The effects of PEA on the γ-phase PVDF crystal structure and the crystallization of PEA within the pre-existing γ-phase PVDF spherulites have been investigated by optical microscopy(OM), infrared spectroscopy(IR) and scanning electron microscopy(SEM). The results demonstrate that the γ-phase PVDF spherulites consist of the lamellae exhibiting a highly curved scroll-like morphology and develop preferentially in PEA-rich blend. With increasing PEA concentration, the scroll diameter increases and the scrolls are better separated from each other. PEA crystallizes first in the interspherulitic region and transcrystalline layer develops. Subsequently, the transcrystalline layer of PEA continues to grow within the γ-phase PVDF spherulites, e.g., in the region between the scrolls, until impinging on other PEA transcrystalline layers or spherulites. The crystallization kinetics results indicate that the growth rate of PEA crystals in the intraspherulitic region of γ-phase PVDF shows a positive correlation with content of PEA, but a negative one with the crystallization temperature of γ-phase PVDF. 相似文献
The structural properties of polycrystalline silicon films, prepared by plasma enhanced chemical vapor deposition system, with different flow rates of SiH4/SiF4 mixtures at 300 °C were investigated. This study indicates that the low hydrogen coverage on the growing surface, under optimum fluorine radicals, will be leaded to an improvement of crystallized area as compared with case of high hydrogen coverage surface. Moreover, the studies of the role of SiH4 and SiF4 radicals show that the SiH4 radicals are important in the nucleation and growth of grains. However, SiF4 radicals are effective in the structural change of grain boundaries regions and by this way, in the present system, establish the growth of grains under the dominant 〈1 1 0〉 direction. The stress investigation indicates that addition of high flow rate of SiF4 in amorphous film, results in the nearly stress free films. Finally, we found that the changes in g-value reflect the changes in the intrinsic compressive and tensile stress in the both polycrystalline and amorphous silicon films. 相似文献
This research aimed to reduce the variability on the data obtained from differential scanning calorimetric (DSC) analysis of the isothermal crystallization kinetics of cocoa butter.
To enable transformation of the DSC crystallization peak to a sigmoid crystallization curve, the DSC peak area has to be integrated. Usually, the start and end points of the crystallization peak are determined visually. The result of this visual determination appeared to be very much dependent on the operator, but also differed considerably when the same operator performed the integration several times. By proposing an objective calculation algorithm to determine the start and end points of integration, the variability caused by the operator during the integration procedure could be eliminated. Furthermore, sample preparation and the DSC heating protocol to melt the sample prior to crystallization were studied. Three heating protocols (65 °C for 15 min, 65 °C for 30 min and 80 °C for 15 min) were compared and it was shown that holding at 65 °C for 15 min was sufficient to eliminate any influence of sample history. Two different sample preparation procedures were compared and it appeared that a change in sample preparation procedure had a significant influence on the measured crystallization process. It is thus important to keep this method constant to eliminate the variability caused by it. 相似文献
With a suitable combination of ligand-stabilised nanoparticle suspension and ionic salt solutions, it is possible to produce microcrystals that are coated with nanoparticles. The self-assembly process of coating microcrystals by gold nanoparticles (NP) is mediated by the crystal lattice. This is the so-called CLAMS process - a generic process for self-organisation of nanoparticles on the surface of crystals [M. Murugeshan, D. Cunningham, J.-L. Martnez-Albertos, R. Vrcelj, B.D. Moore, Chem. Commun. (2005) 2677]. We are exploring here the structural properties of these self-assembled structures by using different imaging techniques. 相似文献
The aim of this work was to understand the crystallization process of terfenadine in solution.Cooling of saturated solutions prepared at 50 °C at different temperatures, evaporating the solvent from nearly saturated solutions at a certain temperature, and exposing ethanol solutions of terfenadine to water vapour atmosphere were the techniques used for obtaining terfenadine specimens. The characterization of these specimens was carried out by thermal microscopy, differential thermal analysis, thermogravimetry and powder X-ray diffraction. Crystalline phases, amorphous solids, and solvates were identified. For the solvents used in the present study, the crystallinity degree of terfenadine decreases from ethanol-water to ethanol and from this to methanol. Decreasing the temperature promotes the formation of amorphous solid material; at low temperatures, methanol and ethanol solvates are also formed.Desolvation, following the terfenadine aggregation process in solution accounts for the different behaviour found for the solvents and for the effect of temperature on the structure. The role of the solvent as structure-mediator is explained on the grounds of the values previously published for the enthalpy of solution of terfenadine in the solvents under study. 相似文献
We investigated iron and cobalt films with 20% carbon concentration with nanocrystalline structure. One of the aims of this work is to analyze the physical nature of high-speed structural self-assembling as often happens in explosive crystallization processes in these films. 相似文献
A simple “chimney” method was used to eliminate the voids in an arrangement of quantum dots sized 2 nm on a solid substrate, which resulted in a large well ordered superlattice of area in the order more than 1 μm2. Based on the principle of speeding up the interparticle interaction of nanoparticles to overcome the particle-substrate one, a lateral centripetal force originated from a glass tube acting as a chimney in a simple evaporation device is imposed. This method allows the packing process to be controlled in a mechanical force field, that is, with the same nanogold dispersion different patterns on a substrate—from separate dots to an ordered compact monolayer or even a multilayer structure—could be easily obtained. 相似文献