Effect of temperature on the luminescence processes of SrAl2O4:Eu

The UV excited and persistent luminescence properties as well as thermoluminescence (TL) of Eu²⁺ doped strontium aluminates, SrAl₂O₄:Eu²⁺ were studied at different temperatures. Two luminescence bands peaking at 445 and 520 nm were observed at 20 K but only the latter at 295 K. Both Sr-sites in the lattice are thus occupied by Eu²⁺ but at room temperature efficient energy transfer occurs between the two sites. The UV excited and persistent luminescence spectra were similar at 295 K but the excitation spectra were different. Thus the luminescent centre is the same in both phenomena but excitation processes are different. Two TL peaks were observed between 50 and 250 °C in the glow curve. Multiple traps were, however, observed by preheating and initial rise methods. With longer delay times only the high temperature TL peak was observed. The persistent luminescence is mainly due to slow fading of the low temperature TL peak but the step-wise feeding process from high temperature traps is also probable.     

Microwave absorption properties of composite powders with low density

The composites of barium ferrite coated on hollow ceramic microspheres were prepared using sol-gel technique. The crystal structure, morphology and microwave absorption properties of composite powders with different weight ratio of microspheres were studied with XRD, EDS, FESEM and vector network analyzer. The results show that the microwave absorption properties of composite powders are greatly improved. The maximum microwave loss of composite powders reaches 31 dB with an amount of 50 wt.% microspheres, and its density is only about 1.80 g/cm³. The effect of hollow ceramic microspheres on the microwave absorption property is also discussed.     

Synthese und Eigenschaften von Sr3Mo1.5Zn0.5O7‐δ, einer Phase mit perowskitverwandter Schichtstruktur

Synthesis and Properties of the Layered Perovskite Phase Sr₃Mo_1.5Zn_0.5O_7‐δ The new layered perovskite phase Sr₃Mo_1.5Zn_0.5O_7‐δ was synthesized by solid state reaction using a Zn/ZnO oxygen buffer. The crystal structure was refined from X‐ray powder pattern by the Rietveld method. The compound crystallizes tetragonal in the space group I4/mmm (no. 139) with the lattice parameters a = 3.9631(3) Å, c = 20.583(1) Å. An oxygen deficiency corresponding to δ ≈ 0.25 was determinated, indicating the presence of molybdenum in mixed valence (Mo⁴⁺ and Mo⁶⁺).     

Preparation and microwave absorption properties of electroless Co-Ni-P coated strontium ferrite powder

A new type of Co-Ni-P coated strontium ferrite nanocomposite was prepared with electroless plating enhanced by ultrasonic wave at room temperature. The plating process was studied carefully. The morphology, crystal structure and microwave absorption properties of the Co-Ni-P coated powder were studied with field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), energy dispersive analysis of X-rays (EDX) and vector network analyzer. The results show that the strontium ferrite powder was successfully coated with Co-Ni-P alloy and possesses excellent microwave absorption properties. The maximum microwave loss of the composite powder reaches −44.12 dB. The bandwidth with the loss above −10 dB exceeds 13.8 GHz.     

复合型铁氧体全极化器

应用耦合波理论 ,对有两组NS/N′S′四磁极磁化铁氧体中极化传输进行了分析 .在X、S波段对多种椭圆极化进行了测试 ,还完成了 0°～ 180°范围内多种线极化波测试 .最后对全极化器应用作了简单介绍 .     

K＋－SrO－La_2O_3／ZnO催化剂上甲烷氧化偶联反应Ⅰ．催化活性和反应气中添加CO_2的影响

Ｋ＋┐ＳｒＯ┐Ｌａ２Ｏ３／ＺｎＯ催化剂上甲烷氧化偶联反应＊Ⅰ．催化活性和反应气中添加ＣＯ２的影响余林徐奕德＊＊郭燮贤（中国科学院大连化学物理研究所催化基础国家重点实验室，大连１１６０２３）关键词钾离子，氧化锶，氧化镧，氧化锌，金属氧化物催化剂，甲烷，...     

Mössbauer study of nanodimensional nickel ferrite – mechanochemical synthesis and catalytic properties

Iron–nickel spinel oxide NiFe₂O₄ nanoparticles have been prepared by the combination of chemical precipitation and subsequent mechanical milling. For comparison, their analogue obtained by thermal synthesis is also studied. Phase composition and structural properties of iron–nickel oxides are investigated by X-ray diffraction and Mössbauer spectroscopy. Their catalytic behavior in methanol decomposition to CO and methane is tested. An influence of the preparation method on the reduction and catalytic properties of iron–nickel samples is established.     

Effects of pH and citric acid contents on characteristics of ester-derived BaFe12O19 powder

The single domain size of BaFe₁₂O₁₉ powder with crystallite sizes less than 200 nm was produced using a citric acid precursor method. Fe³⁺ and Ba²⁺, in a molar ratio of 12, were chelated by COOH⁻ in an aqueous solution. After ethylene glycol additions, esterification, dehydration, and calcination led to the formation of ester-derived BaFe₁₂O₁₉ powder. High pH and/or high citric acid contents in the starting solution are required to complete chelate metallic ions in the solution and to form pure barium ferrite powder at 1073 K. Pure single magnetic domain BaFe₁₂O₁₉ particles of M(30 kOe)≈54 emu/g, M_r≈28 emu/g, and H_c≈3.7 kOe were produced using [citric acid]/[metallic ions]=1.5 and pH7.     

Effects of microstructure on the temperature dependence of relative initial permeability of NiCuZn ferrites

In the present work, ferrites with compositions of (Ni_0.27Zn_0.64Cu_x)Fe_1.98O₄ (x=0.1, 0.2) were prepared by conventional ceramic methods. The relationship between the microstructure and the temperature dependence of relative initial permeability was investigated. It was found that intergranular pores in the ferrites generate large demagnetizing fields, reducing the temperature dependence of the effective anisotropy field H_eff, and decreasing the temperature dependence of the relative initial permeability accordingly. However, intragranular pores pin the movement of domain walls. Compared with the permeability induced by domain wall motion, the permeability that resulted from the spin rotation is more sensitive to temperature. As a result, the relative initial permeability of ferrites becomes more sensitive to temperature with increasing micropores within grains.