Effect of temperature on the luminescence processes of SrAl2O4:Eu

The UV excited and persistent luminescence properties as well as thermoluminescence (TL) of Eu²⁺ doped strontium aluminates, SrAl₂O₄:Eu²⁺ were studied at different temperatures. Two luminescence bands peaking at 445 and 520 nm were observed at 20 K but only the latter at 295 K. Both Sr-sites in the lattice are thus occupied by Eu²⁺ but at room temperature efficient energy transfer occurs between the two sites. The UV excited and persistent luminescence spectra were similar at 295 K but the excitation spectra were different. Thus the luminescent centre is the same in both phenomena but excitation processes are different. Two TL peaks were observed between 50 and 250 °C in the glow curve. Multiple traps were, however, observed by preheating and initial rise methods. With longer delay times only the high temperature TL peak was observed. The persistent luminescence is mainly due to slow fading of the low temperature TL peak but the step-wise feeding process from high temperature traps is also probable.     

La5Al3Ni2 – an Intermetallic Phase Observed upon Crystallization of La50Al25Ni25 Metallic Glass

The yet unknown intermetallic phase La₅Al₃Ni₂ was obtained by partially crystallizing amorphous La₅₀Al₂₅Ni₂₅ at 550 K (further heating above 600 K leads to irreversible disappearance of this phase), and its crystal structure was determined from X‐ray powder diffraction data. The crystal structure of the La₅Al₃Ni₂ phase constitutes a new structure type (Cmcm, a = 14.231Å, b = 6.914Å, c = 10.460Å, oC40) and is built from [Al₃Ni₂] chains surrounded by La atoms. In the ternary system La‐Al‐Ni La₅Al₃Ni₂ is located on the section La₅₀Al_50−nNi_n (0 ≤ n ≤ 50) with the binary compounds LaAl and LaNi as end members. Strikingly, also the crystal structures of the end members can be conceived as chain structures with Al and Ni chains surrounded by La, respectively.     

Self-organized ZnAl2O4 nanostructures grown on -sapphire

Self-organized ZnAl₂O₄ nanostructures with the appearance (in SEM) of high aspect ratio horizontal nanowires are grown on uncatalysed c-sapphire by vapour phase transport. The nanostructures grow as three equivalent crystallographic variants on c-sapphire. Raman and cathodoluminescence spectroscopy confirm that the nanostructures are not ZnO and TEM shows that they are the cubic spinel, zinc aluminate, ZnAl₂O₄, formed by the reaction of Zn and O with the sapphire substrate.     

Magnetic properties of lanthanum orthoferrite fine powders prepared by different chemical routes

Fine powders of lanthanum iron oxide, LaFeO₃, have been prepared by solid state reaction as well as sol-gel synthesis and nebulized spray pyrolysis. Structures, morphologies and magnetic susceptibility measurements of these powders have been examined. The powders prepared by all the three low-temperature routes contain nearly spherical particles with an average diameter of 40 nm. These samples show a lower Neel temperature than the powder prepared by solid state reaction besides showing much lower magnetic susceptibility at low temperatures. Dedicated to Professor C N R Rao on his 70th birthday     

K＋－SrO－La_2O_3／ZnO催化剂上甲烷氧化偶联反应Ⅰ．催化活性和反应气中添加CO_2的影响

Ｋ＋┐ＳｒＯ┐Ｌａ２Ｏ３／ＺｎＯ催化剂上甲烷氧化偶联反应＊Ⅰ．催化活性和反应气中添加ＣＯ２的影响余林徐奕德＊＊郭燮贤（中国科学院大连化学物理研究所催化基础国家重点实验室，大连１１６０２３）关键词钾离子，氧化锶，氧化镧，氧化锌，金属氧化物催化剂，甲烷，...     

配合物LaL3.H2O的合成及表征

本文以３－甲基苯甲酸为配体，合成了与三价稀土镧离子的固体配合物ＬａＬ３．Ｈ２Ｏ，并对该配合物进行了元素分析，红外光谱，ＵＶ光谱，ＴＧ－ＤＴＡ，ＨＮＭＲ等的测试与表征。该配合物属螯合双齿配位。     

Eu,Dy共掺杂SrAl2O4长余辉材料制备新工艺

活化Al-Sr合金粉末水解制备SrAl₂O₄长余辉材料的前驱体,并采用高温固相反应法制备出Eu,Dy共掺杂的SrAl₂O₄长余辉材料,对其微观结构和发光特性进行了研究。实验结果表明:前驱体中Al、Sr元素在微观状态下分布均匀,所制成的长余辉发光材料的发射主峰位于520nm附近,为典型的Eu²⁺离子4f5d-4f的特征发射,初始亮度达到18cd/m²,余辉时间长达46h。     

La（NCS）3.4.5H2O和B15C5在乙醇中的相平衡及热化学研究

采用半微量相平衡方法测定了三元体系Ｌａ（ＮＣＳ）３．４．５Ｈ２Ｏ－Ｂ１５Ｃ５－Ｃ２Ｈ５ＯＨ在２９８．１５Ｋ的溶解度，测定了各饱和溶液的折光率。     

大孔膦酸树脂吸附镧的研究

本文测定了大孔膦酸树脂对La3 的吸附容量，介质pH、温度、吸附时间等因素对吸附的影响。测得吸附速率常数K298＝7．64×10－5S－1，树脂功能基与La3 的络合比为3：1，用化学及红外光谱等方法，得到大孔磷酸树脂吸附La3 的基本参数及其机理。     

β沸石的铝化

β沸石自1988年结构被确定以来受到普遍重视,由干结构上的特殊性,G沸石既具有较强酸性又具有明显的碱性［‘,‘］．但q佛石的高硅铝比使其在化学组成上对碱性的贡献甚微,如果能降低其硅铝比,则有可能获得具有较强碱性的佛石分子筛．直接合成的o佛石,硅铝比一般在10以上．