Hydroxylation-induced modifications of the Al2O3/NiAl(0 0 1) surface at low water vapour pressure

STM, STS, LEED and XPS data for crystalline θ-Al₂O₃ and non-crystalline Al₂O₃ ultra-thin films grown on NiAl(0 0 1) at 1025 K and exposed to water vapour at low pressure (1 × 10⁻⁷-1 × 10⁻⁵ mbar) and room temperature are reported. Water dissociation is observed at low pressure. This reactivity is assigned to the presence of a high density of coordinatively unsaturated cationic sites at the surface of the oxide film. The hydroxyl/hydroxide groups cannot be directly identify by their XPS binding energy, which is interpreted as resulting from the high BE positions of the oxide anions (O_1s signal at 532.5-532.8 eV). However the XPS intensities give evidence of an uptake of oxygen accompanied by an increase of the surface coverage by Al³⁺ cations, and a decrease of the concentration in metallic Al at the alloy interface. A value of ∼2 for the oxygen to aluminium ions surface concentration ratio indicates the formation of an oxy-hydroxide (AlO_xOH_y with x + y ∼ 2) hydroxylation product. STM and LEED show the amorphisation and roughening of the oxide film. At P(H₂O) = 1 × 10⁻⁷ mbar, only the surface of the oxide film is modified, with formation of nodules of ∼2 nm lateral size covering homogeneously the surface. STS shows that essentially the valence band is modified with an increase of the density of states at the band edge. With increasing pressure, hydroxylation is amplified, leading to an increased coverage of the alloy by oxy-hydroxide products and to the formation of larger nodules (∼7 nm) of amorphous oxy-hydroxide. Roughening and loss of the nanostructure indicate a propagation of the reaction that modifies the bulk structure of the oxide film. Amorphisation can be reverted to crystallization by annealing under UHV at 1025 K when the surface of the oxide film has been modified, but not when the bulk structure has been modified.     

A detailed analysis of the photoemission spectra of basic thioaromatic monolayers on noble metal substrates

Analysis of photoemission spectra of complex thioaromatic self-assembled monolayers (SAMs) requires the knowledge and understanding of such spectra for the basic systems. Keeping this goal in mind, synchrotron-based high-resolution X-ray photoelectron spectroscopy was used to characterize SAMs formed from the simplest thioaromatic compounds, namely thiophenol, 1,1′-biphenyl-4-thiol and 1,1′;4′,1″-terphenyl-4-thiol on evaporated Au(1 1 1) and Ag(1 1 1) substrates. The acquired S 2p and C 1s spectra were analyzed in terms of fine structure and initial and final state effects in the photoemission process. The assignment of the individual spectral features was considered in detail. Conclusions on quality and chemical and structural homogeneity of the investigated SAMs were derived.     

Investigation of chemical decomposition of CCl4 on TiO2 near room temperature

Dissociative adsorption of CCl₄ on TiO₂ at 35 °C has been studied by Fourier-transform infrared spectroscopy, X-ray photoelectron spectroscopy, and electron spin resonance. CCl₄ decompose to form CO, CO₂, and CO₃ on the surface, at such a low temperature, in which CO₂ formation is not from CO oxidation on TiO₂, but CO₃ can be produced by CO and CO₂ adsorption. The Cl generated from CCl₄ decomposition is left on the surface and bonded to titanium ions. Mineralization of CCl₄ on TiO₂ involves the lattice oxygens. Thermodynamical driving force and possible reaction routes for CO and CO₂ formation in the CCl₄ decomposition on TiO₂ are discussed.     

CuPc molecules adsorbed on Au(1 1 0)-(1 × 2): growth morphology and evolution of valence band states

We present the growth morphology, the long-range ordering, and the evolution of the valence band electronic states of ultrathin films of copper phthalocyanine (CuPc) deposited on the Au(1 1 0)-(1 × 2) reconstructed surface, as a function of the organic molecule coverage. The low energy electron diffraction patterns present a (5 × 3) reconstruction from the early adsorption stages. High-resolution UV photoelectron spectroscopy data show the disappearance of the Au surface states related to the (1 × 2) reconstruction, and the presence of new electronic features related to the molecule-substrate interaction and to the CuPc molecular states. The CuPc highest occupied molecular orbital gradually emerges in the valence band, while the interface electronic states are quenched, upon increasing the coverage.     

Mathematical topographical correction of XPS images using multivariate statistical methods

For rough heterogeneous samples, the contrast observed in XPS images may result from both changes in elemental or chemical composition and sample topography. Background image acquisition and subtraction are frequently utilized to minimize topographical effects so that images represent concentration variations in the sample. This procedure may significantly increase the data acquisition time. Multivariate statistical methods can assist in resolving topographical and chemical information from multispectral XPS images. Principal component analysis (PCA) is one method for identification of the highest correlation/variation between the images. Topography, which is common to all of the images, will be resolved in the first most significant component. The score of this component contains spatial information about the topography of the surface, whereas the loading is a quantitative representation of the topography contribution to each elemental/chemical image. The simple‐to‐use self‐modelling mixture analysis (Simplisma) method is a pure variable method that searches for the source of most differences in the data and therefore has the potential to distinguish between chemical and topographical phases in images. The mathematical background correction scheme is developed and validated by comparing results to the experimental background correction for samples with differing degrees of topography. Copyright © 2004 John Wiley & Sons, Ltd.     

