The implementation of covalent adaptable networks (CANs) in general resin system is becoming attractive. In this work, we propose a simple post-curing strategy based on the core-shell structured acrylate latex for the achievement on both the improved general performance and the CANs characteristics in latex films. The building to the CANs was relied on the introduction of 4,4′-diaminophenyl disulfide as the curing agent, which cured the acetoacetoxy decorated shell polymer through the ketoamine reaction. The metathesis reaction of aromatic disulfides in the crosslinking segments enabled the thermally induced dynamic behavior of the network as revealed in the stress relaxation tests by comparison with other diamine crosslinking agents without the incorporation of disulfide. The synergism of the dynamic crosslinking of the shell polymer and static crosslinking in the core polymer contributed to the improved mechanical strength (15 MPa, strain% = 250%) and the suppressed water adsorption (~1% in 24 h of soaking) of the latex film, which exhibited above 90% of recovery in both strength and strain from a cut-off film damage within 1 h at 80°C. Moreover, the cured latex film could be recycled, and 75% of the mechanical performance was regained after three fragmentation-hot-pressing cycles. These, in addition with the feasible and environmental friendly characteristics, suggest a sustainable paradigm toward the smart thermosetting latex polymers.     

Precise Synthesis and Thin Film Self-Assembly of PLLA-b-PS Bottlebrush Block Copolymers

The ability of bottlebrush block copolymers (BBCPs) to self-assemble into ordered large periodic structures could greatly expand the scope of photonic and membrane technologies. In this paper, we describe a two-step synthesis of poly(l-lactide)-b-polystyrene (PLLA-b-PS) BBCPs and their rapid thin-film self-assembly. PLLA chains were grown from exo-5-norbornene-2-methanol via ring-opening polymerization (ROP) of l-lactide to produce norbornene-terminated PLLA. Norbonene-terminated PS was prepared using anionic polymerization followed by a termination reaction with exo-5-norbornene-2-carbonyl chloride. PLLA-b-PS BBCPs were prepared from these two norbornenyl macromonomers by a one-pot sequential ring opening metathesis polymerization (ROMP). PLLA-b-PS BBCPs thin-films exhibited cylindrical and lamellar morphologies depending on the relative block volume fractions, with domain sizes of 46–58 nm and periodicities of 70–102 nm. Additionally, nanoporous templates were produced by the selective etching of PLLA blocks from ordered structures. The findings described in this work provide further insight into the controlled synthesis of BBCPs leading to various possible morphologies for applications requiring large periodicities. Moreover, the rapid thin film patterning strategy demonstrated (>5 min) highlights the advantages of using PLLA-b-PS BBCP materials beyond their linear BCP analogues in terms of both dimensions achievable and reduced processing time.     

Strain effects on multiferroic BiFeO3 films

The field of multiferroics has experienced a rapid progress resulting in the discovery of many new physical phenomena. BiFeO₃ (BFO) compound, which is one of the few room-temperature single-phase multiferroics, has contributed subsequently to this progress. As a result, significant review articles have been devoted specifically to this famous system. This chapter is dedicated to the strain effects on the structure stability and property changes of BFO thin films. It is a short and non-exhaustive topical overview that may be seen as an invitation for interested readers to go beyond. There is a very active and prolific research in this field and we apologize to the authors whose relevant work is not cited here. After a short introduction, we will thus review the effect of strain on BFO films by describing the consequences on the structure and the phase transitions as well as on polar, magnetic and magnetoelectric properties.     

Functionalized Silver-Ion-Mediated α-dC/β-dC Hybrid Base Pairs with Exceptional Stability: α-d-5-Iodo-2′-Deoxycytidine and Its Octadiynyl Derivative in Metal DNA

Silver-mediated α-dC–Ag⁺–β-dC hybrid base pairs decorated with 5-iodo- or 5-octadiynyl residues are well accommodated in duplex DNA. A strong T_m increase and favorable thermodynamic data for duplex DNA were observed after addition of silver ions. The phenomenon is particularly obvious when both nucleobases of the base pairs are functionalized. Neither the position of the base pair, nor the type of 5-substituent had a negative influence. On the contrary, functionalization of conventional silver-mediated β-dC–Ag⁺–β-dC homo base pairs showed a negative impact induced by the bulky substituents. To this end, cytosine modified 12-mer oligodeoxynucleotides were prepared by solid-phase synthesis employing new α-anomeric 2′-deoxycytidine phosphoramidites. A multigram scale synthesis was developed for 5-iodo-α-d -2′-deoxycytidine ( 1 ) employing the direct glycosylation of cytosine with Hoffer's α-d -halogenose followed by separation of anomeric DMT nucleosides. Regarding base-pair stability and functionalization silver-mediated α/β-dC hybrid base pairs were found to be superior to β/β-dC homo pairs. According to their extraordinary properties, they might find applications in DNA diagnostics, material science, or nanotechnology.     

