部分还原氧化石墨烯的制备、 表征及对人宫颈癌HeLa细胞的体外杀伤作用

以氧化石墨烯(GO)为原料, 利用温和方法制备了3种不同还原程度的部分还原氧化石墨烯pRGO₁, pRGO₂和pRGO₃(pRGO_1—3)； 利用傅里叶变换红外光谱(FTIR)、 拉曼光谱(Raman)、 X 射线光电子能谱(XPS)、 紫外-可见光谱(UV-Vis)、 透射电子显微镜(TEM)和 EDS能谱对其结构和形貌进行了表征. 细胞实验结果表明, 无激光照射下pRGO_1—3本身的细胞毒性较低; 近红外(NIR)激光照射下pRGO_1—3通过光热和光毒性双重作用杀伤肿瘤细胞. 实验结果显示了pRGO 在肿瘤光热疗法和光动力疗法领域的应用潜力.     

Calcium-based coordination polymers from a solvothermal synthesis of HKUST-1 in 3D printed autoclaves

A mixed-metal 1D coordination polymer [CaCu(HBTC)₂(H2O)₈]_n (where H₃BTC – benzene-1,3,5-tric arboxylic acid) was obtained in a solvothermal synthesis of a well-known copper-containing metal–organic framework [Cu₃(BTC)₂(H₂O)₃]_n (HKUST-1) in autoclaves 3D-printed from commercial polypropylene. This material was a source of calcium ions, apparently, leaking from a colorant (calcium carbonate) promoted by glacial acetic acid as a modulator used to produce large single crystals of HKUST-1. This finding was confirmed by elemental analysis and a model experiment that resulted in a new calcium-based 1D coordination polymer [Ca(H₂BTC)₂(H₂O)₅]_n under the same solvothermal conditions with no copper or calcium salts put into a 3D-printed autoclave.     

Photothermal Oxidation of Cinnamyl Alcohol with Hydrogen Peroxide Catalyzed by Gold Nanoparticle/Antimony-Doped Tin Oxide Nanocrystals

Gold nanoparticles with different mean sizes were formed on antimony-doped tin oxide nanocrystals by the temperature-varied deposition-precipitation method (Au/ATO NCs). Au/ATO NCs possess strong absorption in the near-infrared region due to Drude excitation in addition to the localized surface plasmon resonance (LSPR) of AuNPs around 530 nm. Au/ATO NCs show thermally activated catalytic activity for the oxidation of cinnamyl alcohol to cinnamaldehyde by hydrogen peroxide. The catalytic activity increases with a decrease in the mean Au particle size (d_Au) at 5.3 nm≤d_Au≤8.2 nm. Light irradiation (λ_ex >660 nm, ∼0.5 sun) of Au/ATO NCs increases the rate of reaction by more than twice with ∼95 % selectivity. Kinetic analyses indicated that the striking enhancement of the reaction stems from the rise in the temperature near the catalyst surface of ∼30 K due to the photothermal effect of the ATO NCs.     

Biosynthesis of zinc oxide nanoparticles using Euphorbia milii leaf constituents: Characterization and improved photocatalytic degradation of methylene blue dye under natural sunlight

A facile biosynthesis route was followed to prepare zinc oxide nanoparticles (ZnO NPs) using Euphorbia milii (E. milii) leaf constituents. The SEM images exhibited presence of spherical ZnO NPs and the corresponding TEM images disclosed monodisperse nature of the ZnO NPs with diameter ranges between 12 and 20 nm. The Brunauer–Emmett–Teller (BET) analysis revealed that the ZnO NPs have specific surface area of 20.46 m²/g with pore diameter of 2 nm–10 nm and pore volume of 0.908 cm³/g. The EDAX spectrum exemplified the existence of Zn and O elements and non-appearance of impurities that confirmed pristine nature of the ZnO NPs. The XRD pattern indicated crystalline peaks corresponding to hexagonal wurtzite structured ZnO with an average crystallite size of 16.11 nm. The FTIR spectrum displayed strong absorption bands at 512 and 534 cm^?1 related to ZnO. The photocatalytic action of ZnO NPs exhibited noteworthy degradation of methylene blue dye under natural sunlight illumination. The maximum degradation efficiency achieved was 98.17% at an illumination period of 50 min. The reusability study proved considerable photostability of the ZnO NPs during photocatalytic experiments. These findings suggest that the E. milii leaf constituents can be utilized as suitable biological source to synthesis ZnO NPs for photocatalytic applications.     

Fabricating Dual-Atom Iron Catalysts for Efficient Oxygen Evolution Reaction: A Heteroatom Modulator Approach

Understanding the thermal aggregation behavior of metal atoms is important for the synthesis of supported metal clusters. Here, derived from a metal–organic framework encapsulating a trinuclear Fe^III₂Fe^II complex (denoted as Fe₃) within the channels, a well-defined nitrogen-doped carbon layer is fabricated as an ideal support for stabilizing the generated iron nanoclusters. Atomic replacement of Fe^II by other metal(II) ions (e.g., Zn^II/Co^II) via synthesizing isostructural trinuclear-complex precursors (Fe₂Zn/Fe₂Co), namely the “heteroatom modulator approach”, is inhibiting the aggregation of Fe atoms toward nanoclusters with formation of a stable iron dimer in an optimal metal–nitrogen moiety, clearly identified by direct transmission electron microscopy and X-ray absorption fine structure analysis. The supported iron dimer, serving as cooperative metal–metal site, acts as efficient oxygen evolution catalyst. Our findings offer an atomic insight to guide the future design of ultrasmall metal clusters bearing outstanding catalytic capabilities.     