Investigation of the Li1+xV3O8 electrode–organic electrolyte interface by scanning photoelectron microscopy

To investigate the formation of a solid electrolyte interface (SEI) on the Li_1+xV₃O₈ electrode surface in the thermodynamic stability range of the organic electrolyte, we applied scanning photoelectron microscopy (SPEM) to a pristine electrode and to an electrode after ten cycles. The F K-edge absorption spectrum of the cycled electrode showed that LiF forms on the electrode surface during the lithium insertion–extraction process in the Li_1+xV₃O₈/Li cell. The photoelectron spectrum for the cycled electrode showed intense spectral features corresponding to Li 1s, F 2s, F 2p, and P 2p electron signals, whereas these spectral features were of negligible intensity for the pristine electrode. The above results give strong support for the formation of an SEI that consists of LiF and compounds containing phosphorus during operation of the battery. The SPEM images also revealed that the fluorine distribution on the surface of the cycled electrode was inhomogeneous.     

超稳Y沸石制备技术对沸石铝分布的影响 Ⅱ.均匀铝分布的超稳Y沸石的制备

对水热处理后得到的USY沸石作进一步的酸处理以及采用改进的氟硅酸盐溶液骨架富硅工艺,分别得到了经XPS剖面分析证实为铝分布均匀的超稳Y沸石HAY-Ⅰ和HAY-Ⅱ。IR分析表明,在酸处理过程中从USY沸石中去掉的那部分非骨架铝类与3690cm~(-1)处羟基有关,仍残留在HAY-Ⅰ沸石中的那部分非骨架铝类与3670cm~(-1)和3600cm~(-1)处羟基有关。XRD和化学分析表明HAY-Ⅰ沸石仍含有约50％的非骨架铝类,而HAY-Ⅱ沸石则基本上不含非骨架铝类,HAY-Ⅱ沸石还显示更高的结晶保留度。DTA分析表明,HAY-Ⅰ和HAY-Ⅱ两种沸石的热稳定性均高于USY沸石。     

New interpretations of XPS spectra of nickel metal and oxides

A current interpretation of XPS spectra of Ni metal assumes that the main 6 eV satellite is due to a two hole c3d⁹4s² (c is a core hole) final state effect. We report REELS observation in AES at low voltages of losses (plasmons and inter-band transitions) corresponding to the satellite structures in Ni metal 2p spectra. The satellite near 6 eV is attributed to a predominant surface plasmon loss. A current interpretation of Ni 2p spectra of oxides and other compounds is based on charge transfer assignments of the main peak at 854.6 eV and the broad satellite centred at around 861 eV to the cd⁹L and the unscreened cd⁸ final-state configurations, respectively (L is a ligand hole). Multiplet splittings have been shown to be necessary for assignment of Fe 2p and Cr 2p spectral profiles and chemical states. The assignments of Ni 2p states are re-examined with intra-atomic multiplet envelopes applied to Ni(OH)₂, NiOOH and NiO spectra. It is shown that the free ion multiplet envelopes for Ni²⁺ and Ni³⁺ simulate the main line and satellite structures for Ni(OH)₂ and NiOOH. Fitting the NiO Ni 2p spectral profile is not as straightforward as the hydroxide and oxyhydroxide. It may involve contributions from inter-atomic, non-local electronic coupling and screening effects with multiplet structures significantly different from the free ions as found for MnO. A scheme for fitting these spectra using multiplet envelopes is proposed.     

A comparative XPS and UPS study of VOx layers on mineral TiO2(001)‐anatase supports

Four vanadium oxide layers on mineral TiO₂(001)‐anatase supports with different thickness (3–33 Å) were prepared with reactive d.c. magnetron sputtering and were extensively studied with photoelectron spectroscopy. Al Kα radiation and 150 eV synchrotron radiation were used as excitation sources. The evolution of the 2p, 3s and 3p core level line shapes of V and Ti as a function of the vanadium oxide thickness was studied, as well as the O1s and O2s core lines and the valence band. All the V2p spectra of the deposited vanadium oxide layers consist of at least 60% V⁵⁺, the rest being V⁴⁺. The V3p region is complicated by multiplet splitting, which prevents the determination of the vanadium oxidation state. The V3p multiplet splitting is different for the two excitation energies. No reduction of the titania support surface due to the vanadium oxide deposition was observed. Copyright © 2006 John Wiley & Sons, Ltd.     

Electrocatalytic activity of ordered intermetallic PtSb for methanol electro-oxidation

Ordered intermetallic PtSb had been synthesized by arc-melted and then sintering treatment. The electro-oxidation of liquid methanol on PtSb was investigated at room temperature by cyclic voltammetry and chronoamperometry. The results are compared to those at a polycrystalline platinum electrode surface. It was found that PtSb intermetallic was catalytically more active than pure platinum according to the onset potential and current density. X-ray diffraction (XRD) and XPS technologies had been used to investigate the crystal structure and electron effect.