Desorption of carboxylates and phosphonates from galvanized steel: Towards greener lubricants

This paper studies the removal of chemisorbed carboxylates and phosphonates from TiO₂-coated galvanized steel using NaOH_(aq). XPS and FTIR data show that NaOH_(aq) is effective at desorbing these species and so is an alternative to gas phase processes (eg, plasma cleaning). Tribological investigations show that NaOH_(aq)-treated surfaces show reduced friction and wear, relative to the “as-received” galvanized steel. This is ascribed to carbonate (present as an impurity in NaOH) that adsorbs to the surface of the substrate during NaOH_(aq) immersion. Carbonate removal through sonication in water generates surfaces that show friction similar to “as-received” galvanized steel. This work is useful in areas (eg, automotive manufacturing), where the effective removal of lubricants following tribological contact is key to subsequent paint adhesion.     

二硫代钼酸锌高温稳定性及其润滑性能的研究

在实验室中全成了二硫代钼酸锌粉,并考察了其作为固体润滑剂的高温摩擦学性能,同时采用热重分析对其热稳定性进行了评价,采用Ｘ射线光电子能谱分析了摩擦表面典型元素的化学状态。结果表明,二硫代钼酸锌在空气中的第一分解温度为２４９．８℃,摩擦磨损试验结果表明,二硫代钼酸锌作为固体润滑剂在室温到５００℃温度范围内具有较代的摩擦系数,但摩擦系数随温度的升高而增大。磨损表面Ｘ射线光电子能谱分析结果表明,该固体润滑     

植物油酸新戊二醇对苯二甲酸复合酯的合成及性能

用新戊二醇(NPG)和对苯二甲酰氯(TPA)反应生成“低聚物”中间体,当n(NPG)/n(TPA)由2.4增加至3.0时,中间体的聚合度(m)在3.5~1.45之间,收率75.5%。再将中间体与油酸、菜籽油酸进行酯化得到复合酯,收率88.5%。结果表明,复合酯的粘度随着分子量的增大而增大,粘度指数大于125,凝点低于－27℃,氧化稳定性随分子量的增大而提高,生物降解率＞70%,最大无卡咬负荷(PB)为784N,磨斑直径0.41mm,热分解温度＞250 ℃,因此植物油酸新戊二醇对苯二甲酸复合酯是性能良好的绿色润滑剂。     

Novel emulsion graft copolymerization onto the silylmethyl group of poly(dimethylsiloxane)

The influence of radical initiators upon the emulsion graft copolymerization of styrene and acrylonitrile onto poly(dimethylsiloxane) (PDMS) was studied. As initiators, a series of peroxides and hydroperoxides were coupled with ferrous sulfate, among which the tert-butyl peroxylaurate system gave the highest grafting efficiency (30%). The tert-butyl peroxylaurate initiator fulfills the criteria for efficient radical grafting by generating only the tert-butoxy radical, which is reluctant to form a carbon radical via β-scission, being highly hydrophobic, and not carrying a tertiary hydrogen that may be abstracted by a radical. ¹³C-NMR analysis of the products showed that the grafting occurred on the silylmethyl groups of PDMS to give 10–25 grafts per polymer and graft ratio in the range 44–140%. The PDMS graft copolymers thus obtained could be used as surface-modifying agents to improve the lubricity and water-repellency of ABS [poly(styrene-co-acrylonitrile)-graft-polybutadiene]. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35: 2607–2617, 1997     

油酸新戊二醇己二酸复合酯的合成及其润滑性能

新戊二醇(NPG)和己二酸(AA)通过酯化反应合成了"低聚物"中间体(1).当n(NPG):n(AA)＝1.5～3.0时,1的聚合度(m)在4.34～2.10,收率97%.以对甲苯磺酸为催化剂,甲苯为带水剂,1与油酸进行酯化得到复合酯(2),收率83%～89%.测定了2的黏度、黏度指数、氧化稳定性、生物降解率、摩擦磨损性能和热稳定性.结果表明,2的黏度和氧化稳定性随着m的增大而增大,100 ℃时的黏度在18.3 mm~2·s~(-1)～30.1 mm~2·s~(-1),黏度指数均超过200,凝点低于-43 ℃,生物降解率＞96%,最大无卡咬负荷(P_B)为784 N,磨斑直径0.40 mm,热分解温度＞300 ℃.1和2的结构经IR表征.     

