Facile non‐lithographic route to highly aligned silica nanopatterns using unidirectionally aligned polystyrene‐block‐polydimethylsiloxane films

Thin films (monolayer and bilayer) of cylinder forming polystyrene‐block‐polydimethylsiloxane (PS‐b‐PDMS) were shear aligned by the swelling and deswelling of a crosslinked PDMS pad that was physically adhered to the film during solvent vapor annealing. The nanostructures formed by self‐assembly were exposed to ultraviolet‐ozone to partially oxidize the PDMS, followed by calcination in air at 500 °C. In this process, the PS segments were fully decomposed, while the PDMS yielded silica nanostructures. The highly aligned PDMS cylinders were thus deposited as silica nanolines on the silicon substrate. Using a bilayer film, the center‐to‐center distance of these features were effectively halved from 38 to 19 nm. Similarly, by sequential shear‐alignment of two distinct layers, a rhombic array of silica nanolines was fabricated. This methodology provides a facile route to fabricating complex topographically patterned nanostructures. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1058–1064     

Effects of poly[styrene‐b‐(ethylene‐co‐butylene)‐b‐styrene] on the charge distributions of low‐density polyethylene/polystyrene blends

The effect of the triblock copolymer poly[styrene‐b‐(ethylene‐co‐butylene)‐b‐styrene] (SEBS) on the formation of the space charge of immiscible low‐density polyethylene (LDPE)/polystyrene (PS) blends was investigated. Blends of 70/30 (wt %) LDPE/PS were prepared through melt blending in an internal mixer at a blend temperature of 220 °C. The amount of charge that accumulated in the 70% LDPE/30% PS blends decreased when the SEBS content increased up to 10 wt %. For compatibilized and uncompatibilized blends, no significant change in the degree of crystallinity of LDPE in the blends was observed, and so the effect of crystallization on the space charge distribution could be excluded. Morphological observations showed that the addition of SEBS resulted in a domain size reduction of the dispersed PS phase and better interfacial adhesion between the LDPE and PS phases. The location of SEBS at a domain interface enabled charges to migrate from one phase to the other via the domain interface and, therefore, resulted in a significant decrease in the amount of space charge for the LDPE/PS blends with SEBS. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2813–2820, 2004     

Structural morphology of poly(styrene)-poly(butyl acrylate) polymer-polymer composites studied by dynamic mechanical measurements

The emulsion polymerization process allows production of polymer particles with different structural morphologies. Films obtained after coalescence keep some memory of this morphology, but large modifications can occur during coalescence. In the present case, one of the polymers, polystyrene (PS), exhibits a glass temperature (Tg) much higher than the filmification temperature (close to room temperature), while the other one, poly(butyl acrylate) (PBA), has a much lowerTg. Furthermore, it is well known that dynamic mechanical measurements can be very helpful in providing information on the morphology of polymer materials, i.e., on geometrical and topological arrangement of homopolymer domains. At first, this method was used for comparison of two types of films: i) the first one obtained from structured-core (PS)-shell (PBA) particles, ii) the second one obtained from a blend of homopolymer particles (PS and PBA). It appears that the expected core-shell particles lost their geometric structure in the second film. Second, comparison of the predicted dynamic modulus and experimental data shows that i) strong interactions exist between PS nodules unless their coalescence has occured, leading to an abnormally high modulus at room temperature, ii) after achieving their coalescence, PS forms a more or less continuous phase. Both phenomena strongly depend on the particle size and their respective volume fractions.     

Structural anisotropy in friction‐deposited layers of polystyrene

Friction‐deposited layers of atactic polystyrene (PS) on inert and OH‐grafted gold substrates were the subject of this study to establish a relationship between the friction process and the resulting anisotropy of the transferred polymer chains. We show, by using polarization‐modulation infrared reflection‐absorption spectroscopy that the deposited PS chains involve an anisotropy in which PS main backbone is rather perpendicular to the friction support, fact that is surprising when compared with the majority of polymers where the anisotropy is along the sliding direction. Moreover, our calculation of the orientation angles revealed that PS chains are more perpendicular in the transferred layers than in spin‐coated films. This particular anisotropy is probably due to a parallel reorientation of the phenyl ring on the friction support whatever the surface chemistry is. On the other hand, this study was useful to rectify the assignment of infrared bands unclearly reported in the literature. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3272–3281, 2006     

PSt-b-PEO增容PA6/PS共混体系的研究

采用动态力学方法（ＤＭＡ），形态学方法（ＳＥＭ），研究了ＰＳｔ ｂ ＰＥＯ存在下尼龙６（ＰＡ６）／聚苯乙烯（ＰＳ）共混体系的相容性．研究表明，ＰＡ６和ＰＳ的简单共混体系，分散相相畴尺寸大，相界面清晰，断裂面光滑，呈脆性断裂，相容性极差，属不相容体系．而加入少量ＰＳｔ ｂ ＰＥＯ后分散相尺寸变小，界面层变厚，界面粘结力增强，表现出韧性特征．     

