含二苯甲烷结构四元共缩聚杂萘聚芳酰胺的合成与性能

采用自制二胺1,2-二氢-2-(4-氨基苯基)-4-[4-(4-氨基苯氧基)-苯基]-二氮杂萘-1-酮、商品二胺4,4′-二氨基二苯甲烷和对苯二胺与对苯二甲酰氯进行低温溶液缩聚反应,改变三种二胺的比例,得到了一系列共聚酰胺树脂,其特性粘数为1·24~2·32dL/g,用FT-IR、1H-NMR手段研究了聚合物的结构;利用DSC和TGA研究了聚合物的耐热性能,结果表明,该类聚合物具有较高玻璃转化温度(301℃以上);氮气气氛中5%热失重温度在438℃以上;用一定比例的二胺制得的聚合物分别能溶于N-甲基吡咯烷酮、N,N-二甲基乙酰胺等非质子极性溶剂中并浇注得到韧性薄膜.     

Synthesis and characterization of new soluble poly（aryl ether nitrile）s containing phthalazinone moiety

A series of novel poly（aryl ether nitrile）s containing phthalazinone moiety were synthesized by the nucleophilic displacement reaction of bisphenol-like monomers （I） with 2,6-difluorobenzonitrile. The inherent viscosities ranged from 0.46 to 1.07 dL g^-1. The glass transition temperatures were in the range of 277-295℃, and the temperatures for 10% weight loss in nitrogen atmosphere were found between 495 and 527 ℃. The structures of these resultant polymers were confirmed by FT-IR and 1^H NMR. Moreover, the properties of poly（aryl ether nitrile）s including solubility and crystallinity were also studied.     

Lyotropic liquid crystalline poly(aryl ether ketone) copolymer containing phthalazinone moiety and biphenyl mesogen

A novel lyotropic liquid crystalline material poly(aryl ether ketone) copolymer containing phthalazinone moiety and biphenyl mesogen named P-8515 was developed by a mild solution polycondensation method. The molecular weight (M_n) was 53,000 and the value of molecular weight distribution index (MDI) was 2.49 detected by GPC. The critical concentration (C^∗) of P-8515 was 36 wt% and P-8515 exhibited characteristic nematic lyotropic liquid crystalline phases in NMP solution at different concentrations and the phase morphology changed to a typical threaded texture when shear forces were induced from PLM observations. The T_g value was 238 °C and the value for 5% weight loss temperature was 515 °C in nitrogen from DSC and TGA determinations, respectively.     

Allyl phthalazinone synthesis,polymerization and polymer properties

A phthalazinone monomer with an allyl group, i.e. 4-（3-allyl-4-hydroxyphenyl）phthalazin-1（2H）-one, was synthesized and then copolymerized with 4-（4-hydroxylphenyl）（2H）-phthalazin-1-one and 2,6- diflurobenzonitrile by means of aromatic nucleophilic polycondensation to provide a series of crosslinkable poly（aryl ether nitrile）s. The virgin copolymers exhibited good solubility in polar organic solvents with relative high molecular weights （Mw： 45,130-58,403, inherent viscosities： 0.58-0.75 dL/ g）. After cross-linking, the thermal stability and solvent resistance of the polymer increased.     

含二氦杂萘酮结构全芳香杂环聚合物的研究进展

高性能高分子材料在高温下仍保持优异的综合性能,是航空航天、电子电气、高速轨道交通等重要高技术领域不可或缺的材料。在不牺牲耐热性能的前提下改善高性能聚合物的加工性能一直是国内外研究的热点。含二氮杂萘酮结构高性能聚合物是高性能高分子材料的新成员。本文主要综述了含二氮杂萘酮结构的聚芳醚（包括聚芳醚砜酮系列、聚芳醚腈砜酮系列、...     

用于燃料电池质子交换膜的含萘及氮杂环结构的新型磺化聚酰亚胺的合成及性能

将自制的4,4'-二氨基二苯醚-2,2'-二磺酸基(ODADS)、 含氮杂环芳香二胺1,2-二氢-2-(4-氨基苯基)-4-[4-(4-氨基苯氧基)-苯基]-二氮杂萘-1-酮(DHPZ-DA)和1,4,5,8-萘四甲酸二酐(NTDA)进行直接缩合聚合反应, 通过改变磺化二胺单体的含量来改变聚合物的磺化度, 成功地合成了一系列高分子量的不同磺化度的六元环聚酰亚胺(SPIs), 其特性粘度在0.55-1.47 dL/g. 采用FTIR和 1H NMR技术表征了聚合物的结构. 研究了经溶液浇铸成磺化聚合物膜的理化性质. 结果表明, 随着聚合物磺化度的增大, 膜的含水率和离子交换能力增大, 尺寸稳定性、 对水的稳定性以及抗氧化性降低.     

Synthesis and characterization of novel poly（aryl ether sulfone ketone）s containing phthalazinone and biphenyl moieties

A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures （Tg） and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction （WAXD）.     

SYNTHESIS AND CHARACTERIZATION OF POLY(PHTHALAZINONE ETHER PHOSPHINE OXIDE)S BY N―C COUPLING REACTION

<正>Based on several unsymmetrical,twist,noncoplanar phthalazinone-containing monomers 2a-2e and an active bis(4-fluorophenyl)phenyl phosphine oxide(BFPPO) monomer,a series of novel poly(phthalazinone ether phosphine oxide)s (PPEPO) was synthesized by anhydrous K_2CO_3 mediated N—C coupling reaction in DMAc.The polymers exhibited good thermal properties with T_gs ranging from 267℃to 306℃and 5%weight loss temperatures in nitrogen higher than 430℃, together with high char yield upon prolonged heating at 800℃(35%—56%).Moreover,the polymers were readily soluble in common organic solvents,such as N-methyl-2-pyrrolidone,chloroform and m-cresol.These polymers had inherent viscosities in the range of 0.45-0.72 dL/g and could be cast into flexible and colorless films by spin coating or casting approach.     

SYNTHESIS AND CHARACTERIZATION OF POLY(PHTHALAZINONE BIPHENYL ETHER SULFONE KETONE)S FROM 4,4'-DICHLOROBENZOPHENONE

A series of poly(aryl ether sulfone ketone)s containing phthalazinone and biphenyl moieties were synthesized by aromatic nucleophilic displacement polycondensation of 4-(4-hydroxylphenyl)(2H)-phthalazin-1-one(DHPZ),4,4'- dichlorobenzophenone(DCB),4,4'-dichlorodiphenyl sulfone(DCS) and 4,4'-biphenol(BP) in different molar ratios.The obtained copolymers were characterized by different instrumental techniques(FTIR,TGA,DSC,WAXD,etc.).The inherent viscosities of these polymers were in the range of 0.43-0.56 d...     

4,4’-二氯二苯酮合成二氮杂萘联苯酮结构聚醚砜酮的研究

以4-(4-羟基苯基)*2,3-二氮杂萘-1-酮(DHPZ)、4,4’-二氯二苯砜(DCS)和4,4’-二氯二苯酮(DCK)为原料,采用分步加料的方法,合成了系列高分子量的聚芳醚砜酮共聚物(PPESKs),其特性黏度在0.40 ～0.61dL/g之间,解决了由于DCK活性低不适合用于聚芳醚合成的问题.采用FTIR、示差...