A post curing strategy toward the feasible covalent adaptable networks in polyacrylate latex films

The implementation of covalent adaptable networks (CANs) in general resin system is becoming attractive. In this work, we propose a simple post-curing strategy based on the core-shell structured acrylate latex for the achievement on both the improved general performance and the CANs characteristics in latex films. The building to the CANs was relied on the introduction of 4,4′-diaminophenyl disulfide as the curing agent, which cured the acetoacetoxy decorated shell polymer through the ketoamine reaction. The metathesis reaction of aromatic disulfides in the crosslinking segments enabled the thermally induced dynamic behavior of the network as revealed in the stress relaxation tests by comparison with other diamine crosslinking agents without the incorporation of disulfide. The synergism of the dynamic crosslinking of the shell polymer and static crosslinking in the core polymer contributed to the improved mechanical strength (15 MPa, strain% = 250%) and the suppressed water adsorption (~1% in 24 h of soaking) of the latex film, which exhibited above 90% of recovery in both strength and strain from a cut-off film damage within 1 h at 80°C. Moreover, the cured latex film could be recycled, and 75% of the mechanical performance was regained after three fragmentation-hot-pressing cycles. These, in addition with the feasible and environmental friendly characteristics, suggest a sustainable paradigm toward the smart thermosetting latex polymers.     

Precise Synthesis and Thin Film Self-Assembly of PLLA-b-PS Bottlebrush Block Copolymers

The ability of bottlebrush block copolymers (BBCPs) to self-assemble into ordered large periodic structures could greatly expand the scope of photonic and membrane technologies. In this paper, we describe a two-step synthesis of poly(l-lactide)-b-polystyrene (PLLA-b-PS) BBCPs and their rapid thin-film self-assembly. PLLA chains were grown from exo-5-norbornene-2-methanol via ring-opening polymerization (ROP) of l-lactide to produce norbornene-terminated PLLA. Norbonene-terminated PS was prepared using anionic polymerization followed by a termination reaction with exo-5-norbornene-2-carbonyl chloride. PLLA-b-PS BBCPs were prepared from these two norbornenyl macromonomers by a one-pot sequential ring opening metathesis polymerization (ROMP). PLLA-b-PS BBCPs thin-films exhibited cylindrical and lamellar morphologies depending on the relative block volume fractions, with domain sizes of 46–58 nm and periodicities of 70–102 nm. Additionally, nanoporous templates were produced by the selective etching of PLLA blocks from ordered structures. The findings described in this work provide further insight into the controlled synthesis of BBCPs leading to various possible morphologies for applications requiring large periodicities. Moreover, the rapid thin film patterning strategy demonstrated (>5 min) highlights the advantages of using PLLA-b-PS BBCP materials beyond their linear BCP analogues in terms of both dimensions achievable and reduced processing time.     

ZnO nanowire lines and bundles: Template-deformation-guided alignment for patterned field-electron emitters

One-dimensional ZnO materials have been promising for field-emission (FE) application, but how to facially control the alignment of ZnO emitters is still a great challenge especially for patterned display application. Here, we report the fabrication of novel ZnO nanowire (NW) line and bundle arrays for patterned field-electron emitters. The effects of PS template size and heating time on the resulted ZnO nanoarrays were systematically studied. The deformation degree of PS templates was controlled and hence utilized to adjust the alignment of electrochemically deposited ZnO arrays. It was found that the length of NW lines and the density of NW bundles can effectively tuned by the PS template heating time. The optimal FE performance with turn-on electric field as low as of 4.4 V μm⁻¹ and the field-enhancement factor as high as of 1450 were achieved through decreasing the screening effect among the patterned field-electron emitters.     

Strain effects on multiferroic BiFeO3 films

The field of multiferroics has experienced a rapid progress resulting in the discovery of many new physical phenomena. BiFeO₃ (BFO) compound, which is one of the few room-temperature single-phase multiferroics, has contributed subsequently to this progress. As a result, significant review articles have been devoted specifically to this famous system. This chapter is dedicated to the strain effects on the structure stability and property changes of BFO thin films. It is a short and non-exhaustive topical overview that may be seen as an invitation for interested readers to go beyond. There is a very active and prolific research in this field and we apologize to the authors whose relevant work is not cited here. After a short introduction, we will thus review the effect of strain on BFO films by describing the consequences on the structure and the phase transitions as well as on polar, magnetic and magnetoelectric properties.     

