Crystallographic report: catena‐Aqua(2,2′‐bipyrimidine)lithium(I) perchlorate

A lithium(I) coordination polymer has been formed from LiClO₄ and the 2,2′‐bipyrimidine (bpym) ligand in which each square pyramidal lithium(I) atom is coordinated in the basal plane by four nitrogen donor atoms derived from two bpym ligands and one water molecule at the apical position. These are connected into a layer structure via hydrogen‐bonding interactions involving the perchlorate anions. Copyright © 2004 John Wiley & Sons, Ltd.     

Synthesis of bioactive indolocarbazoles: synthesis, nucleophilic ring-opening and chiral base desymmetrisation of a cyclic sulfate intermediate

A number of new functionalised bridged indolocarbazole systems have been prepared by ring-opening reactions of a key cyclic sulfate intermediate, prepared from the corresponding diol by the action of sulfuryl diimidazole and DBU. The same cyclic sulfate also undergoes an unprecedented asymmetric rearrangement to a chiral ketone, on treatment with a chiral lithium amide base.     

Plasticized microporous poly(vinylidene fluoride) separators for lithium-ion batteries. III. Gel properties and irreversible modifications of poly(vinylidene fluoride) membranes under swelling in liquid electrolytes

Microporous poly(vinylidene fluoride) (PVdF) separators for lithium-ion batteries, used in liquid organic electrolytes, have been characterized with respect to the swelling phenomena on dense PVdF membranes (obtained through hot pressing). In the first and second parts of this study, we have described the swelling equilibria and swelling kinetics of dense PVdF. Here the thermal properties of PVdF gels and their irreversible modifications induced by swelling are characterized. Particular attention is paid to crystallinity modifications, polymer plasticization, and membrane degradation. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2308–2317, 2004     

Synthesis and cyclization of 1-arylalk-1-ene-3,5-diynylamines

An investigation of the reaction of 1-lithio-1,3-diynes, generated in situ, with nitriles has been carried out. In the case of aromatic nitriles 1-arylalk-1-ene-3,5-diynylamines are formed, which undergo dimerization and cyclization on isolation, giving 3-(alka-1,3-diynyl)-4-(alk-2-ynyl)-2,6-diarylpyridines. The effect of the nature of the substituent in the benzonitrile molecule on the selectivity of the reaction and the yield of the products has been determined. A scheme is proposed for the conversions and the structures of the intermediates have been established. __________ Translated from Khimiya Geterotsiklicheskikh Soedinenii, No. 5, pp. 701–710, May, 2006.     

Structural and lithium intercalation studies of Mn(0.5−x)CaxTi2(PO4)3 phases (0≤x≤0.50)

Materials from the Mn_(0.5−x)Ca_xTi₂(PO₄)₃ (0≤x≤0.50) solid solution were obtained by solid-state reaction in air at 1000 °C. Selected compositions were investigated by powder X-ray diffraction analysis, ³¹P nuclear magnetic resonance (NMR) spectroscopy and electrochemical lithium intercalation. The structure of all samples determined by Rietveld analysis is of the Nasicon type with the R space group. Mn²⁺/Ca²⁺ ions occupy only the M1 sites in the Ti₂(PO₄)₃ framework. The divalent cations are ordered in one of two M1 sites, except for the Mn_0.50Ti₂(PO₄)₃ phase, where a small departure from the ideal order is observed by XRD and ³¹P MAS NMR. The electrochemical behaviour of Mn_0.50Ti₂(PO₄)₃ and Mn_(0.5−x)Ca_xTi₂(PO₄)₃ phases was characterised in Li cells. Two Li ions can be inserted without altering the Ti₂(PO₄)₃ framework. In the 0≤y≤2 range, the OCV curves of Li//Li_yMn_0.50Ti₂(PO₄)₃ cells show two main potential plateaus at 2.90 and 2.50–2.30 V. Comparison between the OCV curves of Li//Li_(1+y)Ti₂(PO₄)₃ and Li//Li_yMn_0.50Ti₂(PO₄)₃ shows that the intercalation occurs first in the unoccupied M1 site of Mn_0.50Ti₂(PO₄)₃ at 2.90 V and then, for compositions y>0.50, at the M2 site (2.50–2.30 V voltage range). The effect of calcium substitution in Mn_0.50Ti₂(PO₄)₃ on the lithium intercalation is also discussed from a structural and kinetic viewpoint. In all systems, the lithium intercalation is associated with a redistribution of the divalent cation over all M1 sites. In the case of Mn_0.50Ti₂(PO₄)₃, the stability of Mn²⁺ either in an octahedral or tetrahedral environment facilitates cationic migration.     

Dehydration and dehydroxylation of reduced charge montmorillonite

Reduced charge montmorillonites (RCM) were prepared by the thermal treatment of lithiumsaturated montmorillonite. Samples prepared by mild thermal treatment with lithium contained more water sorbed than the original montmorrilonite. When RCMs were prepared, part of the lithium cations reacted with hydroxyl groups in the octahedral sheet and released protons, which reacted with the structure. Acid treatment probably enhanced the surface area. which was reflected in the amount of water sorbed. Deprotonation of hydroxyl groups was proved by the measurements of the ignition loss. The heating of lithium saturated montmorillonite at higher temperatures brough about the collapse of the interlayers and a decrease in the amount of water sorbed.     

Inorganic Sol-Gel Preparation of Medium Sized Microparticles of Li2TiO3 from TiCl4 as Tritium Breeding Material for Fusion Reactors

Microspheres of Li₂TiO₃ were fabricated by a classical, inorganic sol-gel process from commercially available TiCl₄. Elaborated process consists of the following main steps: (1) dissolving of TiCl₄ in concentrated aqueous HCl and addition of LiOH; (2) formation of sol emulsion in 2-ethylhexanol-1 containing the surfactant SPAN-80 (EH); (3) gelation of emulsion drops by extraction of water with partially dehydrated EH; (4) impregnation of gel to Li:Ti molar ratio MR = 2; (5) thermal treatment at 1200°C in order to receive chloride free product. This temperature can be significantly lowered (to 750°C) by dechlorination starting solution TiCl₄ by chemical treatment of the with nitric acid to form of nitrate-stabilized titania sols. Tritium release from sol-gel made Li₂TiO₃ microspheres were found very close to that observed for other traditional materials, however for the first sample process starts slightly earlier.     

三硼酸锂晶体的生长形态

用自由生长系统研究了三硼酸锂ＬｉＢ_３Ｏ_５（ＬＢＯ）晶体的实际生长形态。实验表明，它的各晶面簇的重要性的顺序为：｛１１０｝＞｛０１１｝＞｛２０１｝＞｛１１１｝。讨论了ＬＢＯ晶体的生长习性与内部结构之间的关系并应用负离子配位多面体理论模型解释了ＬＢＯ晶体的生长形态。