Nanocomposite hydrogel consisting of Na‐montmorillonite with enhanced mechanical properties

A new kind of nanocomposite (NC) hydrogel with Na‐montmorillonite (MMT) is presented in this article. The NC hydrogels were synthesized by free radical copolymerization of acrylamide and (3‐acrylamidopropyl) trimethylammonium chloride (ATC) in the presence of MMT and N,N′‐methylene‐bis‐acrylamide used as chemical cross‐linker. Due to the cation‐exchange reaction between MMT and ATC (cationic monomer) during the synthesis of NC hydrogels, MMT platelets were considered chemical “plane” cross‐linkers, different from “point” cross‐linkers. With increasing amount of MMT, the crosslinking degree enhanced, causing a decrease of the swelling degree at equilibrium. Investigations of mechanical properties indicated that NC hydrogels exhibited enhanced strength and toughness, which resulted from chemical interaction between exfoliated MMT platelets and polymer chains in hydrogels. Dynamic shear measurements showed that both storage modulus and loss modulus increased with increasing MMT content. The idea described here provided a new route to prepare hydrogels with high mechanical properties by using alternative natural Na‐MMT. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1020–1026     

Strategies for synthesizing non-bioaccumulable alternatives to PFOA and PFOS

This minireview describes the strategies for synthesis of fiuorinated surfactants potentially nonbioaccumulable.Various strategies have been focused on(Ⅰ) reducing the length of the perfluorocarbon chain,(Ⅱ) introducing hetero atoms into the fluorocarbon chain,(Ⅲ) introducing branch(herein and after branch means the fluoro-carbon chain section is not straight).In most cases,the surface tensions versus the surfactant concentrations have been assessed.These above strategies led to various highly fiuorinated(perfluorinated or not perfluorinated) surfactants whose chemical changes enabled to obtain novel alternatives to perfluorooctanoic acid(PFOA) and perfluorooctane sulphonate(PFOS).     

Naphthalimide‐phthalimide derivative based photoinitiating systems for polymerization reactions under blue lights

Naphthalimide‐phthalimide derivatives (NDPDs) have been synthesized and combined with an iodonium salt, N‐vinylcarbazole, amine or 2,4,6‐tris(trichloromethyl)‐1,3,5‐triazine to produce reactive species (i.e., radicals and cations). These generated reactive species are capable of initiating the cationic polymerization of epoxides and/or the radical polymerization of acrylates upon exposure to very soft polychromatic visible lights or blue lights. Compared with the well‐known camphorquinone based systems used as references, the novel NDPD based combinations employed here demonstrate clearly higher efficiencies for the cationic polymerization of epoxides under air as well as the radical polymerization of acrylates. Remarkably, one of the NDPDs (i.e., NDPD2) based systems is characterized by an outstanding reactivity. The structure/reactivity/efficiency relationships of the investigated NDPDs were studied by fluorescence, cyclic voltammetry, laser flash photolysis, electron spin resonance spin trapping, and steady state photolysis techniques. The key parameters for their reactivity are provided. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 665–674     

Fluorine containing phosphazene polymers

In this paper we highlighted the synthesis, characterization, and practical exploitation of different types of polyphosphazenes substituted with fluorinated groups. There are several ways in which fluorine atoms can be inserted into polyphosphazenes, all of which leading to different polymers showing a wide range of characteristics. In general it is true that the insertion of fluorine atoms into phosphazene macromolecules leads to an enhancement of the thermal stability, flame resistance, low-temperature elastomericity, and chemical inertness of the phosphazenes obtained. The contribution of Italian research groups to the preparation and exploitation of organic commercial macromolecules grafted onto fluorinated polyphosphazenes is also reviewed.     

UV‐ignited frontal polymerization of an epoxy resin

By combining frontal polymerization and radical‐induced cationic polymerization, it was possible to cure thick samples of an epoxy monomer bleached by UV light. The effect of the relative amounts of cationic photoinitiator and radical initiator was thoroughly investigated and was related to the front's velocity and its maximum temperature. The materials obtained were characterized by quantitative conversion also in the deeper layers, not reached by UV light. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2066–2072, 2004     

Cationic polymerization of styrene in a neutral ionic liquid

The cationic polymerization of styrene in a neutral ionic liquid, 1‐butyl‐3‐methylimidazolium hexafluorophosphate, with a 1‐phenetyl chloride/TiCl₄ initiating system is reported. The polymerization proceeds to a high conversion, but an analysis of the matrix‐assisted laser desorption/ionization time‐of‐flight spectra of the polymers indicates that chain transfer is significant, leading to a lack of control over the molecular weight and molecular weight distribution. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3230–3235, 2004     

Dark cure studies of cationic photopolymerizations of epoxides: Characterization of kinetic rate constants at high conversions

The effective propagation rate constant (k_p; averaged over all the propagating active centers) was characterized for solvent‐free cationic photopolymerizations of phenyl glycidyl ether over the entire range of conversions, including the high conversion regime in which mass transfer limitations become important. The profile for the k_p as a function of conversion was found to exhibit a constant plateau value at low to intermediate conversions, followed by a monotonic increase above a threshold value of conversion. To explain this trend, it is proposed that at high conversion the diffusional mobility of the photoinitiator counterion is reduced whereas the mobility of the cationic active center remains high because of reactive diffusion. Therefore, with increasing conversion, the average distance between the active centers and counterions may increase, resulting in an increase in the propagation rate constant. The profiles for the k_p values were investigated as a function of the temperature, photoinitiator anion, and photoinitiator concentration. As the photoinitiator concentration was increased, the plateau value of the effective propagation rate constant decreased whereas the threshold conversion increased. All of the experimental trends are consistent with the proposed increase in ion separation at high conversions. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4409–4416, 2004     

