Mechanistic Aspects of a Highly Active Dinuclear Zinc Catalyst for the Co‐polymerization of Epoxides and CO2

The dinuclear zinc complex reported by us is to date the most active zinc catalyst for the co‐polymerization of cyclohexene oxide (CHO) and carbon dioxide. However, co‐polymerization experiments with propylene oxide (PO) and CO₂ revealed surprisingly low conversions. Within this work, we focused on clarification of this behavior through experimental results and quantum chemical studies. The combination of both results indicated the formation of an energetically highly stable intermediate in the presence of propylene oxide and carbon dioxide. A similar species in the case of cyclohexene oxide/CO₂ co‐polymerization was not stable enough to deactivate the catalyst due to steric repulsion.     

Characterizations of Tb:Zn2SiO4 films on silicon wafer prepared by sol-gel dip-coating and solid-phase reaction

Terbium-doped Zn_2SiO_4 films were successfully prepared on Si wafers by a simple sol-gel dip-coating and solid-phase reaction method of ZnO and SiO_2. X-ray diffraction (XRD) and UV－Vis absorption results revealed that films processed below 850℃ were ZnO in wurzite structure, and films processed above 850℃ were Zn_2SiO_4 in wellimite structure. Photoluminescence measurements of the Tb-doped Zn_2SiO_4 films showed two strong emission bands at 490 and 545nm. The photoluminescence lifetime was 4.6ms.     

Influence of radiation on thin ZnS-Tb films

Changes in thin zinc-sulfide films under the action of the γ-radiation of Co⁶⁰ are studied by investigating electroluminescence spectra of terbium embedded in these films as a luminescent probe. It is shown that changes in the relation of the intensities of bands, a decrease in their halfwidth and the background component, and simplification of the spectrum are observed in a short-wave region of the Tb radiation spectrum that corresponds to⁵D₃→⁷F_j transitions. The same modification of the radiation spectrum is characteristic of ZnS films whose crystalline structure is ordered in the course of thermal annealing at a temperature of 350°C. Based on the analysis of the data obtained it is inferred that irradiating the ZnS films with small radiation doses of 10⁴–10⁵ rad leads to the ordering of their crystalline structure due to the elimination of one of the types of structural defects. Institute of Physics of Semiconductors, National Academy of Sciences of Ukraine, 45, Nauka Ave., Kiev-28, 252650. Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 64, No. 3, pp. 338–341, May–June, 1997.     

生物小分子与铜锌超氧化物歧化酶相互作用的波谱学研究及其应用

本工作以ESR和NMR为主要手段,并结合其它生化方法,考察了氨基酸、核酸碱基、糖等生命基本物质,和抗坏血酸等生命必需物质与钢锌超氧化物歧化酶的相互作用,实验观测到氨基酸、核酸碱基和抗坏血酸在水溶液中可以与酶中的Cu²⁺作用而使其脱离活性部位,以小分子络合物形式游离在溶液中,同时使酶失活,脱离活性部位的Cu²⁺的比例和酶的失活程度取决于小分子配体的加入量及其与Cu²⁺的络合能力。此外,首次尝试使用ESR方法,并借助氨基酸与酶的作用,考察了铜锌超氧化物歧化酶在盐酸胍变性和热变性过程中的构象变化行为,结果表明这一方法是直观而有效的。     

The origin of the formation of cavities in galvanized coatings

The role of water‐soluble corrosion products on galvanized wires was examined. The samples used were industrial hot‐dip galvanized wires, which were exposed to the open air under all weather conditions for a relatively short time (6 and 12 months), in an urban environment close to the sea. The samples were studied by different methods, i.e. scanning electron microscopy (SEM), transmission electron microscopy (TEM), X‐ray diffraction (XRD) and optical microscopy (OM). Several phases were detected because of the galvanization procedure and the steel substrate. Furthermore, phases which were formed as a result of the reaction of zinc with the atmosphere were also detected. These were oxides like ZnO, carbonates like ZnCO₃ and hydrated Zn and Fe sulfates. Their presence influences the corrosion resistance of the wires, which finally, strongly depends on the solubility of the wires in water. The SO₄^2? compounds especially are very soluble and consequently are easily removed from the coating surface, leading to its degradation by the formation of cavities. In any case, their presence, even after a short period of exposure, implies that the coating is highly affected by the atmosphere of the modern city. Copyright © 2006 John Wiley & Sons, Ltd.     

两种以Znq2为基体的新型电致发光材料的合成与性能

以8-羟基喹啉为配体的金属配合物是一种性能优良的有机电致发光材料,其中有关8-羟基喹啉铝(Alq₃)研究已有大量报道,8-羟基喹啉锌(Znq₂)研究还有待发展。介绍了两种以Znq₂为基体的新型有机电致发光材料Znq₂(H₂O)₂和(Znq₂)₄的合成方法。用IR、XRD、TG、DTA和荧光测试方法进行表征与分析表明:Znq₂(H₂O)₂和(Znq₂)₄的玻璃化温度(T_g)分别为104.2℃和204.9℃;在161℃下Znq₂(H₂O)₂脱去水分子成为Znq₂,在361℃高温下四聚体(Znq₂)₄裂解为单体Znq₂;Znq₂(H₂O)₂和(Znq₂)₄具有很好的发光性能,在光致发光谱中λ_max分别是505,550nm。     

微分脉冲溶出伏安法同时测定食品中的锌铁锰

在1％乙二胺-0．1mol／L酒石酸钠-pH11．82 Britton—Robinson缓冲溶液体系中用微分脉冲溶出伏安法同时测定锌、铁、锰三种微量元素。它们的峰电位分别为-1184，-1392和-1456mV(vs．Ag/AgCl)；线性范围分别为：0.001—0.015，0．005—0．05和0．04—0．7μg／mL，最低检出浓度分别为0．0007，0．0014和0．0193μg／mL。本法操作简便、准确、灵敏度较高，用于食品中这三种元素的分析，结果令人满意。     

Crystallographic report: Crystal structure of tetra(4‐methyl‐5‐imidazole‐carboxyaldehyde)zinc(II) diperchlorate

The central zinc(II) atom in the title complex is tetrahedrally coordinated by four nitrogen atoms derived from 4‐methyl‐5‐imidazolecarboxyaldehyde ligands with Zn? N in the range 2.007(3) to 2.026(4) Å. Copyright © 2003 John Wiley & Sons, Ltd.     

Crystallographic report: Crystal structure of a one‐dimensional zinc(II) coordination polymer containing 4,4′‐biphenyldicarboxylate hemihydrate

A one‐dimensional zinc(II) coordination polymer has been constructed from zinc(II), 4,4′‐biphenyldicarboxylate and pyridine in which each zinc(II) atom is coordinated by two pyridine ligands and two monodentate 4,4′‐biphenyldicarboxylate ligands that define a distorted tetrahedral geometry. Copyright © 2003 John Wiley & Sons, Ltd.