The dielectric behaviour of doped near-stoichiometric lithium niobate in the terahertz range

The dielectric properties of near-stoichiometric LiNbO₃:Fe and LiNbO₃:Ce single crystals have been investigated using terahertz time domain spectroscopy in a frequency range of 0.7-1.6 THz at room temperature. When coupled with an applied external optical field, obvious photorefractive effects were observed, resulting in a modulation of the complex dielectric constant for the crystals. The variation in refractive index, |Δn|, had a linear relationship with the applied light intensity, accompanied by a step-like decrease at high intensity. The findings were attributed to the internal space charge field of the photorefraction and the light-induced domain reversal in the crystals.     

近化学计量比铌酸锂晶体组分测定与缺陷观察

采用助熔剂提拉法生长得到近化学计量比LiNbO3晶体.用多种方法测定了晶体组分,结果表明生长得到的晶体中[Li2O]含量为49.80;摩尔分数;对晶体缺陷的研究表明晶体质量有待提高,并分析了晶体中出现包裹物的原因.     

近化学计量组分掺铒铌酸锂晶体光学特性研究

用气相输运平衡技术成功地制备出了近化学计量组分的Er∶LiNbO₃晶体,系统 地研究了该 晶体的吸收边移动、可见—红外透射谱、荧光光谱的物理特性.与同成分Er∶LiNbO_{3晶体 相比, 近化学计量组分Er∶LiNbO3晶体的吸收边出现了“蓝移”;OH^{-吸收带明显减弱 ;在可见—近红外波段呈现出更高的透过率;同时Er3+离子的发光强度也明显 提高. 这些结果表明近化学组分的Er∶LiNbO关键词： 近化学组分掺铒铌酸锂晶体 -}吸收带')" href="#">OH^-吸收带 透射谱 荧光光谱}     

近化学计量比Tb:Fe:LiNbO3晶体的光谱特性及组分测定

按化学计量比,用提拉法成功生长了不同掺量的Tb:Fe:LiNbO3晶体,分别测量了掺杂LiNbO3晶体在紫外(313nm)曝光前后的吸收光谱,曝光后吸收谱线整体上移,找到了吸收谱线上移最大的掺量比.并用差热分析仪DTA测量了居里温度Tc, 从而计算出Li/Nb的比例.分析表明,Tb:Fe:LiNbO3晶体的存储性能与掺量、定比有密切的联系,是一种优良的大容量体全息记录材料.     

The effect of an optical pump on the absorption coefficient of magnesium-doped near-stoichiometric lithium niobate in terahertz range

The absorption coefficient of magnesium-doped near-stoichiometric lithium niobate crystal is measured by terahertz time-domain spectroscopy in a frequency range of 0.2 THz~0.9 THz at room temperature. The absorption coefficient is modulated by external optical pump fields. Experimental results show that the absorption coefficient of near-SLN：Mg crystal is approximately in a range of 22 cm- 1_35 cm- 1 in a frequency range of 0.2 THz-0.9 THz and tunable up to nearly 15%. Further theoretical analysis reveals that the variation of absorption coefficient is related to the number of light-induced carriers, domain reversal process, and OH- absorption in this crystal.     

近化学配比LiNbO3晶体双色光全息记录的实验研究

实验用红光记录紫光敏化,研究了几种不同掺杂浓度和氧化还原状态的近化学配比铌酸锂晶体的双色全息记录特性,如其饱和衍射效率和记录灵敏度的变化规律。实验结果表明,晶体的饱和衍射效率随透射光强与紫外光强比值的增加先增加后减小,而记录灵敏度在不断减小。Mn含量相同时,Tb含量越高的晶体饱和衍射效率越高,而记录灵敏度越低。Tb含量相同时,含Mn比不含Mn的晶体的饱和衍射效率低,但记录灵敏度更高。还原晶体的饱和衍射效率和记录灵敏度均比氧化晶体高。记录光与敏化光的比值、掺杂浓度和氧化还原状态对晶体的全息特性产生影响。通过适当调整上述参数之间的关系,可对材料的全息记录特性进行优化。     

