Thermal degradation behaviour of poly(vinyl chloride) in the presence of poly(N′-acryloyl benzhydrazide)

The thermal degradation behaviour of poly(vinyl chloride), PVC, in the presence of poly(N′-acryloyl benzhydrazide), PABH, has been studied using continuous potentiometric determination of the evolved hydrogen chloride gas from the degradation and by measuring the extent of discoloration of the degraded samples. Blending this polymeric additive with dibasic lead carbonate, DBLC, reference stabilizer in different ratios had synergistic effects on both the thermal stability and the extent of discoloration of PVC.     

Vanillin–Schiff’s bases as organic thermal stabilizers and co-stabilizers for rigid poly(vinyl chloride)

Vanillin–Schiff’s bases (VSB) were examined as thermal stabilizers and co-stabilizers for rigid poly(vinyl chloride) (PVC) in air at 180 °C. Their high stabilizing efficiency were shown by their high thermal stability value (Ts), which is the time elapsed for the detection of HCl gas, if compared with dibasic lead carbonate and cadmium–zinc soap reference stabilizers used industrially, with better extent of discoloration. Blending these derivatives with reference stabilizers in different ratios greatly lengthens the thermal stability and the extent of discoloration of the PVC.Condensation products of Vanillin with amines are very active biologically, besides having good complexation ability with metal ions. The Ni²⁺ and Co²⁺ complexes of VSB derivatives gave better thermal stability and less discoloration than the parent organic stabilizer. Also, blending these complexes with either of the used reference stabilizers in different ratios gave better thermal stability and lower extent of discoloration. Thermogravimetric analysis confirmed the improved stability of PVC in the presence of the VSB derivatives, compared to blank PVC, PVC stabilized with reference stabilizers and PVC stabilized with binary mixture of VSB derivatives with reference stabilizer.The stabilizing efficiency of Vanillin–Schiff’s base (VSB) derivatives is attributed to the replacement of the labile chlorine atoms on the PVC chains by a relatively more stable moiety of the organic stabilizer.     

Influence of lanthanum stearate as a co-stabilizer on stabilization efficiency of calcium/zinc stabilizers to polyvinyl chloride

Influence of lanthanum stearate (LaSt₃) as a co-stabilizer on stabilization efficiency of calcium stearate (Ca)/zinc glutarate (Zn) stabilizers to polyvinyl chloride (PVC) at 180 °C in air was investigated. The results showed that combination of LaSt₃ with Ca/Zn stabilizers presented an obvious improvement of stabilization efficiency to PVC compared with the Ca/Zn stabilizers. Moreover, addition of LaSt₃ to the Ca/Zn stabilizers could significantly enhance static stability time of PVC. Incorporation of 2 phr LaSt₃ co-stabilizer to PVC containing 3 phr Ca/Zn stabilizers resulted in marked increase of onset degradation temperature and reductions in average degradation rate as well as the dynamic storage modulus (G′) and loss modulus (G″) at 180 °C. Influence of Ca/Zn ratio on tensile strength of PVC in the absence or in the presence of LaSt₃ was discussed in detail. At low Ca/Zn ratios LaSt₃ had an obvious improvement in the tensile strength, while at high Ca/Zn ratios this effect became inconspicuous.