LaB6-ZrB2共晶复合材料的组织特征及控制

用电弧炉和电子束悬浮区熔炉法制备了ＬａＢ６ＺｒＢ２共晶复合材料，并用ＳＥＭ和ＴＥＭ方法对其显微组织进行了研究。结果表明，ＬａＢ６ＺｒＢ２形成纤维状共晶组织，控制凝固条件可得到定向排列的组织，ＬａＢ６基体上均匀分布着直径为０２～１２μｍ的ＺｒＢ２纤维，纤维长度可达１００μｍ以上。对于固液界面为平面生长的试样，其结晶学取向关系为［００１］ＬａＢ６∥［００１］ＺｒＢ２，（１１０）ＬａＢ６∥（０１０）ＺｒＢ２。     

PVP-semi-IPN-PCL/PLA水凝胶制备及负载卡马西平药物共晶体外释放

通过N-乙烯基吡咯烷酮(N-vinyl pyrrolidone, NVP)在聚己内酯(polycaprolactone, PCL)、聚乳酸(poly(lactic acid),PLA)乙酸乙酯溶液中自由基聚合,制得聚乙烯吡咯烷酮(Polyvinylpyrrolidone, PVP)/聚己内酯、聚乳酸半互穿网络(semi-interpenetrating network, semi-IPN)水凝胶(PVP-semi-IPN-PCL/PLA)。实验制得疏水/亲水比例分别为1∶9、3∶7、5∶5的三种水凝胶。采用溶剂挥发法制备卡马西平-丁二酸药物共晶(carbamazepine-succinic acid, CBZ-SUC)。使用PVP-semi-IPN-PCL/PLA负载CBZ-SUC共晶,考察上述三种凝胶药物载体的载药能力及体外释放行为。使用1∶9、3∶7、5∶5比例凝胶制备了载药量分别为17%、19%、21%,包封率分别为71%、83%、89%的载药凝胶,其在37℃,pH=6.8 PBS溶液中体外释放效果均优于未使用凝胶载体的CBZ-SUC共晶。其中,3∶7组载药凝胶的累积释放量最高,...     

高密度聚乙烯与乙烯丙烯辛烯－1共聚物共混体系的相容性

用ＤＳＣ和ＷＡＸＤ方法研究了高密度聚乙烯／聚（乙烯丙烯辛烯－１）（ＨＤＰＥ／ＥＰＯ）共混体系的结晶性能。共混物的ＤＳＣ曲线皆呈单峰，表明共混体系形成了共晶。晶胞参数ａ及结晶度随共混物组成而变，进一步证明ＨＤＰＥ／ＥＰＯ共混体系的相容性．     

共晶含能材料研究进展

共晶是不同种类的分子(两种或两种以上)通过氢键等分子间相互作用,形成具有特定结构和性能的多组分分子晶体,不同含能材料形成共晶可以有效改善炸药的感度、安全性等性能。针对目前高能炸药的改性需求,共晶在含能材料领域中的应用具有巨大的潜力。综述了共晶的形成原理及生长特性,总结了常见共晶的制备方法和表征方法,评述了含能材料共晶的研究现状和发展前景。     

CL-20/TNT共晶炸药的分子动力学研究

运用分子动力学(MD)方法,选择凝聚态分子势能优化力场(COMPASS),对六硝基六氮杂异伍兹烷(ε-CL-20)、2,4,6-三硝基甲苯(TNT)晶体及其等摩尔比的CL-20/TNT混合炸药和共晶炸药进行不同温度下恒定粒子数等压等温(NPT)系综模拟研究.结果表明,CL-20/TNT共晶的内聚能密度(CED)和结合能随温度的升高逐渐减小;共晶的CED比混合炸药的大,结合能是混合炸药的2倍多,预示其稳定性明显增强.对相关函数和局部放大结构显示共晶中组分分子间作用主要来自TNT中H和CL-20中O以及CL-20中H和TNT中O之间形成的氢键.通过波动法求得的弹性力学性能结果表明,CL-20/TNT共晶的拉伸模量(E)、体积模量(K)和剪切模量(G)介于ε-CL-20和TNT晶体之间,且随温度的升高而下降,符合一般预期;但共晶炸药的柯西压(C12-C44,Cij弹性系数)、K/G和泊松比(ν)均比其组分炸药ε-CL-20和TNT高得多,预示该共晶具有异常高的延展性和弹性伸长,主要是二组分呈层状交替排列且之间存在较强相互作用所致.     

