Dextran-modified iron oxide nanoparticles

Dextran-modified iron oxide nanoparticles were prepared by precipitation of Fe（Ⅱ） and Fe（Ⅲ） salts with ammonium hydroxide by two methods. Iron oxide was precipitated either in the presence of dextran solution, or the dextran solution was added after precipitation. In the second method, the iron oxide particle size and size distribution could be controlled depending on the concentration of dextran in the solution. The nanoparticles were characterized by size-exclusion chromatography, transmission electron microscopy and dynamic light scattering. Optimal conditions for preparation of stable iron oxide colloid particles were determined, The dextran/iron oxide ratio 0-0,16 used in precipitation of iron salts can be recommended for synthesis of nanoparticles suitable for biomedical applications, as the colloid does not contain excess dextran and does not coagulate.     

WS2 超细粉体的固相法合成

WS2 超细粉体的固相法合成;WS2;固相反应;过硫系数;高能球磨;粒度     

碳酸氢铵沉淀法制备氧化钇粉体时反应条件对产物粒度的影响

研究了碳酸氢铵沉淀法的反应条件对氧化钇粒度的影响,探讨了粒度变化规律。发现在沉淀反应中,晶型碳酸钇铵的形成与否是影响氧化钇粒度的关键因素。在较低的反应温度下,当碳酸氢铵和氯化钇的浓度大于0.25mol·L-1,摩尔比大于5,陈化时间大于60min时得到碳酸钇铵沉淀,经煅烧可获得粒度(D50)大于1μm的氧化钇。当反应物浓度较低、摩尔比小,陈化时间较短时得到无定型碳酸钇沉淀,煅烧沉淀可获得粒度(D50)小于0.5μm的氧化钇。实验证明选择适当的沉淀反应条件,可制备D50在0.3～10μm范围内的不同粒度级别的氧化钇粉体。     

Preparation of Small Particle Sized ZnAl-Hydrotalcite-Like Compounds by Ultrasonic Crystallization

Ultrasonic technology has been intensively studied recently due to its special features. In this paper, an ultrasonic crystallization method was introduced for the preparation of ZnAl-Hydrotalcite-Like compounds (ZnAl-HTLcs). Samples with high crystallinity, small particle size and narrow particle size distribution were obtained and fully characterized using conventional techniques of XRD, FT-IR and TGDTA. The results prove that both ultrasonic frequency and ultrasonic power have effects on the sizes of the product particles. By varying the ultrasonic power from 250 W to 88 W, with the ultrasonic frequency fixed at 59 kHz, the median particle size of the samples increased from 0.37 μm to 0.82 μm. By altering the hydrothermal treatment time from 1 h to 5 h at 110℃, the median particle size of ZnAl-HTLcs synthesized via ultrasonic crystallization increased from 0.88 μm to 1.11 μm.     

烟叶样品在进行近红外分析测试前的样品处理方法

本发明涉及烟叶样品在进行近红外分析测试前的样品处理方法，属烟草样品的近红外光谱分析测试技术领域。本发明的烟叶样品在进行近红外分析测试前的样品处理方法包括干燥粉碎及压样三步骤，其中：a．粉碎步骤为：将干燥的样品取出并静止10S后放入家用食物搅拌器中进行粉碎处理，粉碎时间为20-30S，粉碎粒度达375μm以下；b．压样步骤为：将质量为300g的重锤自然平稳置入装有粉碎后样品的样品杯中，取出重锤，随后将样品杯放入仪器样品池内进行测量10min就能完成一个烟叶样品的测试工作。本发明具有操作简单、节省时间、成本低、效率高等优点。     

用于筛膜反应器的γ-MnO2纳米粉的合成

醋酸锰与柠檬酸发生沉淀反应生成锰配合物,经热分解和酸处理手段最终制备出γ-MnO2纳米材料,用X射线衍射、差热/热重分析、透射电镜及原子力显微镜等手段对合成的样品进行了表征.同时考察了反应条件对反应速度、最终产品粒度的影响.结果表明,通过对反应条件的控制可以在一定程度上控制产品的粒度,得到了均粒度和超细粒度的γ-MnO2纳米材料.对于异丙醇和环己烷等氧化脱氢反应,γ-MnO2纳米筛膜反应器与传统的固定床反应器相比反应物的转化率提高了20%.     

几种非金属矿物对硫化氢吸附性能的研究

某些非金属矿物具有吸附性[1 5]。本文测试了硅藻土、浮岩、沸石和麦饭石等非金属矿物的主要理化性能,研究了上述矿物在不同条件下对硫化氢的吸附性能,探讨了吸附剂粒度、用量、吸附时间和温度对吸附率的影响及吸附机理。在适当的条件下,各种材料对硫化氢的吸附率均能达到90%;吸附能力依次为硅藻土>麦饭石>沸石>浮岩。1　实验部分1 1　材料和试剂采集原矿标本硅藻土(抚松露水河)、浮岩(长白山天池)、麦饭石(长白山遥林)、斜发沸石(长春市净月潭),经粗选、粉碎、制备成不同粒径的吸附剂。X荧光光谱仪(PW140/10型,荷兰)和等离子直读光谱…     

中国内陆大气颗粒物的搬运、沉积及反映的气候变化——Ⅰ.现代大气气溶胶

分析了中国内陆3个地点尘暴和非尘暴期间大气颗粒物中17种微量元素的浓度-粒度分布。表明这些地点的大气颗粒物主要由矿物气溶胶(即粉尘)组成。对黄土高原上空非尘暴大气微量元素的统计分析,导出粗粒子主要有两种来源——土壤粉尘和被污染的粉尘,细粒子的两种来源是土壤粉尘和人为污染物。在年尺度上,粉尘对黄土高原的大气干输入主要取决于非尘暴过程。利用清除系数估算的粉尘湿沉积通量只占总沉积的4％—11％。     

油脂加氢催化剂镍晶粒度与活性的关系研究

油脂加氢催化剂镍晶粒度与活性的关系研究何新秀刘华（成都理工学院应用化学系６１００５９）许清淮（川化集团公司成都６１０３０１）关键词加氢催化剂制备工艺条件镍晶粒度预知活性油脂加氢催化剂的性能如活性、过滤性、选择性等的优劣主要由活性物质、助剂和载体等化学...     

不同溶剂体系中改性氢氧化镁的分散行为

研究了不同的表面改性剂对超细氢氧化镁的表面改性.并分别以水和乙醇为溶剂,研究了表面改性后氢氧化镁的分散行为.实验结果表明,以水为溶剂的体系,六偏磷酸钠分散性能最好,而以乙醇为溶剂,硅烷偶联剂KH-550分散性能最好,其用量为基体量的5%左右,可使制备的超细氢氧化镁粒径达到0.2 μm尺度以下.试验结果对进一步认识超细氢氧化镁的性质及其应用具有重要意义.