全文获取类型
收费全文 | 156篇 |
免费 | 26篇 |
国内免费 | 107篇 |
专业分类
化学 | 259篇 |
晶体学 | 3篇 |
力学 | 2篇 |
物理学 | 25篇 |
出版年
2023年 | 1篇 |
2022年 | 3篇 |
2021年 | 6篇 |
2020年 | 6篇 |
2019年 | 4篇 |
2018年 | 7篇 |
2017年 | 4篇 |
2016年 | 11篇 |
2015年 | 8篇 |
2014年 | 16篇 |
2013年 | 8篇 |
2012年 | 18篇 |
2011年 | 22篇 |
2010年 | 19篇 |
2009年 | 17篇 |
2008年 | 21篇 |
2007年 | 14篇 |
2006年 | 25篇 |
2005年 | 14篇 |
2004年 | 15篇 |
2003年 | 15篇 |
2002年 | 7篇 |
2001年 | 13篇 |
2000年 | 4篇 |
1999年 | 4篇 |
1998年 | 3篇 |
1997年 | 3篇 |
1993年 | 1篇 |
排序方式: 共有289条查询结果,搜索用时 31 毫秒
1.
Chunlin Li Yilu Fu Guozhu Bian Tiandou Hu Yaning Xie Jing ZhanDepartment of Chemical Physics University of Science and Technology of China Hefei China Institute of High Energy Physics Chinese Academy of Sciences Beijing China 《天然气化学杂志》2003,12(3)
The Ni/CeO2-ZrO2-Al2O3 catalyst with different Al2O3 and NiO contents were prepared by hydrothermal synthesis method. The catalytic performance for CO2 reforming of CH4 reaction, the interaction among components and the relation between Ni content and catalyst surface basicity were investigated. Results show that the interaction between NiO and Al2O3 is stronger than that between NiO and CeO2-ZrO2.The addition of Al2O3 can prevent the formation of large metallic Ni ensembles, increase the dispersion of Ni, and improve catalytic activity, but excess Al2O3 causes the catalyst to deactivate easily. The interaction between NiO and CeO2 results in more facile reduction of surface CeO2. The existence of a small amount of metallic Ni can increase the number of basic sites. As metallic Ni may preferentially reside on the strong basic sites, increasing Ni content can weaken the catalyst basicity. 相似文献
2.
3.
Feng-Yun Wang Soofin Cheng Chen-Hung Chung Ben-Zu Wan 《Journal of Solid State Electrochemistry》2006,10(11):879-885
Electrolytes of Ce1-x-y
Y
x
Mg
y
O2-0.5x-y
were prepared with citrate method and were characterized by inductively coupled plasma-atomic emission spectrometry, energy dispersive spectrometry, powder X-ray diffraction, and impedance spectroscopy. The effect of composition on the structure, conductivity, and stability of the electrolytes were investigated. When 0≤x≤ about 0.2 and 0≤y≤ about 0.05, the electrolytes were all single phase materials of ceria-based solid solution. However, when y> about 0.05, the electrolytes became two-phase materials, Y3+ and Mg2+ co-doped ceria-based solid solution and free MgO. The sample with nominal composition of Ce0.815Y0.065Mg0.12O2-d
showed ionic conductivity at 973 K close to or even a little higher than that of similarly prepared Ce0.9Gd0.1O1.95, but had lower cost of raw materials and a little better stability in reducing atmosphere. The existing of free MgO improved the stability of the electrolytes in reducing atmosphere, but too much free MgO reduced the conductivity. 相似文献
4.
