solution prepared by dissolution of Te in hydroxymethane sulfinic acid to obtain CdTe. The structural analysis indicates that CdTe thin films have a zinc-blende structure. The average nanocrystal size was 19.4 nm and the thickness of the films 170 nm. The Raman characterization shows the presence of the longitudinal optical mode and their second order mode, which indicates a good crystalline quality. The optical transmittance was less than 5% in the visible region (400–700 nm). The compositional characterization indicates that CdTe films grew with Te excess.     

Annealing temperature dependent structural and optical properties of electrodeposited CdSe thin films

Cadmium selenide films were synthesized using simple electrodeposition method on indium tin oxide coated glass substrates. The synthesized films were post annealed at 200 °C, 300 °C and 400 °C. X-ray diffraction of the films showed the hexagonal structure with crystallite size <3 nm for as deposited films and 3–25 nm for annealed films. The surface morphology of films using field emission scanning electron microscopy showed granular surface. The high resolution transmission electron microscopy of a crystallite of the film revealed lattice fringes which measured lattice spacing of 3.13 Å corresponding to (002) plane, indicating the lattice contraction effect, due to small size of CdSe nanocrystallite. The calculation of optical band gap using UV–visible absorption spectrum showed strong red-shift with increase in crystallite size, indicating to the charge confinement in CdSe nanocrystallite.