Zn,Co双掺杂近化学计量比LiNbO_3晶体的生长及性能

以K_2O为助熔剂,应用坩埚下降法生长出了Co~(2+) 初始浓度为0.5 mol;,以及ZnO分别为3 mol;与6 mol;的单掺与双掺杂SLN晶体(分别用SLN0, SLN3, SLN6表示).测定了晶体上下部位的吸收与发射光谱.在晶体的吸收光谱中均可观察到520 nm,549 nm,612 nm,1447 nm四个吸收峰,表明Co~(2+)处于晶体的八面体场中.ZnO的掺入明显地改变了吸收峰的相对强度.在520 nm光的激发下,观察到776 nm的荧光发射,其荧光强度的相对强弱也与ZnO的掺杂量有明显的联系.从吸收边带估算出SLN0, SLN3, SLN6晶体中Li2O的含量分别为49.06 mol;,49.28 mol;, 49.10 mol;.ZnO的掺杂量对Co~(2+)在铌酸锂晶体中的浓度分布有很大的影响作用,当ZnO的掺入量为3 mol;时,明显地抑制了Co~(2+)在LiNbO_3晶体中的掺入,当ZnO掺杂量达到6 mol;时,抑制作用减弱.本文从Zn~(2+)在LiNbO_3中随浓度变化的分凝情况以及对Co~(2+)的排斥作用解释了Co~(2+)在晶体中的分布特性以及光谱的变化情况.     

助熔剂坩埚下降法生长近化学计量比Co:LiNbO3晶体

以K2O为助熔剂,在较大的温度梯度(90～100℃/cm)条件下进行引种和晶体生长,应用坩埚下降法成功地生长出了初始CO2+掺杂浓度为0.5mol;的近化学计量比的铌酸锂晶体.测定了该晶体的红外光谱与吸收光谱,与同成份的LiNbO3晶体相比,其紫外吸收边向短波方向移动,OH-红外吸收峰的位置发生变化.观测到520,549,612nm三个分裂的尖吸收峰以及1400nm左右为发光中心的吸收带.从吸收特性可以判断,Co离子在铌酸锂晶体中呈现+2价.比较上部与下部晶体的吸收强度,可以推测出沿着晶体生长方向Co2+离子浓度逐渐降低,Co2+离子在晶体中有效的分凝系数大于1.     

近化学计量比LiNbO3晶体畴结构研究

利用提拉法,从富锂(Li2O:Nb2O5=58.5:41.5)熔体中生长了φ40mm×40mm的近化学计量比铌酸锂晶体.用同步辐射异常散射技术结合化学腐蚀法观察了晶体中的畴结构,在y方向发现存在180°反向铁电畴结构,而另外的N-SLN单晶z向切片为单畴结构,表明了所生长的近化学计量比铌酸锂晶体具有区域性单畴.     

掺铁近化学配比铌酸锂晶体的紫外光致吸收和弛豫过程的研究

生长了系列掺杂低铁(质量分数分别为0×10-6,3×10-6,5×10-6,10×10-6,25×10-6,50×10-6、100×10-6)的近化学配比铌酸锂(SLN)晶体,测量了它们的紫外-可见光谱,并通过477nm处的线性吸收系数估算晶体中Fe2+和Fe3+的浓度。利用抽运(365nm)-探测(632.8nm)法测量不同掺杂浓度晶体光致吸收的动态过程和稳态特性,结果表明光致吸收是以扩展指数的形式衰减的,其衰减时间常数(即小极化子的寿命)随掺杂浓度和抽运光强增加而减小,扩展指数因子随抽运光强的增加而减少。根据电子的输运方程,利用四阶龙格-库塔方法对电子输运过程进行数值求解,模拟了掺铁铌酸锂(Fe:SLN)晶体的光致吸收的全过程,与实验所得结果符合得很好。