深过冷Ag-Cu-Ge三元共晶合金的相组成与凝固特征

在Ag_38.5Cu_33.4Ge_28.1三元共晶合金的深过冷实验中，获得的最大过冷度为175 K(0.22T_E). XRD分析表明，不同过冷条件下其共晶组织均由(Ag),(Ge)和η(Cu₃Ge)三相组成. 在小过冷条件下，三个共晶相协同生长，凝固组织粗大.随着过冷度的增大，共晶组织明显细化，(Ge)相与其他两相分离，以初生相方式生长，而(Ag)相与η相始终呈二相层片共晶方式共生生长. 当过冷度超过80 K时，初生相(Ge)由小过冷时的块状转变为具有小面相特征的枝晶方式生长. 部分小面相(Ge)枝晶出现规则的花状，花瓣数介于5—8之间，并且过冷度越大(Ge)相越容易分瓣. 花状(Ge)枝晶的晶体表面为{111}晶面簇，择优生长方向为〈100〉晶向族. 关键词： 三元共晶 晶体形核 深过冷 快速凝固     

镧对Al—Si共晶合金组织及性能的影响

采用光学显微镜、扫描电镜、电子探针及X射线衍射等方法对金属型铸造和砂型铸造条件下,镧变质Al-Si共晶合金的特点和规律进行了研究。结果发现,镧对Al-Si共晶合金具有较强的变质作用;镧的加入量、熔液状态、保温时间及搅拌作用等对镧的变质效果均有影响;镧的变质具有长效性,且存在变质的“潜伏期”;镧能使合金的拉伸强度(σ_b)和延伸率(σ_s)提高,但两者不同时达到最大值。     

Ternary Eutectic Growth in a Highly Undercooled Liquid Alloy

The crystal nucleation and growth mechanism during the formation of Ag42.4 Cu21.6 Sb36 ternary eutectic are investigated under substantial undercoo]ing conditions. The x-ray diffraction analysis shows that the solidified eutectic phases are not invo]ved (Ag) within a wide undercooling range of 6-114 K. This indicates that under high undercooling condition, the phase constitution of Ag-Cu-Sb eutectic is different from that in the equilibrium phase diagram. With the increase of undercoo]ing, the crystalline morpho]ogy of Ag42.4 Cu21.6 Sb36 alloy transforms from the mixed structure of primary θ(Cu2Sb), two pseudobinary eutectics and (ε θ Sb) ternary eutectic into a unique (ε θ Sb) ternary eutectic. The calculated results indicate that θ(Cu2Sb) is the leading nucleating phase among the three eutectic phases. In addition, the growth morpho]ogy of primary ε(Ag3Sb) compound in Ag60Cu6Sb34 alloy exhibits the characteristics of solid solution and its orthorhombic dendrite grows along the (111) directions.     

Rapid Hypoeutectic Growth Within a Highly Undercooled Liquid Under containerless Condition

Rapid hypoeutectic growth from a highly undercooled liquid was accomplished by containerless processing Ni-32% Sb hypoeutectic alloy in a 3m drop tube.The containerless state during the free fall of the droplet produces substantial undercooling up to 350K(0.24TL).The growth mechanism is found to transform from primary α Ni dendrite plus lamellar eutectic to lamellar eutectic and finally to anomalous eutectic if droplet undercooling exceeds the two thresholds of 112K and 242K,respectively.Based on the current eutectic and dendritic growth models,the eutectic coupled zone is calculated and used to explain the growth mechanism transition.Calculations also indicate that the growth of α-Ni primary dendrite was mainly controlled by solute diffusion.     

喷射沉积过共晶Al—Si合金的微观组织和抗磨性能

采用扫描电子显微镜和Falex-6型摩擦磨损试验机研究了普通铸造和喷射沉积过共晶Al—Si合金的微观组织和摩擦学性能．显微组织观察和摩擦磨损试验结果表明，喷射沉积能够显著改变过共晶Al—Si合金中初晶Si相的形态和尺寸，细化合金的基体组织；与普通铸造合金相比，沉积态合金具有更好的耐磨性能．