HgCl2/I2复合催化剂协同催化合成异丙醇钇的研究

以金属钇和异丙醇为原料，以HgCl2/I2为复合催化剂，通过对金属钇的机械加工以增加其比表面，并将异丙醇脱水使其含水量降低至0．05％，体系在82℃回流5h，经过滤、减压蒸馏，得到了白色海绵状异丙醇钇，其产率高达83％，合成时间比文献报道的缩短了19h，产率提高了8％。文章确定了催化剂的最佳用量为20gY加入60mg HgCl2/I2，研究了合成产率与HgCl2/I2催化剂和HgCl2催化剂的依赖关系及异丙醇中含水量对合成产率的影响，并对HgCl2/I2的催化作用机理进行了初步探讨。     

Diode-Pumped Self-Q-Switched Cr,Nd：YAG Laser with High Average Output Power

A diode end-pumped self-Q-switched Cr,Nd:YAG laser was established with pulse duration in the range of 8-10ns. The maximum average output power was 4.4 W and the slope efficiency was 27% using an output coupler of R=70%. At pumping power of 17.4 W the laser produces high-quality pulses at 1064 nm in a TEMoo-mode.     

Fabrication of Zeolite A Rods with Irregular Macropores by Self-assembly of Zeolite A Microcrystals Using Microwave-assisted Hydrothermal Synthesis

Zeolite A rods by self-assembly of zeolite A microcrystal were successfully synthesized by microwave-assisted hydrotherrnal synthesis. The average size of zeolite crystals consisting of self-assembling materials was about 300 nm and the length of zeolite rods was in the range of 15--30μm.     

HoYb:YVO4的上转换发光研究

研究了960nm激光激发下HoYb双掺钒酸钇晶体HoYb:YVO4的直接上转换增敏发光,发现了Ho3+离子的上转换发光现象,HoYb:YVO4晶体的上转换发光是5F5→5I8最强,而5S2→5I8相对小了一个数量级,这是由于YVO4晶体既有很强的振子强度又有很大的多声子无辐射弛豫造成的. 关键词： 上转换发光 直接增敏(敏化) 钒酸钇YVO4晶体 Ho3+离子     

Antiphase State in Passively Q-Switched Yb：YAG Microchip Lasers with a Nd,Cr：YAG as Saturable Absorber

We experimentally investigate the antiphase dynamics phenomenon that occurs in a diode-pumped passively Q-switched Yb:YAG multimode laser with a Nd,Cr:YAG saturable absorber. Due to the effect of spatial hole burning, the multimode lasers with one, two, or three modes at different pump power are observed, and the pulses sequences display classic antiphase dynamics.     

离子束合成钇硅化物的结构及红外谱特征

将稀土金属钇离子注入到n型单晶Si(111)中制备出钇硅化物埋层.利用x射线衍射、卢瑟福背散射和傅里叶红外吸收谱测量分析了样品的结构、原子的埋层分布和振动模式.结果表明，Y离子在注入过程中已与基底中的Si原子形成了YSi2结构相.真空下的红外光辐照处理促使YSi2择优取向生长，埋层中Si与Y的平均原子浓度比由24下降为20，与六方YSi2的化学计量比一致.还给出了钇硅化物的特征红外吸收谱.     

超稳Y沸石制备技术对沸石铝分布的影响 Ⅱ.均匀铝分布的超稳Y沸石的制备

对水热处理后得到的USY沸石作进一步的酸处理以及采用改进的氟硅酸盐溶液骨架富硅工艺,分别得到了经XPS剖面分析证实为铝分布均匀的超稳Y沸石HAY-Ⅰ和HAY-Ⅱ。IR分析表明,在酸处理过程中从USY沸石中去掉的那部分非骨架铝类与3690cm~(-1)处羟基有关,仍残留在HAY-Ⅰ沸石中的那部分非骨架铝类与3670cm~(-1)和3600cm~(-1)处羟基有关。XRD和化学分析表明HAY-Ⅰ沸石仍含有约50％的非骨架铝类,而HAY-Ⅱ沸石则基本上不含非骨架铝类,HAY-Ⅱ沸石还显示更高的结晶保留度。DTA分析表明,HAY-Ⅰ和HAY-Ⅱ两种沸石的热稳定性均高于USY沸石。