溶胶-凝胶制备技术与新型催化材料Ⅲ.溶胶粒子表面修饰方法制备催化膜

提出用溶胶粒子表面修饰方法，结合溶胶凝胶技术制备无机催化膜．该方法的基本原理是利用合适的金属配合物在胶粒表面的吸附作用，经溶胶凝胶过程，将活性组分结合到无机膜中．实验测定结果表明：（ＮｉＥＤＴＡ）２－，ＶＯ－３，ＭｏＯ２－４，（Ｐｄ（ＮＨ３）４）２＋，ＰｄＣｌ２－４，ＰｔＣｌ２－６和ＲｈＣｌ３－６可用来修饰ＡｌＯＯＨ溶胶．以Ｐｄ／γＡｌ２Ｏ３催化膜的制备为例，经三次溶胶凝胶过程，可制得无裂缺的厚度为９μｍ的Ｐｄ／γＡｌ２Ｏ３催化膜，膜材料的平均孔直径为６ｎｍ，Ｐｄ被均匀地分布在膜的顶层，其平均粒径为２３ｎｍ．     

纳米氧化钛-乙二醇溶胶溶液的研究

选用了钛酸丁酯、硬脂酸和乙二醇作为表面活性剂，采用表面化学修饰和表面物理修饰2种方法修饰纳米氧化钛，然后分散在乙二醇溶剂中形成溶胶溶液．并通过红外光谱仪、紫外分光计、原子力显微镜，分析了表面化学修饰后的纳米氧化钛表面化学结构的变化，观测了纳米氧化钛溶胶在乙二醇溶剂中稳定性．试验结果表明表面活性剂与纳米氧化钛的表面的不饱和键之间形成了新的化学结构，粒子表面可能接枝上有机长链，提高了纳米粒子在溶剂中的相容性．表面化学修饰后的纳米氧化钛与乙二醇溶剂形成了较稳定的溶胶体系，而且纳米溶胶粒径较小．表面活性剂添加量与纳米粒子添加量控制在(1～1．2)：1时，可以获得纳米溶胶粒径较小，同时溶胶稳定性较好的纳米氧化钛-乙二醇溶胶体系．     

Electron Holography of Barrier Structures in Co／ZrAlOx／Co Magnetic Tunnel Junctions

We investigate the potential profiles and elemental distribution of barriers in Co/ZrAlOx/Co magnetic tunnel junctions (MTJs) using electron holography (EH) and scanning transmission electron microscopy. The MTJ barriers are introduced by oxidizing a bilayer consisting with a uniform 0.45-nm Al layer and a wedge-shaped Zr layer (0-2 nm). From the scanning transmission electron microscopy, AlOx and ZrOx layers are mixed together, indicating that compact AlOx layer cannot be formed in such a bilayer structure of barriers. The Eli results reveal that there are no sharp interfaces between the barrier and magnetic electrodes, which may be responsible for a smaller tunnelling magnetoresistance compared with the MTJs of Co/AlOx/Co.     

溶胶-凝胶法制备小颗粒(Y,Gd)BO_3∶Eu及其表征

用溶胶 凝胶方法制备了平均粒径为 1～ 2 μm的小颗粒、高发射效率的 (Y ,Gd)BO3 ∶Eu红色发射荧光体。用XRD、SEM、粒度分析和PL光谱对荧光体作了表征和研究。常规固相反应合成 (Y ,Gd)BO3 ∶Eu需在 1 2 0 0℃以上才能形成均一的固溶体。而溶胶 凝胶法制取稀土正硼酸盐 80 0℃灼烧已可形成均一的单相 (Y ,Gd)BO3 ∶Eu,在 1 1 0 0℃可得到发光亮度最高的荧光体。它的亮度是常规固相反应于 1 2 0 0℃制得的荧光体的 1 2 0 %。采用溶胶 凝胶法制取 (Y ,Gd)BO3 ∶Eu荧光体 ,可在相当宽的实验条件范围内得到小粒径、窄分布和高亮度的荧光体 ,且有良好的颗粒形貌。     

Spin-Polarized Tunnelling Magnetoresistance Effects in La0.833K0.167MnO3／SrTiO3 Polycrystalline Perovskite Manganites

