玻璃陶瓷材料中Tm3+离子红外到蓝色上转换发光

系统研究了PbF2+GeO2+WO3ⅩⅣTmF3玻璃陶瓷材料中,在近红外光(1.06μm)激发下,Tm3+离子的发光特性.实验中观测到Tm3+离子的两组峰值位置分别在20920cm-1和22173cm-1的蓝色上转换发光,并证实这两组上转换发光分别与吸收三个和四个光子有关,同时建立了上转换发光的模型.为了选择最佳掺杂浓度,详细地测量了Tm3+离子峰值为20920cm-1的蓝色上转换发光强度与TmF3浓度的关系.     

Selective Propargylation of Carbonyl Compounds and Imines with Barium Reagents

A Barbier‐type regioselective propargylation of aldehydes and ketones with (3‐bromobut‐1‐ynyl)trimethylsilane has been achieved using reactive barium as a low‐valent metal in THF. Especially in the case of ketones, the corresponding homopropargylic alcohols form almost exclusively. In the reaction of α,β‐unsaturated carbonyl compounds, only 1,2‐adducts have been observed. This method is also applicable to propargylation of imines, and the corresponding homopropargylic amines are obtained regiospecifically in good yields with diastereomeric ratios of up to 87:13.     

Bi12TiO20纳米粉体的制备及其光吸收特性研究

以钛酸四丁酯和硝酸铋为原料 ,利用化学溶液分解法制备了Bi12 TiO2 0 纳米多晶粉体 .采用XRD和TEM对其结构和形貌进行了表征 .结合热重 差热 (TG DTA)分析 ,探讨了Bi12 TiO2 0 晶相的形成机理 .通过UV Vis漫反射谱的测定 ,研究了Bi12 TiO2 0 纳米晶粉体的光吸收特性 .结果显示 ,从组成为化学计量比的前驱液中可以很容易制得纯Bi12 TiO2 0 纳米晶粉体 ,该Bi12 TiO2 0 纳米晶粉体呈现了在很宽的波长范围内 (5 6 0～ 385nm )对光的吸收的特性 .     

Towards the synthesis of MAX-phase functional coatings by pulsed laser deposition

Pulsed laser deposition with a Nd:YAG laser was used to grow thin films from a pre-synthesized Ti₃SiC₂ MAX-phase formulated ablation target on oxidized Si(1 0 0) and MgO(1 0 0) substrates. The depositions were carried out in a substrate temperature range from 300 to 900 K, and the pressure in the deposition chamber ranged from vacuum (10⁻⁵ Pa) to 0.05 Pa Argon background pressure. The properties of the films have been investigated by Rutherford backscattering spectrometry for film thickness and stoichiometric composition and X-ray diffraction for the crystallinity of the films. The silicon content of the films varied with the energy density of the laser beam. To suppress especially the silicon re-sputtering from the substrate, the energy of the incoming particles must be below a threshold of 20 eV. Therefore, the energy density of the laser beam must not be too high. At constant deposition energy density the film thickness depends strongly on the background pressure. The X-ray diffraction measurements show patterns that are typical of amorphous films, i.e. no Ti₃SiC₂ related reflections were found. Only a very weak TiC(2 0 0) reflection was seen, indicating the presence of a small amount of crystalline TiC.     

Precipitation and characterization of uniform submicrometer lead titanate particles. Part II: Reaction mechanism

The chemical mechanism of the precipitation of lead titanium peroxohydroxide particles in a solution of nitrilotriacetate (NTA) complexes of lead and titanium peroxo-hydroxide is envisioned as the interaction between cations of lead hydroxide and anions of polymeric titanium peroxo-hydroxide.     