Application of the essential work of fracture concept to nanostructured polymer materials

The first part of the paper deals with a critical discussion of the methodical basis of essential work of fracture (EWF) concept with respect to the specimen geometry (especially the notch depth) and application to polymers. In the second part, an in situ testing device, which combines a tensile testing machine with an optical strain-field measuring system, has successfully demonstrated possibility of characterization of fracture behaviour of polystyrene-polybutadiene block copolymers and block copolymer/homopolymer blends as examples of nanostructured polymer materials. It has been shown that knowledge of the time evolution of the strain field close to the crack tips leads to a simple verification of the basic precondition for the applicability of the EWF concept, the precondition “plastic zone coalescence-before-stable crack propagation”.     

重氮树脂与十二烷基硫酸钠相互作用研究

重氮树脂与十二烷基硫酸钠相互作用研究罗杨磊曹维孝（北京大学化学与分子工程学院北京１００８７１）关键词重氮树脂，十二烷基硫酸钠，负性ＰＳ版随着化学与生命科学领域的发展，大分子与小分子在溶液的相互作用越来越受到关注．表面活性剂因其具有自组装能力，...     

用含偶氮基的聚苯乙烯大分子引发剂合成两亲性嵌段共聚物

采用含偶氮基的聚苯乙烯预聚物（ＰＳ ＡＣＰＣ）作为引发剂，合成了苯乙烯（Ｓｔ）分别与甲基丙烯酸（ＭＡＡ）、甲基丙烯酸（β 羟丙酯）（ＨＰＭＡ）的嵌段共聚物，考察了ＰＳ ＡＣＰＣ引发第二单体的聚合反应行为，以及影响第二单体转化率和均聚物含量、共聚物组成的因素．用溶解性、凝胶渗透色谱（ＧＰＣ）、红外光谱（ＩＲ）、核磁共振（ＮＭＲ）、动态接触角（ＤＣＡ）等表征了嵌段共聚物．     

SYNTHESIS AND PROPERTIES OF POLYSTYRENE／LAPONITE NANOCOMPOSITES

Exfoliated polystyrene (PS)/laponite nanocomposites were prepared successfully. The characteristic doo1 diffraction peak of organo-laponite disappeared in the XRD patterns of nanocomposites, indicating that the laponite layers were exfoliated and the ordered crystal structure of laponite was destroyed because of the styrene polymerization. TEM observations showed that the exfoliated laponite primary particles were dispersed randomly in the PS matrix with lateral dimensions from 1 nm to 10 rim. SEM results showed that the PS/laponite nanocomposite particles were almost monodispersed spheres with the size of about 120 rim. Because of the interaction between PS and laponite nanolayers, the nanocomposites exhibited higher thermal stability and glass transition temperature when compared to pure PS.     

从溶胀平衡研究玻璃态高聚物的凝聚缠结网络

在13~15℃室温条件下对聚苯乙烯(PS)颗粒在二氧六环/水混合溶剂中的溶胀情况进行目视观察,可以看到,当减小混合溶剂二氧六环/水中的水含量时,PS颗粒从玻璃态到溶胀的玻璃态、溶胀的高弹态、流体态的转变,与PS颗粒升温时从玻璃态到高弹态、流体态的转变相对应.选定混合溶剂二氧六环/水(水6·8wt%)对一个单分散PS试样(Mw=1·68×105)在30℃进行分相平衡和溶胀平衡的测定.分相平衡是先将PS/二氧六环/水(混合溶剂水含量6·8wt%)体系加热到130℃使PS溶解成一均相溶液,然后在冷却过程中分相,在30℃达分相平衡(30天)时,浓相高分子体积浓度p″=0·304,稀相几乎为纯溶剂.从Flory-Huggins相平衡理论得出此体系的高分子-溶剂相互作用参数χ=0·63.本工作使用的单分散PS试样在选定的混合溶剂,即二氧六环/水(水6·8wt%)中,30℃时不能溶解只能溶胀,单分散PS颗粒淬冷试样(密度ρp=1·0451g/mL)到达溶胀平衡(80天)时浓相高分子体积浓度p″=0·308.而此淬冷试样经在80℃热处理100h后的老化试样(ρp=1·0470g/mL)达溶胀平衡(70天)时p″=0·312.从溶胀过程中浓相体积变化曲线可知试样经在80℃热处理过程中凝聚网络趋向于更均一,更接近热处理温度下的平衡态,试样密度增大,网络产生了新的链间凝聚,物理交联密度增大(凝聚点间分子量减小).从溶胀平衡理论并取χ=0·63(分相平衡)可得到淬冷试样的物理交联点间分子量Mc=11·6×104,老化试样的物理交联点间分子量Mc=6·9×104.实验结果说明溶胀过程及溶胀平衡的测定可以反映玻璃态高聚物中的凝聚网络结构的细节,而且非常敏感.