煤直接液化油中混合酚的分离研究

利用分子筛择形特点，对煤直接液化油中的混合酚实施高效分离。本研究选取间甲酚和对甲酚作为分离煤直接液化油馏分段混合酚的模型化合物，采用化学液相沉积法对HZSM-5吸附剂的孔口结构进行改变，分析分子筛硅铝比及颗粒粒径对模型化合物间甲酚和对甲酚吸附分离性能的影响，以获得高性能固相吸附剂，并将其应用于180-190℃馏分段混合酚分离。结果表明，当分子筛硅铝比为25、粒径为3-5 μm时，分子筛的孔口结构调节效果最优；当正硅酸乙酯的最小用量为0.2 mL/g时，固相吸附剂的吸附量为0.03 g/g，对甲酚选择性高于95%。由于外表面沉积物对吸附剂的孔口结构变化，导致对甲酚选择性的提高。进一步采用HZSM-5（1）吸附剂对真实煤直接液化油混合酚的分离中发现，苯酚和对甲酚的选择性均达到100%。     

Can a Procedure for the Growth of Single-layer Graphene on Copper be used in Different Chemical Vapor Deposition Reactors?

In the last decade, catalytic chemical vapor deposition (CVD) has been intensively explored for the growth of single-layer graphene (SLG). Despite the scattering of guidelines and procedures, variables such as the surface texture/chemistry of catalyst metal foils, carbon feedstock, and growth process parameters have been well-scrutinized. Still, questions remain on how best to standardize the growth procedure. The possible correlation of procedures between different CVD setups is an example. Here, two thermal CVD reactors were explored to grow graphene on Cu foil. The design of these setups was entirely distinct, one being a “showerhead” cold-wall type, whereas the other represented the popular “tubular” hot-wall type. Upon standardizing the Cu foil surface, it was possible to develop a procedure for cm²-scale SLG growth that differed only by the carrier gas flow rate used in the two reactors.     

Lipase‐Supported Metal–Organic Framework Bioreactor Catalyzes Warfarin Synthesis

A green and sustainable strategy synthesizes clinical medicine warfarin anticoagulant by using lipase‐supported metal–organic framework (MOF) bioreactors (see scheme). These findings may be beneficial for future studies in the industrial production of chemical, pharmaceutical, and agrochemical precursors.     

Physical aging in amorphous poly(ethylene furanoate): Enthalpic recovery,density, and oxygen transport considerations

The current work utilizes three separate techniques to study the physical aging process in amorphous poly(ethylene furanoate) (PEF), which is a recently introduced engineering thermoplastic with enhanced properties compared to petroleum‐sourced poly(ethylene terephthalate). Differential scanning calorimetry aging experiments were conducted at multiple aging temperatures and times, and the resultant enthalpic recovery values compared to the theoretical maximum enthalpy loss evaluated from calculations involving extrapolation of the equilibrium liquid line. Density measurements reveal densification of the matrix for the aged versus unaged samples, and provide an estimate for the reduction in free volume for the aged samples. Complementary oxygen permeation and pressure‐decay sorption experiments provide independent verification of the free volume reduction mechanism for physical aging in glassy polymers. The current work provides the first detailed aging study for PEF. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 389–399     

Facile non‐lithographic route to highly aligned silica nanopatterns using unidirectionally aligned polystyrene‐block‐polydimethylsiloxane films

Thin films (monolayer and bilayer) of cylinder forming polystyrene‐block‐polydimethylsiloxane (PS‐b‐PDMS) were shear aligned by the swelling and deswelling of a crosslinked PDMS pad that was physically adhered to the film during solvent vapor annealing. The nanostructures formed by self‐assembly were exposed to ultraviolet‐ozone to partially oxidize the PDMS, followed by calcination in air at 500 °C. In this process, the PS segments were fully decomposed, while the PDMS yielded silica nanostructures. The highly aligned PDMS cylinders were thus deposited as silica nanolines on the silicon substrate. Using a bilayer film, the center‐to‐center distance of these features were effectively halved from 38 to 19 nm. Similarly, by sequential shear‐alignment of two distinct layers, a rhombic array of silica nanolines was fabricated. This methodology provides a facile route to fabricating complex topographically patterned nanostructures. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1058–1064     

Thermal gradient induced sidebranching in directional solidification

The polycrystalline perovskitelike manganese oxides La_1-xA_xMnO (A = Na, and K, ) have been fabricated by sol-gel technique. For all the compositions explored in this work, the average manganese oxidation state is practically constant, at for A = Na, and for A = K, respectively. A close relationship is confirmed to hold between the Curie temperature (T_c) and the bond distance of Mn-O. Results of magnetic measurements show that these materials can be utilized as suitable candidates for magnetic refrigerants with wide applied temperature span, for their significant entropy change and the easily tuned Curie temperature. Received: 12 September 1997 / Revised: 18 December 1997 / Accepted: 21 January 1998     

设计性、研究性实验对学生创新能力的培养

根据设计性、研究性实验的特点,从几个方面、不同的角度,阐述了设计性、研究性实验对学生创新能力培养的作用与意义。     

GaN氢化物气相外延生长系统的设计与制作

根据GaN氢化物气相外延生长(HVPE)的原理,设计制作了双温区卧式HVPE系统．根据实际生长中出现的问题和CaN样品的测试情况,对系统进行了逐步的调试和改进．     

Roles of SiH4 and SiF4 in growth and structural changes of poly-Si films

The structural properties of polycrystalline silicon films, prepared by plasma enhanced chemical vapor deposition system, with different flow rates of SiH₄/SiF₄ mixtures at 300 °C were investigated. This study indicates that the low hydrogen coverage on the growing surface, under optimum fluorine radicals, will be leaded to an improvement of crystallized area as compared with case of high hydrogen coverage surface. Moreover, the studies of the role of SiH₄ and SiF₄ radicals show that the SiH₄ radicals are important in the nucleation and growth of grains. However, SiF₄ radicals are effective in the structural change of grain boundaries regions and by this way, in the present system, establish the growth of grains under the dominant 〈1 1 0〉 direction. The stress investigation indicates that addition of high flow rate of SiF₄ in amorphous film, results in the nearly stress free films. Finally, we found that the changes in g-value reflect the changes in the intrinsic compressive and tensile stress in the both polycrystalline and amorphous silicon films.     

Electrical properties and Schottky diodes using N-N′diphenyl-1-4phenylenediamine

Thin films of, N-N′diphenyl 1-4phenylene-diamineane are prepared using vacuum sublimation technique. The electrical conductivity from room temperature down to 127 K is studied. It is found that the conduction of charge carriers obeys T^−1/2 dependence on temperature. The average hopping distance, hopping energy, density of states and their variation due to post-deposition heat treatment are studied. Schottky diodes are fabricated with gold as ohmic contact and aluminium as Schottky contact. From the observed current voltage characteristics the saturation current density, diode ideality factor and the barrier height are determined. Their variation with air annealing is also investigated.