In this study, parenchyma cellulose, which was extracted from maize stalk pith as an abundant source of agricultural residues, was applied for preparing cellulose nanoparticles (CNPs) via an ultrasound-assisted etherification and a subsequent sonication process. The ultrasonic-assisted treatment greatly improved the modification of the pith cellulose with glycidyltrimethylammonium chloride, leading to a partial increase in the dissolubility of the as-obtained product and thus disintegration of sheet-like cellulose into nanoparticles. While the formation of CNPs by ultrasonication was largely dependent on the cellulose consistency in the cationic-modified system. Under the condition of 25% cellulose consistency, the longer sono-treated duration yielded a more stable and dispersible suspension of CNP due to its higher zeta potential. Degree of substitution and FT-IR analyses indicated that quaternary ammonium salts were grafted onto hydroxyl groups of cellulose chain. SEM and TEM images exhibited the CNP to have spherical morphology with an average dimeter from 15 to 55 nm. XRD investigation revealed that CNPs consisted mainly of a crystalline cellulose Ι structure, and they had a lower crystallinity than the starting cellulose. Moreover, thermogravimetric results illustrated the thermal resistance of the CNPs was lower than the pith cellulose. The optimal CNP with highly cationic charges, good stability and acceptable thermostability might be considered as one of the alternatively renewable reinforcement additives for nanocomposite production. 相似文献
Iron catalysts have been used widely for the mass production of carbon nanotubes (CNTs) with high yield. In this study, UV/visible spectroscopy was used to determine the Fe catalyst content in CNTs using a colorimetric technique. Fe ions in solution form red–orange complexes with 1,10-phenanthroline, producing an absorption peak at λ=510 nm, the intensity of which is proportional to the solution Fe concentration. A series of standard Fe solutions were formulated to establish the relationship between optical absorbance and Fe concentration. Many Fe catalysts were microscopically observed to be encased by graphitic layers, thus preventing their extraction. Fe catalyst dissolution from CNTs was investigated with various single and mixed acids, and Fe concentration was found to be highest with CNTs being held at reflux in HClO4/HNO3 and H2SO4/HNO3 mixtures. This novel colorimetric method to measure Fe concentrations by UV/Vis spectroscopy was validated by inductively coupled plasma optical emission spectroscopy, indicating its reliability and applicability to asses Fe content in CNTs. 相似文献
Tin and titanium ferrocyanides were studied as adsorbents for alkali metal ions, viz., 134Cs and 22Na, which represent radioactive wastes. The ferrocyanides were prepared in granular form. The tin version contained 11.2% water, while the titanium version contained 17.7% water. The exchange capacities for Cs+ and Na+ in the hydrated tin version were about 1.5 and 0.7 meq/g, respectively, while those in the titanium version were 2.2 and 1.2 meq/g, respectively. Drying at 250°C decimated those capacities. The diffusional time constant of Cs+ at 25°C, determined via Fick's second law, was of order of magnitude 1 × 10–3 s–1, though there were minor differences due to particle size and the form of ferrocyanide. Similarly, the effective diffusivity was of order of magnitude 1 × 10–8 cm2/s. The titanium version responded slightly faster than the tin version. Likewise, equilibrium measurements in mixtures with sodium nitrate, potassium nitrate, or uranium oxide, showed that the titanium version exhibited significantly greater selectivity for Cs+ than did the tin version. Unfortunately, tests of complete elution of the Cs+ from the ferrocyanides were mostly disappointing. Work continues on that subject. 相似文献
Cationic polymer as a kind of flocculant is widely applied in purification treatment of waste water. Because it has positive charge group, it is able to connect strongly the suspended matters, short cellulose and other microparticles. The research on synthesis of cationic polymer and application in treatment of waste water is very universal abroad. But domestic research on those is not general. The technology of synthesis of PEM is simple, and the production cost is low. It is easy to apply in treatment of waste water.Synthesis of PEM Emulsion FlocculantSome distilled water, PVA(poly(vinyl alcohol)), EA(ethyl acrylate), and K2S2O8(potassium persulfate) were put into reaction vessel. Kept stirring up under nitrogen. When heated the solution to 40℃, dropped the water solution of MTA[(2-methacryloxylethyl)trimethyl ammonium].Maintained the temperature at 70℃, reacted about 7-8 hours. Then got the PEM emulsion. Changed the ratio of EA and MTA. Obtained a series of PEM emulsions.Stability and Convertibility of PEM EmulsionThe test results showed that when the EA/MTA was 85/15, the PEM emulsion was most stable.When the total monomer quantity was 35%, the convertibility of PEM emulsion was the highest,i.e.98.6%.The MTA Copolymerization Ratio and Morphology of PEM EmulsionWhen the monomers EA/MTA=85/15 and total monomer quantity was 35%, the MTA copolymerization ratio of PEM emulsion was 95.15%(the highest), and the PEM emulsion was some microspheres with 100-180nm of diameter.The Test Results of PEM Emulsion in Treatment of Waste Water The PEM emulsion flocculant was applied in treatment of waste water of paper mill, and measured the precipitation time(t) and transmittancy(T). The test results were showed in table 1. The optimum value of PEM which was able to make the waste water of paper mill into clear water was 0.008%. 相似文献
Cancer immunotherapy aims at stimulating the immune system to react against cancer stealth capabilities. It consists of repeatedly injecting small doses of a tumor-associated molecule one wants the immune system to recognize, until a consistent immune response directed against the tumor cells is observed.
We have applied the theory of optimal control to the problem of finding the optimal schedule of injections of an immunotherapeutic agent against cancer. The method employed works for a general ODE system and can be applied to find the optimal protocol in a variety of clinical problems where the kinetics of the drug or treatment and its influence on the normal physiologic functions have been described by a mathematical model.
We show that the choice of the cost function has dramatic effects on the kind of solution the optimization algorithm is able to find. This provides evidence that a careful ODE model and optimization schema must be designed by mathematicians and clinicians using their proper different perspectives. 相似文献