A New Triterpene from the Orchid Pholidota yunnanensis

A new triterpene, 25-methylenecyclopholidonyl p-hydroxy-trans-cinnamate, was isolated from a orchid Pholidota yunnanensis. The structure elucidation and ^1H, ^13C-NMR assignments were achieved by spectral and chemical method.     

纳米累托石-TiO2光催化剂的制备及表征

以TiCl4和累托石为主要原料，制备出纳米累托石-TiO2粉末，并用X-衍射、透射电镜等对其进行表征．结果表明：纳米累托石-TiO2粉末平均直径为17．5nm当焙烧温度从500℃升至800℃时，累托石-TiO2粉末的比表面积从65．7m^2／g下降至3．3m^2／g，单位质量吸附剂的孔体积从0．1430cm。／u降到0．0213cm^3／g；当焙烧温度从300℃上升至500℃时，孔径变化不大，属中孔范围；当焙烧温度升至800℃时，一些孔道出现坍塌，不利于纳米累托石-TiO2粉末的光催化活性．     

稀土-碱土-过渡金属类钙钛石(A2BO4)复合氧化物催化剂的固态物化性质及对Nox 消除反应的催化性能

用柠檬酸络合法制备了多个系列的类钙钛石(A2BO4)结构的复合氧化物催化剂, 系统地研究探讨了该类催化剂的晶体与光谱结构、缺陷结构、对NO和CO等小分子的吸附性能、对氧的吸脱性能及氧化还原性能和稳定性, 同时考察了上述多个系列催化剂对NO直接分解和CO还原NO反应的催化性能. 发现Ni系A2BO4复合氧化物是NO直接分解的高活性催化体系, 特别是LaSrNiO4-λ催化剂具有很高NO的分解活性, 其活性高于文献报道Y-Ba-CuO/MgO的和Co系ABO3催化剂. 同时发现LaSrCuO4-λ具有较高的CO还原NO催化性能. 提出了在类钙钛石复合氧化物催化剂上NO分解和还原反应统一的氧化还原反应机制, 并比较了两个反应的异同点, 确认了氧空位在上述反应中的作用. 并较深入的探讨了取代效应、过渡元素、稀土元素和结构效应对NO分解和CO还原NO反应的影响机制. 本文分析总结了作者在类钙钛石(K2NiF4)结构复合氧化物的固态物化性质及对 Nox消除反应的催化性能方面的基础性研究结果.     

姑婆山浅变生褐帘石的初步研究

对姑婆山花岗杂岩体中的褐帘石作Ｘ射线粉晶衍射、红外光谱及穆斯堡尔谱分析，证明褐帘石属浅变生态，但加热８００℃、恒温４小时后可恢复为结晶态，与结晶态褐帘石相比，浅变生褐帘石在偏光显微镜下虽然呈非匀性，但是在Ｘ射线衍射图上却少了许多衍射线，强度亦有所减弱；红外光谱也少了几个强吸收峰，而且谱带向低频区位移；穆斯堡尔谱特征参数Ｉ．Ｓ，显著降低，而Ｏ．Ｓ除Ｍ３位Ｆｅ＾３＋的值减小外，均有所增大，导致褐帘石发     

水淬渣-累托石颗粒吸附材料的制备及应用

研究了水淬渣-累托石颗粒吸附材料制备工艺条件、再生方法及其去除铜冶炼工业废水中重金属的条件.试验结果表明,累托石与水淬渣的比例为1∶1,另加入10%的添加剂(IS)和50%的水,焙烧温度为400℃时,制成的颗粒吸附材料体积密度为1.06kg/m3,显气孔率为62.29%,吸水率为58.82%,抗压强度为2.22Mpa,吸附效果好,散失率较低.在未调节铜冶炼工业废水pH值的条件下,颗粒吸附材料用量为0.05g/cm3,反应时间为40min,吸附温度为25℃(常温)时,Cu2 、Pb2 、Zn2 、Cd2 、Ni2 的去除率分别为98.2%、96.3%、78.6%、86.2%、64.2%,处理后的水符合国家污水综合排放标准(GB8978-1996)一级标准.颗粒吸附材料对Zn2 、Cu2 有很好的选择性.吸附饱和的颗粒吸附材料用1mol/L氯化钠溶液再生效果好.该颗粒吸附材料具有分离容易、可重复使用、处理效果好、应用前景广阔的优点.     

钠硼解石——水体系溶解和相平衡的研究(英)

Ulexite dissolution in water has been studied in the wide temperature range from 10℃ to 93℃ and two higher temperatures at 120 ℃ and 240 ℃. The analytical results showed that ulexite dissolved congruently from 10 ℃ to 35 ℃ and incongruently from 40 to 68 ℃. The solid component of ulexite, NaCaB₅O₆(OH)₆·5H₂O was dehydrated to form NaCaB₅O₆(OH)₆·H₂O from 50 to 68 ℃ and finally amorphous solid at 68 ℃. This amorphous solid converted into priceite at 71 ℃ and then converted completely to priceite at the boiling point(93℃) of the solution. At both 120 and 240 ℃, the dissolution of ulexite was an incongruent process. Above 120 ℃, ulexite became amorphous solid and then transformed into priceite. In addition to the solid to solid transformation, crystallization of priceite from the solution has also been observed. Based on our experimental results, mechanisms of dissolution, transformation, and crystallization of borate in ulexite-water system are discussed.     

铯榴石硫酸浸出提取铯盐工艺研究

简述了铯榴石提铯工艺的概况, 确定了铯榴石硫酸法生产铯盐的工艺, 研究了铯榴石硫酸浸出的主要工艺的条件, 优化选择了硫酸浸出的最佳条件, 为工业化生产提供了可靠的依据.     

改性累托石吸附水溶液中苯酚的研究I吸附条件的确定

用十二烷基二甲基苄基氯化铵 (1227)、十六烷基三甲基溴化铵 (1631)、十八烷基三甲基溴化铵 (1831) 3种表面活性剂改性天然累托石 (REC) 粘土,分别得到3种有机改性累托石:1227-REC、1631-REC和1831-REC。用有机改性累托石作吸附剂,对水溶液中的苯酚进行吸附研究,考察了pH值、吸附时间、吸附剂用量、温度等因素对吸附效果的影响。结果发现,在本文研究条件下,3种吸附剂对苯酚达到较理想吸附效果的合理条件是:pH值分别为6、8、8;吸附平衡时间分别需要90、20、40min;吸附剂用量均为20g/L;常温。在确定的合理条件下,去除率分别能达到66.2%、99.0%、99.8%。     

钠硼解石碳化机理的研究

采用Ｃａ（２＋）选择电极，ｐＨ电极和电导电极对钠硼解石水溶液碳化过程进行跟踪测定。实验结果表明：反应分二步进行，反应最终结果是钠硼解石完全分解，硼全部进入溶液并大部分以Ｈ３ＢＯ３的形式存在，同时考察了温度，气流量对钠硼解石水溶液碳化结果的影响。根据碳化机理，提出了较佳的碳化条件。