基于DIS数字信息化系统对透光物质透光性能的研究

采用DIS数字信息化系统,对不同浓度的蓝墨水溶液在激光光源照射下的透射平均照度及照度分布图像进行实验研究,得到了平均照度值随溶液浓度变化的规律。对不同颜色塑料膜片对白炽灯光源透过照度值及照度分布图像进行实验研究得到及其相关之规律。     

Characterization of ZnO:AI films deposited by r.f.magnetron-sputtering at low temperature

Transparent conducting ZnO:AI thin films with good adhesion and Iow resistivity have been prepared on organic substrates and Coming 7059 glass substrates by r.f. magnetron-sputtering technique at Iow substrate temperature (25-210℃). Structural and photoelectric properties of the deposited films are investigated. The deposited films are polycrystalline with hexagonal structure and a preferred orientation with the c-axis perpendicular to the substrate. Only the (002) peak is observed.High quality films with resistivity as Iow as 1.0 x 10- 3Ω@ cm and 8.4 x 10- 4Ω@ cm, the average transmittance over 74% and 85% in the wavelength range of the visible spectrum have been obtained on different substrates.     

磁控溅射ZnO薄膜生长的等离子体发射光谱研究

通过反应磁控溅射过程中的等离子体发射光谱，研究了制备ZnO薄膜的沉积温度、氧气流量比例R=O₂/(O₂+Ar)对Zn和O原子发射光谱的影响，并结合ZnO薄膜的结构和物理性能，探讨了沉积温度在ZnO薄膜生长中的作用.研究结果显示：当R≥0.75%时， Zn的溅射产额随R的增加基本呈线性下降规律.当R介于10%—50%时，氧含量的变化相对平缓，有利于ZnO薄膜生长的稳定性控制.Zn原子发射光谱强度随沉积温度的变化可以分为三个阶段.当沉积温度低于250℃时，发射光谱强 关键词： ZnO 薄膜生长 反应磁控溅射 等离子体发射光谱     

(111)择优取向的Pb(Zr0.52Ti0.48)O3铁电薄膜的制备及研究

选用不同浓度的Pb(Zr_0.52Ti_0.48)O₃溶胶，用Sol-gel法在Pt/Ti/SiO₂/Si基片上沉积一层厚度不同的Pb(Zr_0.52Ti_0.48)O₃ (PZT52)过渡层，经400℃烘烤、550℃退火等程序后，再用Sol-gel法在PZT52过渡层上沉积Pb(Zr_0.52Ti_0.48)O _{关键词： PZT铁电薄膜 择优取向 过渡层 剩余极化强度}     

Au-Au2S复合纳米球壳微粒的空腔谐振及参量讨论

Au-Au2S复合纳米球壳微粒（金纳米球壳），是一种新型复合结构的纳米微粒，其结构为纳米级的Au2S介质球外包裹了一层几个纳米厚的黄金球壳。这种复合纳米球壳微粒可以被抽象为球型谐振腔。报道了它的空腔谐振吸收的实验结果，并且运用经典理论结合介观结构特征，讨论了有关Au-Au2S复合纳米球壳微粒空腔谐振吸收的一些重要参量，其中包括谐振吸收波长、品质因数、谐振能量等。另外，还讨论了金球壳的厚度对这些重要参量的影响。     

金属薄膜制备及物性测量系列实验

介绍了由模拟真空实验和“金属薄膜的制备”、“金属薄膜厚度的测量”、“金属薄膜电阻率的测量”,以及“金属薄膜生长过程的动态监测”等4个实验组成的金属薄膜制备与物性测量系列实验.这组实验与现代科学技术发展联系紧密,仪器设备可靠,操作简单,适合于普通物理实验阶段的研究性教学.