Enhancing the Water Stability of Al‐MIL‐101‐NH2 via Postsynthetic Modification

The resistance of metal–organic frameworks towards water is a very critical issue concerning their practical use. Recently, it was shown for microporous MOFs that the water stability could be increased by introducing hydrophobic pendant groups. Here, we demonstrate a remarkable stabilisation of the mesoporous MOF Al‐MIL‐101‐NH₂ by postsynthetic modification with phenyl isocyanate. In this process 86 % of the amino groups were converted into phenylurea units. As a consequence, the long‐term stability of Al‐MIL‐101‐URPh in liquid water could be extended beyond a week. In water saturated atmospheres Al‐MIL‐101‐URPh decomposed at least 12‐times slower than the unfunctionalised analogue. To study the underlying processes both materials were characterised by Ar, N₂ and H₂O sorption measurements, powder X‐ray diffraction, thermogravimetric and chemical analysis as well as solid‐state NMR and IR spectroscopy. Postsynthetic modification decreased the BET equivalent surface area from 3363 to 1555 m² g^?1 for Al‐MIL‐101‐URPh and reduced the mean diameters of the mesopores by 0.6 nm without degrading the structure significantly and reducing thermal stability. In spite of similar water uptake capacities, the relative humidity‐dependent uptake of Al‐MIL‐101‐URPh is slowed and occurs at higher relative humidity values. In combination with ¹H‐²⁷Al D ‐HMQC NMR spectroscopy experiments this favours a shielding mechanism of the Al clusters by the pendant phenyl groups and rules out pore blocking.     

基于DIS数字信息化系统对透光物质透光性能的研究

采用DIS数字信息化系统,对不同浓度的蓝墨水溶液在激光光源照射下的透射平均照度及照度分布图像进行实验研究,得到了平均照度值随溶液浓度变化的规律。对不同颜色塑料膜片对白炽灯光源透过照度值及照度分布图像进行实验研究得到及其相关之规律。     

Characterization of ZnO:AI films deposited by r.f.magnetron-sputtering at low temperature

Transparent conducting ZnO:AI thin films with good adhesion and Iow resistivity have been prepared on organic substrates and Coming 7059 glass substrates by r.f. magnetron-sputtering technique at Iow substrate temperature (25-210℃). Structural and photoelectric properties of the deposited films are investigated. The deposited films are polycrystalline with hexagonal structure and a preferred orientation with the c-axis perpendicular to the substrate. Only the (002) peak is observed.High quality films with resistivity as Iow as 1.0 x 10- 3Ω@ cm and 8.4 x 10- 4Ω@ cm, the average transmittance over 74% and 85% in the wavelength range of the visible spectrum have been obtained on different substrates.     

属间远缘杂交水稻耐旱性生理特性的比较研究

采用在ＹＯＳＨＩＤＡ水稻专用培养营养液中添加一定量的ＰＥＧ ６０００的方法，比较研究了模拟干旱胁迫条件下属间远缘杂交新型水稻品种“远诱１号”（Ｙ）及其水稻亲本“圭６３０”（Ｇ）、高梁亲本“桃长红”（Ｔ）以及生产推广杂交组合“汕优６３”（Ｓ）等试验材料某些生态生理特性的差异。研究结果表明，在－１．０ＭＰａ的高渗胁迫下，Ｙ、Ｇ、Ｔ的萌发系数均有不同程度的下降，正常培养条件下的萌发系数ＧＣ分别为３６．９     

(111)择优取向的Pb(Zr0.52Ti0.48)O3铁电薄膜的制备及研究

选用不同浓度的Pb(Zr_0.52Ti_0.48)O₃溶胶，用Sol-gel法在Pt/Ti/SiO₂/Si基片上沉积一层厚度不同的Pb(Zr_0.52Ti_0.48)O₃ (PZT52)过渡层，经400℃烘烤、550℃退火等程序后，再用Sol-gel法在PZT52过渡层上沉积Pb(Zr_0.52Ti_0.48)O _{关键词： PZT铁电薄膜 择优取向 过渡层 剩余极化强度}     

Au-Au2S复合纳米球壳微粒的空腔谐振及参量讨论

Au-Au2S复合纳米球壳微粒（金纳米球壳），是一种新型复合结构的纳米微粒，其结构为纳米级的Au2S介质球外包裹了一层几个纳米厚的黄金球壳。这种复合纳米球壳微粒可以被抽象为球型谐振腔。报道了它的空腔谐振吸收的实验结果，并且运用经典理论结合介观结构特征，讨论了有关Au-Au2S复合纳米球壳微粒空腔谐振吸收的一些重要参量，其中包括谐振吸收波长、品质因数、谐振能量等。另外，还讨论了金球壳的厚度对这些重要参量的影响。