脂松香、石炭酸松香树脂和马林酸松香树脂的红外光谱剖析及鉴别

本文对脂松香、石炭酸松香树脂和马林酸松香树脂的红外光谱剖析及鉴别，方法快速，简便，准确。     

含松香骨架的新型手性季铵盐相转移催化剂的合成及其在不对称环氧化反应中的应用

以天然松香为原料合成了4个新型手性季铵盐类相转移催化剂, 并用于催化不对称查尔酮环氧化反应, 发现这类手性相转移催化剂可以有效地催化查尔酮的不对称环氧化, 环氧化产物ee最高达20%.     

Preparation and characterization of rosin glycerin ester and its bromide

Rosin glycerin ester and its bromide were prepared from natural renewable rosin, glycerin and liquid bromine which were first subjected to an esterification reaction, followed by an addition reaction. Their structures were characterized by an infrared (IR) spectrum and their thermal resistance was conducted with thermal gravity (TG) and differential scanning calorimetry (DSC). It showed that the bromide in the rosin glycerin ester decomposed faster than the ester; hence it may be used as fire-resistant material.     

Kinetic study of the reaction of nucleophilic cyclopropanation of C60 fullerene with halogenated maleopimarimide

The kinetics of nucleophilic fullerene cyclopropanation by halomethyl ketones with a diterpene fragment has been studied by the Bingel method, and the influence of the biologically active cyclopropanating agent on the process has been estimated. It has been revealed that favorable conditions for carrying out the reaction result in maximum monofunctionalized methanofullerenes formation with the maximum yield.     

Branched plasticizers derived from eugenol via green polymerization for low/non-migration and externally/internally plasticized polyvinyl chloride materials

The synthesis of nontoxic plasticizers derived from the waste residues of the rosin-processing industry can reduce pollution and promote the high-value utilization of the waste residues of rosin. In this study, four kinds of sustainable branched plasticizers derived from a biomass resource, eugenol (derived from the waste residues of the rosin processing industry), were synthesized via one-pot solvent free polymerization and used to plasticize polyvinyl chloride (PVC). Internally plasticized PVC was fabricated using thiolated DPE (branched plasticizers based on eugenol). The thermal stability, tensile properties, microstructure, volatility behavior, and solvent extraction resistance of plasticized PVC were investigated. Compared with the behavior of the commercial plasticizer dioctyl phthalate, the thermal stability, plasticizing efficiency, and migration resistance of the branched plasticizers are superior. The acute oral toxicity dose of each branched plasticizer was extremely high at 5000 mg/kg of body weight, with no deaths among test animals. Compared with externally plasticized PVC, the internally plasticized PVC showed zero weight loss in volatility and leaching tests despite its less effective plasticization. All the branched plasticizers have potential application in plastic products.     

松香改性酚醛环氧树脂的合成与表征

以松香,环氧氯丙烷,甲醛及苯酚等为主要原料,合成了一种新型的环氧树脂。通过正交实验法确定了环氧化反应的最佳实验条件,即环氧化温度90℃,碱用量13 g,催化剂为cat 1,其最佳用量为0.018 mol,环氧氯丙烷的用量为50 g,碱浓度为30%(以上数值均以松香用量为70 g时计)。在最佳实验条件下合成得到了松香改性酚醛环氧树脂(简称RAPE),并用HPLC、FT-IR、NMR对其进行结构表征。结果表明,得到的RAPE其环氧值为0.28 mol/100g,平均聚合度约为3.4,酚羟基和树脂酸上的羧基基本反应完全,得到一种新型的缩水甘油醚型和缩水甘油酯型的环氧树脂。     

基于纳米镍催化的松香加氢研究--树酯酸组成的研究

松香的主要成份是枞酸型树脂酸,其因共轭双键的存在而易被氧化,大大降低了其附加值。经氢化后的松香具有抗氧性好、脆性小、热稳定性高、颜色浅等特点,因而广泛应用于胶粘剂、合成橡胶、涂料、油黑、造纸、电子、食品等工业部门[1]。采用催化加氢的方法可使枞酸型树脂酸中的共轭双键消除[2]。以枞酸为代表的反应式为:松香催化加氢主要有熔融法[3]和溶剂法[4],所用催化剂主要是Pd和N i。熔融法制氢化松香,当反应温度低于200℃时,枞酸加氢速度较慢,反应不完全。温度升高,氢化松香中枞酸含量显著地减少,但温度高于250℃时,树脂酸脱羧严重,甚至…     

二氯化-N,N-′-二(3-脱氢松香酰氧-2-羟丙基)四甲基乙二胺的合成与性能

研究了Gemini表面活性剂中疏水"尾巴"结构对性质的影响,以脱氢松香酸和环氧氯丙烷为原料合成了中间体3-脱氢松香酰氧-2-羟丙基氯,再与四甲基乙二胺反应,得到1种以脱氢松香酰基为疏水链"尾巴"的对称Gemini型双季铵盐阳离子表面活性剂:二氯化-N,N′-二(3-脱氢松香酰氧-2-羟丙基)四甲基乙二胺。在合成工艺条件的基础上,采用IR光谱、MS谱和元素分析测试技术对产物进行了结构确认。结果表明,该产物可降低水的表面张力达34.9 mN/m,临界胶束浓度为1.0×10-4mol/L。表明具有良好疏水性能的2个大"尾巴"使合成的Gemini表面活性剂更易形成胶束,大大提高了表面活性。     

杂多酸催化松香裂解反应研究

对杂多酸 (HPA)催化松香裂解反应及反应条件进行了研究 ,并对裂解产生的挥发油进行了气相色谱分析。研究内容包括反应温度、反应时间、催化剂种类及用量对反应结果的影响。结果表明 :在杂多酸催化剂用量大于 0 .0 5%、反应温度高于 1 80℃的条件下 ,杂多酸可将松香裂解为深色油状物 ,同时生成水和挥发性油。杂多酸的种类、用量以及反应温度的改变不影响裂解产生的挥发油的组分构成 ,但影响某些组分的相对比例。裂解反应包括了碳碳键和碳氢键的断裂     

松香中枞酸型树脂酸的MNDO研究

应用半经验MNDO量子化学计算方法确定了松香中4种枞酸型树脂酸的优化几何构型及相对能量，据此对该类树脂酸分子的构象及相对稳定性作了分析与预测，并与已知的实验结果作了对比。