E.?V.?TsipisEmail author V.?V.?Kharton I.?A.?Bashmakov E.?N.?Naumovich J.?R.?Frade 《Journal of Solid State Electrochemistry》2004,8(9):674-680
Developments of intermediate-temperature solid oxide fuel cells (IT SOFCs) require novel anode materials with a high electrochemical activity at 800–1070 K. The polarization of cermet anodes, made of nickel, ceria and yttria-stabilized zirconia (YSZ) and applied onto a YSZ solid electrolyte, can be significantly reduced by catalytically active ceria additions, the relative role of which increases with decreasing temperature. Further improvement is observed when using Ce0.8Gd0.2O2–
(CGO) having a high oxygen ionic conductivity instead of undoped ceria, owing to enlargement of the electrochemical reaction zone. Nanocrystalline CGO powders with grain sizes of 8–35 nm were thus synthesized via the cellulose-precursor technique and introduced into Ni–CGO–YSZ cermets, and tested in contact with a (La0.9Sr0.1)0.98Ga0.8Mg0.2O3–
(LSGM) electrolyte at 873–1073 K. The results showed that the anode performance can be enhanced by additional surface activation, in particular by impregnation with a Ce-containing solution, and also by incorporation of YSZ, which probably acts as a cermet-stabilizing component. The overpotential of the surface-modified Ni–CGO (25 wt%–75 wt%) anode in a 10% H2/90% N2 atmosphere was approximately 110 mV at 1073 K with a current density of 200 mA/cm2.Presented at the OSSEP Workshop Ionic and Mixed Conductors: Methods and Processes, Aveiro, Portugal, 10–12 April 2003 相似文献
5.
Xiucheng Zheng Xiaoli Zhang Shuping Wang Xiangyu Wang Shihua Wu 《天然气化学杂志》2007,16(2):179-185
In this work, we have reported the influence of the addition of base (KOH) on the physicochemical property of ceria synthesized by alcohothermal process, and the alcohothermal mechanism was also put forward. Furthermore, the prepared CeO2 was used as the support to prepare CuO/CeO2 catalysts via the wet impregnation method. The samples were characterized by N2 adsorption-desorption, X-ray powder diffraction (XRD), high resolution transmission electron microscopy (HRTEM), and temperature-programmed reduction by H2 (H2-TPR). The catalytic properties of the CuO/CeO2 catalysts for low-temperature CO oxidation were studied using a microreactor-GC system. The crystal size of CeO2-A was much smaller than that of CeO2-B, and the corresponding copper oxide catalysts exhibited higher catalytic activity than that of the CeO2-B-supported catalysts under the same reaction conditions. The alcohothermal mechanism indicated that KOH plays a key role in determining the physicochemical and catalytic properties of ceria-based materials. 相似文献
6.
水合醋酸铈直接热分解制备超细氧化铈及其抛光性能 总被引:3,自引:0,他引:3
Ultra fine ceria was prepared by calcining hydrate cerium acetate. The effects of pyrolysis temperature on the particle size, morphology, specific surface area and loose packing density of ceria were investigated, and the removal rate of optical glasses polishing by ceria was determined. The results show that with the increase of pyrolysis temperature, the loose deposit density and crystallinity increases and the specific surface area decreases, however, the particle size decreases firstly and then increases, the minimum medium particle size D50 is 0.47 μm at pyrolysis temperature of 1 000 ℃. The SEM images of ceria prepared by the decomposition at 800 ℃ or at 1 100 ℃ show porous powders or quasi-sphere small particles with loosely agglomeration, respectively. It was found that the removal rate varied with pyrolysis temperature in preparation of ceria and the property of glass polished. The removal rate for three kinds of glasses was in the order of ZF7> F1> K9, and the maximum value appeared at around 1 000 ℃ for ZF7 and F1, and at around 1 100 ℃ for K9. 相似文献
7.
采用脉冲D2反应研究了CeO2在Co-CeO2/SiO2费托合成催化剂中的作用机理. 通过比较在Co-CeO2/SiO2和Co/SiO2催化剂上的脉冲D2反应实验结果发现, CeO2可以提高载体表面 Si-OH 的H-D同位素交换活性和 Si-OH 中H参与CO加氢反应的活性; CeO2不仅增加了催化剂表面活性碳物种的总量,而且活性碳物种以链增长单体-CH2-为主,因而有利于增加费托合成反应速率和链增长几率; CeO2的加入明显提高了催化剂表面碳原子的加氢反应速率,从而减少了碳沉积. 相似文献
8.