离子液体润滑性及导电能力研究进展

具有优异润滑性能的离子液体已经引起科研工作者的广泛关注,本文中介绍了离子液体的作为润滑剂的摩擦学性能,同时对离子液体的导电能力进行了分析.重点介绍了近年来离子液体作为润滑脂导电材料在润滑脂中的导电能力和摩擦学性能.并指出离子液体作为润滑脂导电添加剂仍需解决的问题及未来的研究趋势.     

非离子表面活性剂体系层状液晶中硫化锌纳米颗粒的抗磨性

利用层状液晶中溶剂厚度的限定性,在ＴｒｉｔｏｎＸ－１００／Ｃ１０Ｈ２１ＯＨ／Ｈ２Ｏ体系层状液晶中,分别各以０．１ｍｏｌ／Ｌ的Ｚｎ（ＣＨ３ＣＯＯ）２和Ｎａ２Ｓ水溶液代替组分水制备出粒径约为１０ｎｍＺｎＳ颗粒,并对层状液晶中ＺｎＳ纳米颗粒的抗磨性能进行了研究,结果表明,ＺｎＳ纳米颗粒能提高ＴｒｉｔｏｎＸ－１０Ｃ１０Ｈ２１ＯＨ／Ｈ２Ｏ体系层状液晶的抗磨性,但对极压性能无影响。     

水溶性聚合物-烷基聚乙二醇酯磷酸锌盐的摩擦性能

合成了三种烷基聚乙二醇酯磷酸锌水溶性润滑添加剂，研究表明，分子中聚乙二醇作为水溶性基团，分子量以1000为宜，分子量大小，聚合物在水中溶解性差，影响其润滑性能；分子量过大，导致单位重量聚合物中疏水基团含量相对减少，同样影响其润滑性能，作为油性剂作用的疏水基团，润滑性能优劣顺序为：C17H35－＞C11H23－＞C7H15－，金属元素作为活性元素，铈的抗磨性能优于锌的抗磨性能，一个分子中同时具有亲水性，疏水性，反应性等几类官能团，则兼具油性剂和极压剂功能，是性能优良的水溶性润滑添加剂。     

四硫代钼酸锌的热稳定性及润滑性能研究

合成了四硫代钼酸锌粉末并考察了其作为固体润滑剂在室温至５００℃下的润滑作用;同时采用热重分析对其热稳定性进行了评价,用Ｘ射线光电子能谱对磨损表面典型元素的化学状态进行了分析。结果表明：四硫代钙酸锌在大气中的第一分解温度为２３５．５℃,第二分解温度为７１０．８℃,分解产物为ＺｎＭｏＯ４;在Ｎ２中的分解温度为３６２．８℃和５０７．８℃,产物分别为ＺｎＭｏＳ２和ＺｎＭｏＳ．摩擦磨损试验结果表明,Ｓｉａｌ     

天然鳞片石墨与油溶性添加剂相互作用的研究

考察了天然鳞片状石墨与润滑油脂中几种常用油溶性添加剂的相互作用及其对油品润滑性能的影响．结果表明：仅添加石墨的润滑油的润滑性较差，而添加石墨与含活性基团添加剂的油品润滑性明显提高，石墨与润滑油中几种添加剂具有良好的配伍性和一定的协同作用．利用Ｘ射线光电子能谱仪检测了不同工艺条件下以石墨与含活性元素Ｓ的添加剂复合后Ｓ在石墨上的吸附量．石墨与某些添加剂的协同作用是在摩擦过程中相互作用形成了复合膜的结果．