A sample of La0.833K0.167MnO3-SrTiO3 (LKMO/STO) is fabricated by the sol-gel method. The microstructure,magnetic and transportation properties have been studied. X-ray diffraction patterns indicate that the structure of LKMO/STO is a homogeneous solid solution phase. The resistivity of LKMO/STO shows the insulator behaviour, which is different from La0.833K0.167MnO3 (LKMO) whose resistivity shows metal-insulator transition with decreasing temperature. The low-field (moH = 0.02 T) magnetoresistance decreases from 11% to 0.2% with the increasing temperature from 4 K‘to 220K for the LKMO/STO sample. The magnitude of magnetoresistance in a strong field (μoH = 5.5 T) almost increases linearly with decreasing temperature and reaches the maximum of 65% at the low temperature of 4.2K, which is much higher than that oE LKMO (40%). The enhanced low-field magnetoresistance effects are quantitatively explained by the spin-polarized tunnelling at grain boundaries.     

Fe2O3纳米微粒溶胶非线性光学特性的Z-扫描研究

利用Z扫描技术在透明区域研究了Fe₂O₃纳米微粒水溶胶和表面包覆有机溶胶的非线性光学特性，给出了非线性折射率γ、双光子吸收系数β、自由载流子折射系数σ_r和自由载流子吸收截面σ_ab等重要物理参数，讨论了自由载流子效应对Fe₂O₃纳米微粒非线性特性的影响 关键词：     

p型导电掺In的SnO_2薄膜的制备及表征

采用溶胶 凝胶提拉法成功地制备了p型导电掺In的SnO2 薄膜 .x射线衍射测试结果表明 ,掺In的SnO2 薄膜保持SnO2 的金红石结构 .吸收谱测试结果表明 ,掺In的SnO2 禁带宽度为 3 8eV .霍尔测量结果表明 ,空穴浓度与热处理温度有很大的关系 ,5 2 5℃为最佳热处理的温度 .铟锡原子比在 0 0 5— 0 2 0范围内 ,空穴的浓度与In的含量有直接的关系 ,并随In含量的增加而增加     

Gd2O3:Eu纳米晶的制备及其光谱性质研究

以EDTA为络合剂，聚乙二醇为有机分散剂，用络合溶胶—凝胶法制备出Gd2O3:Eu纳米晶。用XRD，SEM，X—射线能量色散谱仪(EDS)，荧光分光光度计等分析手段对Gd2O3:Eu的纳米晶结构、形貌、组分的均匀性以及发光特性进行了研究。结果表明：EDTA—M凝胶仅在800℃焙烧即可得到颗粒细小、组分均匀、纯立方相的Gd2O3:Eu纳米晶，颗粒基本呈球形，粒径为30nm左右。对样品的激发光谱、发射光谱测定表明：Gd2O3:Eu纳米晶在269nm光激发下发红光，发射光谱谱峰在611nm，与体材料基本相同；激发光谱中电荷迁移带(CTB)明显红移，从体材料的255nm移至269nm，移动了约14nm；猝灭浓度从体材料的6％提高到8％。     

溶胶凝胶软石印法制备Zn_2SiO_4∶Mn图案化薄膜及其发光性能的研究

采用溶胶 凝胶法制备了Zn2SiO4∶Mn薄膜并结合毛细管微模板技术实现了薄膜的图案化,利用X射线衍射(XRD),原子力显微镜,光学显微镜,发光光谱等手段对Zn2SiO4∶Mn的结晶过程、发光性质进行了研究。XRD结果表明,溶胶 凝胶法合成的样品在800℃时已开始结晶,在1000℃时可得到纯相的Zn2SiO4∶Mn,这比传统的固相法的烧结温度低150℃。Zn2SiO4∶Mn薄膜的激发光谱在220nm和280nm之间有一个强的吸收峰,峰值位于248nm,发射光谱的最大值位于522nm,为绿光发射。从原子力显微镜照片可知组成薄膜的粒子比较均匀,其平均直径为220nm。我们获得了四种图案化宽度,分别是5,10,20,50μm。光学显微镜的结果表明,图案薄膜烧结后相对于烧结前有10%～20%的收缩。