Study of archaeological ceramics by total-reflection X-ray fluorescence spectrometry: Semi-quantitative approach

Total-reflection X-ray fluorescence spectrometry has been compared with Instrumental Neutron Activation Analysis in order to test its potential application to the study of archaeological ceramics in the archaeometric field. Two direct solid non-chemical sample preparation procedures have been checked: solid sedimentation and solid chemical homogenization. For sedimentation procedure, total-reflection X-ray fluorescence allows the analysis of the elemental composition with respect to the size fraction but not the average evaluation of the composition. For solid chemical homogenization procedure, total-reflection X-ray fluorescence provides precise (from 0.8% to 27% of coefficient of variation) and accurate results (from 91% to 110% of recovery) for 15 elements (Cr, Hf, Ni, Rb, Al, Ba, Ca, K, Mn, Ti, V, Cu, Ga, Y and Fe) with an easy sample preparation process of the solid clay and without previous chemical treatment. The influence of the particle sizes has been checked by total-reflection X-ray fluorescence sample angle scans and anomalous behaviors have been found for three additional detected elements: As, Sr and Zn, which can be attributed to interference effects of the mineral grain sizes of their associated chemical phases in the total-reflection X-ray fluorescence interference region. The solid chemical homogenization procedure produces data useful for archaeological interpretation, which is briefly illustrated by a case-study. Finally, the decantation procedure data can be also useful for size chemical speciation and, consequently, for alternative environmental total-reflection X-ray fluorescence applications.     

Effect of post-metallization annealing on the ferroelectric properties of sol-gel derived PZT thin films

A series of monolithic Pt-PZT-Pt capacitors was prepared based on sol-gel derived PZT 53/47 films fired to 700 C. After deposition of top Pt electrodes, the capacitors were subjected to post-metallization annealing (PMA) temperatures of 100 C to 700 C. Dielectric and ferroelectric (FE) characterizations were performed. Increasing the PMA temperature produced lower values of spontaneous and remanent polarizations, dielectric constant and leakage currents. The observations are correlated with a proposed FE capacitor model.     

Effects of barium on the nonlinear electrical characteristics and dielectric properties of SnO2-based varistors

The effects of barium on electrical and dielectric properties of the SnO_2·Co_2O_3·Ta_2O_5 varistor system sintered at 1250℃ for 60min were investigated. It is found that barium significantly improves the nonlinear properties. The breakdown electrical field increases from 378.0 to 2834.5V/mm, relative dielectric constant (at 1kHz) falls from 1206 to 161 and the resistivity (at 1kHz) rises from 60.3 to 1146.5kΩ·cm with an increase of BaCO_3 concentration from 0mol% to 1.00mol%. The sample with 1.00mol% barium has the best nonlinear electrical property and the highest nonlinear coefficient (α=29.2). A modified defect barrier model is introduced to illustrate the grain-boundary barrier formation of barium-doped SnO_{2}-based varistors.     

Inorganic Sol-Gel Preparation of Medium Sized Microparticles of Li2TiO3 from TiCl4 as Tritium Breeding Material for Fusion Reactors

Microspheres of Li₂TiO₃ were fabricated by a classical, inorganic sol-gel process from commercially available TiCl₄. Elaborated process consists of the following main steps: (1) dissolving of TiCl₄ in concentrated aqueous HCl and addition of LiOH; (2) formation of sol emulsion in 2-ethylhexanol-1 containing the surfactant SPAN-80 (EH); (3) gelation of emulsion drops by extraction of water with partially dehydrated EH; (4) impregnation of gel to Li:Ti molar ratio MR = 2; (5) thermal treatment at 1200°C in order to receive chloride free product. This temperature can be significantly lowered (to 750°C) by dechlorination starting solution TiCl₄ by chemical treatment of the with nitric acid to form of nitrate-stabilized titania sols. Tritium release from sol-gel made Li₂TiO₃ microspheres were found very close to that observed for other traditional materials, however for the first sample process starts slightly earlier.     

氟氧化物陶瓷的多谱线上转换发光

以氧化硅、氟化铅为基质制备了Er3 :Yb3 共掺杂氟氧化物陶瓷 ,X 射线分析表明陶瓷中存在着 β PbF2 晶相 ,沉积在其中的稀土离子由于具有很低的无辐射跃迁几率而显示出良好的上转换性能。Er3 ,Yb3 离子之间存在的多种能量传递通道 ,导致稀土离子十分丰富的上转换谱线的出现。