Grafting of Polymers onto a Crosslinked Polymer Carrying Carboxyl Groups as a Model Compound for Carbon Black

Abstract

A cation-exchange resin (a crosslinked polymer carrying carboxyl groups) was used as a model compound for carbon black, and the grafting of several polymers to the resin was investigated. Reaction of acyl chloride groups that had been placed on the ion-exchange resin with polymers having hydroxyl or amino groups, such as polypropylene glycol, polyethylene glycol, polybutadiene glycol, polyvinyl alcohol, silicone diol, silicone diamine, and polyethyleneimine, resulted in grafting to the ion-exchange resin. In further experiments, primary amino groups were placed on the cation-exchange resin by reaction of acyl chloride groups with ethylenediamine. It was found that ring-opening polymerization of γmethyl L-glutamate N-carboxyanhydride is initiated by the amino groups on the resin, and polypeptide was grafted from the cation-exchange resin. Therefore, the reactivity of carboxyl groups on the resin was found to be similar to that on carbon black. However, carboxyl groups on the resin failed to initiate the cationic polymerization of vinyl monomers, in contrast to those on carbon black. This suggested that the acidity of carboxyl groups on carbon black is greater than on the cation-exchange resin.     

Formation,Characterization, and Stability of Novel Aluminocarbosilazane Macromolecules

Abstract

A novel class of polycarbosilazane?AlCl₃ macromolecules (AlCSZ) with a Si/Al molar ratio of 1 : 1, 2 : 1, and 3 : 1 were prepared by a two‐step reaction, formation of H₂NCH₂CH₂NH₂?AlCl₃ adducts followed by condensation of H₂NCH₂CH₂NH₂ with (CH₃)₂SiCl₂ in an aprotic solvent containing triethylamine base. The resulting AlCSZ materials were examined by elemental analysis, infrared spectroscopy (FT‐IR), mass spectrometry (MS), and powder x‐ray diffraction (XRD). The average polycarbosilazane chain–chain distances in the aluminum‐free polycarbosilazane and these AlCSZ macromolecules were estimated from the XRD data and found to be 5.94, 6.75, 6.88, and 7.19 Å, respectively. This demonstrates that AlCl₃ is incorporated between the polycarbosilzane chains and has caused chain–chain expansion. The thermal properties of these AlCSZs were investigated by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). They are air stable white solids but decompose in water forming the corresponding dimethylsiloxane, ethylenediamine, and aluminum oxide.