Tetrafunctional initiators for cationic polymerization of olefins

3,3′,5,5′‐Tetrakis(2‐chloro‐2‐propyl)biphenyl (biphenyl tetracumyl chloride, BPTCC) and 1,3‐bis[3,5‐bis(2‐chloro‐2‐propyl)phenoxy]propane (diphenoxypropane tetracumyl chloride, DPPTCC) were synthesized as initiators for quasiliving cationic polymerization of isobutylene (IB). In the synthesis of BPTCC, tetrafunctionality was achieved via the coupling of dimethyl 5‐bromoisophthalate (DMBI) using nickel dibromide bis(triphenylphosphine) and zinc in the presence of a base; in the synthesis of DPPTCC, two equivalents of dimethyl 5‐hydroxyisophthalate were linked via reaction with 1,3‐dibromopropane in the presence of potassium carbonate. Both initiators were used to initiate the polymerization of IB under quasiliving cationic polymerization conditions. PIB initiated from BPTCC revealed a chain end/molecule value (as determined by ¹H‐NMR) of 3.85, verifying the nearly exclusive production of 4‐arm polyisobutylene (PIB). GPC analysis revealed a narrow peak representing the target four‐arm PIB, with a slight shoulder at high elution volumes (low molecular weights). GPC analysis of the PIB initiated by DPPTCC revealed multimodal distributions, suggesting the formation of two‐, three‐, and four‐arm star polymers during the polymerization. This behavior was attributed to Friedel–Crafts alkylation of the initiator core after the addition of one IB unit, which was activated by the electron‐donating oxytrimethyleneoxy linking moiety. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5942–5953, 2004     

Controlled synthesis of amphiphilic biodegradable polylactide‐grafted dextran copolymers

The whole controlled synthesis of novel amphiphilic polylactide (PLA)‐grafted dextran copolymers was achieved. The control of the architecture of such biodegradable and potentially biocompatible copolymers has required a three‐step synthesis based on the “grafting from” concept. The first step consisted of the partial silylation of the dextran hydroxyl groups. This protection step was followed by the ring‐opening polymerization of D ,L ‐lactide initiated from the remaining OH functions of the partially silylated polysaccharide. The third step involved the silylether group deprotection under very mild conditions. Based on previous studies, in which the control of the first step was achieved, this study is focused on the last two steps. Experimental conditions were investigated to ensure a controlled polymerization of D ,L ‐lactide, in terms of grafting efficiency, graft length, and transesterification limitation. After polymerization, the final step was studied in order to avoid degradation of both polysaccharide backbone and polyester grafts. The chemical stability of dextran backbone was checked throughout each step of the synthesis. PLA‐grafted dextrans and PLA‐grafted (silylated dextrans) were proved to adopt a core‐shell conformation in various solvents. Furthermore, preliminary experiments on the potential use of these amphiphilic grafted copolymers as liquid/liquid interface stabilizers were performed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2577–2588, 2004     

Desorption behavior of a surfactant in a linear low‐density polyethylene blend at elevated temperatures

The desorption behavior of a surfactant in a linear low‐density polyethylene (LLDPE) blend at elevated temperatures of 50, 70, and 80 °C was studied with Fourier transform infrared spectroscopy. The composition of the LLDPE blend was 70:30 LLDPE/low‐density polyethylene. Three different specimens (II, III, and IV) were prepared with various compositions of a small molecular penetrant, sorbitan palmitate (SPAN‐40), and a migration controller, poly(ethylene acrylic acid) (EAA), in the LLDPE blend. The calculated diffusion coefficient (D) of SPAN‐40 in specimens II, III, and IV, between 50 and 80 °C, varied from 1.74 × 10^?11 to 6.79 × 10^?11 cm²/s, from 1.10 × 10^?11 to 5.75 × 10^?11 cm²/s, and from 0.58 × 10^?11 to 4.75 × 10^?11 cm²/s, respectively. In addition, the calculated activation energies (E_D) of specimens II, III, and IV, from the plotting of ln D versus 1/T between 50 and 80 °C, were 42.9, 52.7, and 65.6 kJ/mol, respectively. These values were different from those obtained between 25 and 50 °C and were believed to have been influenced by the interference of Tinuvin (a UV stabilizer) at elevated temperatures higher than 50 °C. Although the desorption rate of SPAN‐40 increased with the temperature and decreased with the EAA content, the observed spectral behavior did not depend on the temperature and time. For all specimens stored over 50 °C, the peak at 1739 cm^?1 decreased in a few days and subsequently increased with a peak shift toward 1730 cm^?1. This arose from the carbonyl stretching vibration of Tinuvin, possibly because of oxidation or degradation at elevated temperatures. In addition, the incorporation of EAA into the LLDPE blend suppressed the desorption rate of SPAN‐40 and retarded the appearance of the 1730 cm^?1 peak. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1114–1126, 2004