Duncan?P.?FaggEmail author Vladislav?V.?Kharton Jorge?R.?Frade 《Journal of Solid State Electrochemistry》2004,8(9):618-625
Small (2 mol%) cobalt oxide additions to ceria-gadolinia (CGO) materials considerably improve sinterability, making it possible to obtain ceramics with 95–99% density and sub-micrometre grain sizes at 1,170–1,370 K. The addition of Co causes a significant shift of the electrolytic domain to lower pO2. This modification to the minor electronic conductivity of the electrolyte material has influence on the cathodic oxygen reduction reaction. The impedance technique is shown to provide information not only about polarisation resistance, but also about the active electrode area from analysis of the current constriction resistance. It is demonstrated that this current constriction resistance can be related to the minor electronic contributions to total conductivity in these materials. A simple imbedded grid approach gives control of the contact area allowing the properties of the electrolyte materials to be studied. A much lower polarisation resistance for the Co-containing CGO electrolyte is observed, which can be clearly attributed to an increased three-phase reaction area in the Co-containing material, as a consequence of elevated p-type conductivity. 相似文献
9.
水热法制备高纯超细CeO2-ZrO2复合氧化物 总被引:9,自引:0,他引:9
Superfine composite powders of CeO2-ZrO2 (CZ) and CeO2-ZrO2-La2O3 (CZL) were prepared by hydrothermal method. The effects of pH、temperature and time for hydrothermal process on the performance of the resulting powders were studied. The optimized reaction parameters were on follows: the precursor′s pH≈9.0, hydrothermal temperature of 200 ℃ holding for 2 h. Thermal stable powders with average particle size smaller than 10 nm and specific surface area of 171 m2·g-1 were obtained. A BET specific surface area was still at 44 m2·g-1 after calcination at 1 000 ℃ for 6 hours. 相似文献
10.
Werner Unterberger Bernd Jenewein Bernhard Kl?tzer Simon Penner Wolfgang Reichl Günther Rupprechter Di Wang Di Wang Robert Schl?gl Konrad Hayek 《Reaction Kinetics and Catalysis Letters》2006,87(2):215-234
Summary The effect of hydrogen reduction on the structure and catalytic properties of “thin film”and “inverse”model systems for supported
metal catalysts is discussed. Thin film model catalysts were obtained by epitaxial growth of Pt and Rh nanoparticles on NaCl(001),
which were coated with amorphous or crystalline supports of alumina, silica, titania, ceria and vanadia. Structural and morphological
changes upon hydrogen reduction between 473 and 973 K were examined by high resolution electron microscopy. Metal-oxide interaction
sets in at a specific reduction temperature and is characterized by an initial “wetting”stage, followed by alloy formation
at increasing temperature, in the order VOx< TiOx< SiO2< CeOx< Al2O3. “Inverse”model systems were prepared by deposition of oxides on a metal substrate, e.g. VOx/Rh and VOx/Pd. Reduction of inverse systems at elevated temperature induces subsurface alloy formation. In contrast to common bimetallic
surfaces, the stable subsurface alloys of V/Rh and V/Pd have a purely noble metal-terminated surface, with V positioned in
near-surface layers. The uniform composition of the metallic surface layer excludes catalytic ensemble effects in favor of
ligand effects. Activity and selectivity, e.g. for CO and CO2methanation and for partial oxidation of ethene, are mainly controlled by the temperature of annealing or reduction. Reduction
above 573 K turned out to be beneficial for the catalytic activity of the subsurface alloys, but not for the corresponding
thin film systems which tend to deactivate viaparticle encapsulation.</o:p> 相似文献