Annealing temperature dependent structural and optical properties of electrodeposited CdSe thin films

Cadmium selenide films were synthesized using simple electrodeposition method on indium tin oxide coated glass substrates. The synthesized films were post annealed at 200 °C, 300 °C and 400 °C. X-ray diffraction of the films showed the hexagonal structure with crystallite size <3 nm for as deposited films and 3–25 nm for annealed films. The surface morphology of films using field emission scanning electron microscopy showed granular surface. The high resolution transmission electron microscopy of a crystallite of the film revealed lattice fringes which measured lattice spacing of 3.13 Å corresponding to (002) plane, indicating the lattice contraction effect, due to small size of CdSe nanocrystallite. The calculation of optical band gap using UV–visible absorption spectrum showed strong red-shift with increase in crystallite size, indicating to the charge confinement in CdSe nanocrystallite.     

CdSe和ZnO量子点的拉曼光谱研究

本文介绍了用拉曼光谱研究CdSe和ZnO两种Ⅱ Ⅳ族量子点材料的结果,对拉曼峰进行了指认。观察到的光学声子峰位的移动被认为是由量子限制效应引起。     

CdSe量子点的制备与荧光特性研究

主要讨论了CdSe量子点的制备及荧光特性。CdSe量子点由化学方法制备，通过选择不同的反应时间得到不同尺度的量子点样品。用荧光方法研究了量子点样品在石英衬底和有机溶剂中的荧光特性。实验表明，这些量子点都有良好的荧光特性。还用无限深球方势阱模型分析了量子点样品的电子态，并根据荧光参数估算了量子点的尺度．各样品荧光峰具有一致的半峰宽，表明CdSe量子点的成核过程在反应开始时同时完成。     

Spectral and photochemical characteristics of CdSe nanoparticles stabilized in polymer-containing media

The optical characteristics of CdSe nanoparticles, produced in aqueous solutions and polymer films in the reaction of cadmium chloride and sodium selenosulfate, were studied. The main parameters that make it possible to vary the forbidden band width were identified. The absorption, photoluminescence, Raman, and nonstationary decolorization spectra of CdSe nanoparticles of various sizes were analyzed. It was demonstrated that under the conditions of pulsed irradiation the CdSe nanoparticles are capable of accumulating excess electrons and inducing redox transformations in components of the solution (oxygen, methylviologen, and sulfite ions). __________ Translated from Teoreticheskaya i éksperimental’naya Khimiya, Vol. 42, No. 3, pp. 150–155, May–June, 2006.     

CdSe纳米线阵列的制备及其表征(英)

通过在含有SeSO₃^2-和Cd²⁺的室温水溶液中，用模板-电沉积法在纳米孔阵列阳极氧化铝膜(AAM)模板中制备了高有序性的CdSe纳米线阵列，并对其形貌、结构和组分进行了表征。扫描电子显微镜(SEM)和透射电子显微镜(TEM)结果表明，纳米线阵列中的CdSe纳米线具有相同的长度和直径，分别对应于使用的AAM模板的厚度和孔径；X-射线衍射(XRD)和X-射线能谱(EDAX)结果表明，CdSe纳米线中Cd和Se的化学组成非常接近于1∶1，其结构为立方CdSe。另外，对模板-电沉积法制备CdSe纳米线的机理进行了讨论。     

Photocatalytic Synthesis of Composite CdSe/CdS Nanoparticles

We have shown that CdSe/CdS nanocomposites can be obtained in a photocatalytic reaction with participation of CdS nanoparticles from sodium selenosulfate. We have studied the kinetic characteristics of this process in detail and have shown that its most likely mechanism includes a step involving reaction between SeSO^3/2− anions and electrons generated in the conduction band of the CdS nanoparticles during irradiation and stabilized in traps on the semiconductor surface.__________Translated from Teoreticheskaya i Eksperimental’naya Khimiya, Vol. 41, No. 3, pp. 171–175, May–June, 2005.     

Photoelectrochemical behavior of coupled SnO2|CdSe nanocrystalline semiconductor films

A photoelectrochemical cell with a coupled SnO₂|CdSe nanocrystalline semiconductor electrode has been prepared by sequential deposition of SnO₂ and CdSe films onto an optically transparent electrode (OTE), and its photoelectrochemical behavior has been studied. The results show that the coupling of CdSe with SnO₂ leads to an improvement in the performance of OTE|SnO₂|CdSe over OTE|CdSe cells in terms of increased incident photon-to-current conversion efficiency, increased stability and smaller reversal of current. The favorable positioning of the energy bands of SnO₂ and CdSe is responsible for the above observations. Various photoelectrochemical parameters of the OTE|SnO₂|CdSe cell obtained for an incident light power of 0.31 mW cm⁻² at 470nm, are as follows: I_sc ≈ 25–30 μA cm⁻², V_oc ≈ 0.5–0.6 V, ƒƒ = 0.47 and a power conversion efficiency of about 2.25%.     

Preparation and characterization of high-specific-surface-area activated carbons from K2CO3-treated waste polyurethane

An activated carbon with high specific surface area was prepared from polyurethane foam by chemical activation with K2CO3 and the influences of carbonization temperature and impregnation ratio on the pore structure of the prepared activated carbon were investigated. It was found that the specific surface area of the activated carbon was at a maximum value (about 2800 m(2)/g) at a carbonization temperature of 1073 K and at an impregnation ratio of 1.0. It was concluded that the polyurethane foam structure was modified during impregnation by K2CO3, K2CO3 promoted charring during carbonization, and then the weight loss behavior was changed below 700 and above 1000 K, carbon in the char was consumed by K2CO3 reduction, and this led to the high specific surface area. The prepared activated carbon had a very sharp micropore size distribution, compared with the commercial activated carbon having high specific surface area. The amounts of three organic vapors (benzene, acetone, and octane) adsorbed on the prepared activated carbons was much larger than those on the traditional coconut shell AC and the same as those on the commercial activated carbon except for octane. We surmised that the high specific surface area was due to the modification of the carbonization behavior of polyurethane foam by K2CO3.     

发光反应型有机铵分子与CdSe纳米晶的组装

用巯基乙酸做稳定剂制备了水溶性CdSe纳米颗粒, 用十六烷基三甲基溴化铵(HTAB)、发光性(4-甲氧基均二苯乙烯基)二甲基乙基溴化铵 (MODAB)及末端含有双键的(4-甲基丙烯酰氧基均二苯乙烯基)二甲基乙基溴化铵(MSDAB)对该CdSe纳米颗粒进行了混合组装.通过改变三种有机分子的比例可以调控所得组装体的溶解性、聚合性及其发光性质.实验结果表明,当HTAB:MODAB:MSDAB=1:5.98～5.90:0.02～0.10(摩尔比)时,所得组装体具有较好的聚合性、溶解性和荧光性质.     

硒化镉纳米粒子与碘化三甲氨基苯基卟啉钻复合膜光学性能研究

为了探索CdSe纳米粒子合成的最佳条件及其与碘化三甲氨基苯基卟啉钴（CoTAPPI）复合膜的光学性能，采用湿化学法合成了CdSe纳米粒子；利用逐层沉积法组装了CdSe—CoTAPPI复合膜。用紫外-可见吸收光谱监测了成膜过程。利用荧光光谱比较系统地研究了聚苯乙烯磺酸钠（PSS）、放置时间、热处理、紫外光照射等条件对复合膜发光性能的影响，结果发现复合膜的发光性能相对于单一组份的CASe纳米粒子和CoTAPPI都有很大程度改变。