Theoretical studies on the influence of metallic cations on ring opening of propylene oxide catalyzed by metal-salen complexes

We studied the ring opening of propylene oxide (PO) by salen-M coordinated OH⁻ group [M = Al(III), Sc(III), Cr(III), Mn(III), Fe(III), Co(II), Co(III), Ni(II), Cu(II), Zn(II), Ru(III) and Rh(III)]. The results show that the ring-opening energy barriers for M(II) complexes are much lower than those with M(III) complexes in the gas phase, and the barriers correlate linearly with the negative charges on the OH⁻ group and the Fukui function condensed on the OH⁻ group. The nucleophilicity ordering in the gas phase can be rationalized by the ratio of formal positive charges/radius of M cations. Solvent effect greatly increases the barriers of M(II) complexes but slightly changes the results of M(III) ones, making the barriers similar. Analysis indicates that the reaction heats are linearly proportional to the reverse reaction barriers. The relationships established here can be used to estimate the ring-opening barriers and to screen epoxide ring-opening catalysts.     

Functional zinc(II) phthalocyanines bearing Schiff base complexes as oxidation catalysts for bleaching systems

Oxidation catalysis is used to increase the performance of hydrogen peroxide in laundry bleach applications. Bleach catalysts provide cost‐effective, energy‐saving and environmentally friendly bleach systems yielding perfect stain removal at lower temperatures. This comparative study is based on the synthesis of bis[bis(salicylhydrazonephenoxy)manganese(III)] phthalocyaninatozinc(II) ( 2 ), bis[bis(salicylhydrazonephenoxy)cobalt(III)] phthalocyaninatozinc(II) ( 3 ) and bis[bis(salicylhydrazonephenoxy)iron(III)] phthalocyaninatozinc(II) ( 4 ) as tri‐nuclear complexes consisting of two Schiff base complexes substituting a zinc phthalocyanine. Complexion on the periphery to obtain complexes 2 , 3 , 4 was performed through the reaction of a Schiff base‐substituted phthalocyanine using MnCl₂?4H₂O, CoCl₂?6H₂O or FeCl₃?6H₂O salts in basic condition in dimethylformamide. Fourier transform infrared, ¹H NMR, ¹³C NMR, UV–visible, inductively coupled plasma optical emission and mass spectra were applied to characterize the prepared compounds. The bleach performances of the three phthalocyanine compounds 2 , 3 , 4 were examined by the degradation of morin as hydrophilic dye. The degradation progress in the presence of catalysts 2 , 3 , 4 /H₂O₂ combination in aqueous solution was investigated using an online spectrophotometric method. It was found that the catalysts 2 , 3 , 4 exhibited better bleaching performance at 25 °C than tetraactylethylethylenediamine as bleach activator used in powder detergent formulations for stain removal. Copyright © 2015 John Wiley & Sons, Ltd.     

Synthesis of Small‐Sized,Porous, and Low‐Toxic Magnetite Nanoparticles by Thin POSS Silica Coating

In this communication, we report the synthesis of small‐sized (<10 nm), water‐soluble, magnetic nanoparticles (MNPs) coated with polyhedral oligomeric silsesquioxanes (POSS), which contain either polyethylene glycol (PEG) or octa(tetramethylammonium) (OctaTMA) as functional groups. The POSS‐coated MNPs exhibit superparamagnetic behavior with saturation magnetic moments (51–53 emu g^?1) comparable to silica‐coated MNPs. They also provide good colloidal stability at different pH and salt concentrations, and low cytotoxicity to MCF‐7 human breast epithelial cells. The relaxivity data and magnetic resonance (MR) phantom images demonstrate the potential application of these MNPs in bioimaging.     

Synthesis and applications of graphene oxide aerogels in bone tissue regeneration: a review

Development of biocompatible porous supports is a promising strategy in the field of tissue engineering for the repair and regeneration of bone tissues with severe damage. Graphene oxide aerogels (GOAs) are excellent candidates for the manufacture of these systems due to their porosity, ability to imitate bone structure, and mechanical resistance, and according to their surface chemical reactivity, they can facilitate osseointegration, osteogenesis, osteoinduction and osteoconduction. In this review, synthesis of GOAs from the most primary source is described, and recent studies on the use of these functionalized carbonaceous foams as scaffolding for bone tissue regeneration are presented.     

从废水到新能源:光催化燃料电池的优化与应用

随着经济的飞速发展,社会对能源的需求日益扩大,对工业废水的无害化处理也提出了更高的要求。光催化燃料电池 (photocatalytic fuel cell, PFC) 在燃料电池中引入半导体光催化材料作为电极,实现了有机污染物高效降解和同步对外产电的双重功能,在废水无害化与资源化利用方面具有潜在的应用价值。半导体光催化电极是PFC系统高效运行的核心组件,增强其可见光响应和光生载流子分离是提高PFC性能的关键策略。反应器结构设计和运行参数优化也有利于改善PFC性能。本文从PFC基本原理和应用入手,综述了PFC在环境污染物资源化处理中的研究进展,并详细阐述了提高PFC的污染控制性能和产电效率的优化手段,为进一步设计高效稳定的PFC系统并实现其在水污染控制和清洁能源生产中的应用提供理论指导。