用MgB2靶,控制直流磁控溅射工作在异常辉光放电或弧光放电状态,在SrTiO3衬底上原位一次性得到了MgB2超导薄膜,其起始转变温度为32K,零电阻温度为15K. 关键词： 高温超导体 超导薄膜 磁控溅射 二硼化镁     

基于LabVIEW的高温超导材料特性测试实验

高温超导体临界特性的测量是近代物理实验中最为经典的实验之一,本文通过使用GM制冷机,利用Lab-VIEW虚拟仪器软件和高性能采集卡,改进了传统的测量高温超导材料临界特性的实验装置.本测试系统不仅可以测量高温超导体在不同温度下的临界电流,还可以测量其失超传播特性.该实验对于学生了解超导体特性和培养严谨的科学作风十分有益.     

High-temperature expansions to fifteenth order

High-temperature series expansions of the susceptibility and second moment to 15th order are calculated for zero external field on the linear chain (LC), plane square (PSQ), simple cubic (SC), and body-centered cubic (BCC) lattices. Checks for specific models against pertinent work in the literature are detailed.     

石墨-六角氮化硼微晶混合物与水高压反应产物分析

 利用球磨法制备石墨-六角氮化硼微晶混合物，并在6.1 GPa、800~1 500 ℃条件下与水进行高压反应，以便研究用水作触媒合成B-C-N三元化合物的可能性。通过对反应产物的XRD、XPS谱分析发现：高压下随着温度的升高，反应产物中出现再结晶石墨，其晶化程度逐渐提高；但没有出现再结晶六角氮化硼，也未出现立方氮化硼。在球磨不充分条件下，石墨-六角氮化硼混合物的XRD谱没有完全弥散，它们与水高压反应时，能观察到石墨与立方氮化硼分别结晶的现象，但都没有形成B-C-N晶化结构。     

Contributions of Spin–Lattice Relaxation to the Echo Decay of Planar Cu in High-Temperature Superconductors

Measurement ofT_2G, the Gaussian component of the spin-echo envelope of planar Cu nuclei in high-temperature superconductors, gives important information about the real part of the Cu electron spin susceptibility. In the traditional picture of the planar Cu echo decay, the internuclear coupling is assumed to remain static with respect to spin–lattice relaxation and mutual exchange fluctuations. In some circumstances, however, this assumption breaks down. We calculate the internuclear corrections arising from spin–lattice relaxation to the conventional theory ofT_2Gand show thatT_2Gcan be easily corrected for these effects. We argue that mutual exchanges due to the perpendicular indirect couplings are suppressed in these materials. For YBa₂Cu₄O₈, we find a correction on the order of 10% inT_2Gand using the corrected values we find that the isotope ratio⁶³T_2G/⁶⁵T_2Gagrees with theory.     

Synthetic diamond electrodes: Photoelectrochemical behavior of vacuum-annealed undoped polycrystalline diamond films

The photocurrent and photopotential for undoped polycrystalline diamond film electrodes prepared by chemical vapor deposition and annealed in vacuum at 1500–1640°C are measured. The metal-like samples (annealed at 1630°C) have a negligible photosensitivity. Judging from the positive sign of the photopotential and the cathodic direction of the photocurrent, the material under study formally behaves as a p-type semiconductor. The photoeffects are presumably caused by structure defects, in particular, the dislocations in diamond crystallites formed close to intercrystalline boundaries during the high-temperature annealing.Translated from Elektrokhimiya, Vol. 41, No. 3, 2005, pp. 343–349.Original Russian Text Copyright © 2005 by Pleskov, Krotova, Ralchenko, Khomich, Khmelnitskii.     

The high-temperature durability of Rh-free threeway catalysts used for automoble emission control

The high-temperature durability of cordierite honeycomb Rh-free three-way catalysts (TWC) containing additives has been studied by calcining catalysts at various temperatures in the interval of 600≈1100°C. The three-way performances of these catalysts were evaluated for the reaction of carbon monoxide(CO), hydrocarbon(HC) and nitrogen oxides(NOx) at given conditions by using a fixed bed reactor. The results show that after Rh-free TWC are thermally aged in air at 1100°C for 5h and 950°C for 104 h, the TWC still have better three-way activity compared with Rh-containing TWC.     

Copper(II)–Ammonia Complexation Equilibria in Aqueous Solutions at Temperatures from 30 to 250°C by Visible Spectroscopy

The spectra of copper(II)–ammonia solutions in 2 mol-kg^–1 NH₄NO₃(aq) were recorded as a function of pH with a new UV–visible flow cell, capable of operating at conditions up to 325°C and 300 bars. Equilibrium constants for the formation of copper(II)–ammonia complexes Cu(NH₃)_n ²⁺, 1 n 4, from 30 to 150°C were determined by evolving factor analysis and nonlinear least-squares regression. Measurements at higher temperatures were limited by thermal decomposition of NH₄NO₃(aq). The formation constants of Cu(NH₃)_n ²⁺ decrease with temperature, consistent with extrapolations of literature data from measurements below 100°C. Measurements above 150°C were carried out in 0.5 mol-kg^–1 CF₃SO₃H (aq), at the very high ammonia concentrations required to avoid the precipitation of CuO(s). The spectra are consistent with Cu(NH₃)₄ ²⁺ as the predominant species, based on extrapolations of peak maxima and molar absorptivities from lower temperatures. Shifts in the spectra of Cu²⁺ and the Cu(NH₃)_n ²⁺ species to higher wavelength and increases in molar absorbance with increasing temperature are discussed in terms of the structure of the complexes.     

稀土变质热锻模具铸钢高温磨损性能的研究

研究了稀土（RE）变质热锻模具铸钢的高温磨损性能，并与热锻模具钢H13钢和3Cr2W8V钢进行对比，探讨了稀土元素的作用和热锻模具铸钢的高温磨损机理。结果表明：随着RE加入量的增加，热锻模具铸钢的磨损率先减后增，RE加入量在质量分数为0．05％时热锻模具铸钢具有最佳的高温磨损性能。RE变质热锻模其铸钢的高温耐磨性明最高于H13钢和3Cr2W8V钢。高温磨损机理为氧化磨损和氧化物的疲劳剥落，磨屑为块状的Fe2O3和Fe3O4。