Preparation and Optical Properties of SnO2／SiO2 Nanocomposite

SnO2/SiO2 nanocomposites have been prepared by the soaking-thermal-decomposing method, tin oxide nanoparticles are uniformly dispersed in the mesopores of silica. The optical absorption edge of the obtained nanocomposite presents a redshift compared with bulk tin oxide, With the increasing annealing temperature during the procedure of the sample preparation, the optical absorption edge of the sample moves to shorter wavelength (blueshift). These optical properties can be ascribed to the amorphous structure and band defects of surface layers of the tin oxide nanoparticles.     

d轨道分裂和过渡金属化合物性质的研究

用群的表示来讨论过渡金属化合物中心离子在不同对称场中d轨道分裂 ,并通过群链的分解 ,应用广义Wigner-Eckart定理来研究d轨道分裂能。然后进一步解释过渡金属二硫属化合物电子结构、电学性质的特点和宝石的致色机理     

Ni-SDC固体氧化物燃料电池阳极的合成和性质

采用柠檬酸-硝酸盐溶胶-凝胶低温自蔓延燃烧法制备氧化镍（NiO）粉末和Ce0.8Sm0.2O1.9（SDC）粉末，并将NiO与SDC按不同质量比和不同制备工艺制备了固体氧化物燃料电池（SOFC）的阳极前身。再用自组装的还原装置将其在820℃经2．5h还原后，采用四端子法测量其电导率值。分析了阳极片电导率与阳极片微结构、Ni的质量百分数、混合研磨时间及烧结温度之间的关系。结果显示，阳极片的电导率强烈依赖于镍含量和制备工艺。     

聚（3—丁基噻吩）电导的热稳定性

研究了导电聚合物聚（３－丁基噻吩）（ＰＢＴ）在大气环境下的导电热稳定性。在室温至２２０℃范围内，测试电导率随时间及温度的变化。ＴＧＡ分析以及化学分析的结果表明：掺杂态的ＰＢＴ大约在１４０℃附近有一转化温度，低于或高于这一转化温度，电导率下降的决定因素各不相同。高于转化温度时，电导率下降的主要原因是反离子和高分子主链的解离，进而发生化学反应，影响了高分子主链的结构。ＸＰＳ测试结果表明：经热处理后的Ｐ     

双（1,2—丙二胺）合铜的TCNQ盐的合成与光谱研究

合成了导电性ＴＣＮＱ盐Ｃｕ（ｐｎ）２（ＴＣＮＱ）ｎ（ｎ＝２和３，ｐｎ＝１，２－丙二胺，ＴＣＮＱ＝７，７，８，８－四氰基对苯二醌二甲烷）。红外光谱、电子光谱和Ｘ－光电子能谱研究表明ＴＣＮＱ盐中存在ＴＣＮＱ°和ＴＣＮＱ－，ＴＣＮＱ°与ＴＣＮＱ－之间发生了部分电子转移，致使铜呈混合价态。它们的粉末室温电导率为１．１×１０－５～２．４×１０－６ｏｈｍ－１ｃｍ－１。     

凝胶型聚合物电解质的电导率与温度的关系

凝胶型聚合物电解质的电导率与温度的关系孙晓光，林云青，齐力，景遐斌，王佛松（中国科学院长春应用化学研究所长春１３００２２）关键词凝胶电解质，离子电导率，活化能无定形聚合物电解质电导与温度的依赖关系一般可用Ｖｏｇｅｌ－Ｔａｍｍａｎ－Ｆｕｌｃｈｅｒｃ（Ｖ...     

Ce0.8Y0.2O1.9-Ca3(PO4)2-K3PO4复合电解质在中温区的质子导电性及在常压合成氨中的应用

A precursor of Ce_0.8Y_0.2O_1.9(YDC) solid electrolyte was synthesized by the gol-gel method. YDC and phosphates powders were prepared by mixing the YDC and phosphates according to different weight ratios. The mixtures of the YDC and binary phosphates were ground and sintered at 1 400 ℃. The proton conductivity in solid electrolyte of the sintered samples was examined using electrochemical methods at 400～800 ℃. Ammonia was synthesized from nitrogen and hydrogen at atmospheric pressure in the solid state proton conducting cell reactor. The optimal condition for the ammonia production was determined. The result indicated that composite electrolyte of 80wt% YDC: 20wt% binary phosphates as proton conductor could obtain the highest ionic conductivity and ammonia production rate among the four samples, the rate of evolution of ammonia was up to 9.5 × 10^-9 mol·s^-1·cm^-2.     

双冠醚的研究I.Shiff碱型双冠醚的合成和性质

本文合成了七种新的芳(杂)环桥联Shiff碱型双冠醚.电导率测量结果说明它们与四苯基硼钾,铷,铯生成的是2:1夹心型 配合物(冠醚单元:金属离子);与钠离子生成的是1:1配合物.此外,将4'-氨基苯并15-冠-5分别与α,α'-呋喃二甲醛和邻苯二甲醛缩合得到的双冠醚3e和4制成pvc膜钾离子选择性电极,证明它们对.钠离子的选择系数都在10[-4]左右.     

TiO2/P(VdF-HFP)杂化纤维微孔膜的制备及其电化学性能

用电纺法制备了TiO₂/P(VdF-HFP)(聚偏氟乙烯-六氟丙烯共聚物)杂化纤维微孔膜, 用SEM观察了杂化纤维微孔膜的形貌, 并测算了这类由超细纤维相互搭接而形成的微孔膜的孔隙率. 这种微孔膜吸附LiPF₆/EC-DMC-EMC(碳酸乙烯酯-二甲基碳酸酯-碳酸甲乙酯)电解质溶液后得到凝胶聚合物电解质膜. 用电化学方法测试了聚合物电解质膜的离子电导率、锂离子迁移数等参数, 并研究了TiO₂纳米晶的掺入对聚合物电解质电化学性能的影响. 结果表明, TiO₂的掺入降低了P(VdF-HFP)聚合物基体的结晶度, 改善了凝胶聚合物电解质的低温电化学性能.     

聚苯胺水基胶体分散液及其复合物的研究：Ⅱ.紫外光谱及导电性能

利用紫外可见光谱研究了聚苯胺在水基胶体分散液中掺杂与脱掺杂过程，证实了ＰＡｎ的掺杂与脱掺杂是完全可逆的过程。当ｐＨ＝３．５时，开始脱掺杂，当ｐＨ＝６．０时，掊掺杂已基本结束。ＰＡｎ颗粒的大小也对紫外光谱有影响。当聚苯胺颗粒尺寸达到纳米量级时，复合膜光谱吸收峰明显半移，表现出表面效应和量子尺寸效应。