化整为零:聚合物/粘土纳米复合材料的微观结构和阻隔性能

在聚合物基体中掺入少量的层状硅酸盐所制备的聚合物／粘土纳米复合材料，其阻隔性能明显地优于纯聚合物及其传统的复合材料。实验及分析结果表明，聚合物／粘土纳米复合材料的微观结构和阻隔性能主要受控于粘土剥离后的径厚比．一简单的重整化群模型被用来评估粘土几何因素（诸如径厚比、取向、剥离程度等）对聚合物／粘土纳米复合材料阻隔性能的影响，所得到的逾渗阈值及最佳粘土含量与实验结果吻合。     

掺钕聚甲基丙烯酸甲酯的光学特性

研究了制备的掺钕螯合物Nd(DBM)3Phen材料的吸收光谱、激发光谱、荧光光谱,应用Judd-Ofelt理论计算了该材料的强度参量．分析了钕离子激发态4F3／2的辐射寿命(631 μs)和4F3／2→4IJ′跃迁的受激发射截面和荧光分支比．     

镅污染手套箱系统的去污技术

考虑到手套箱系统的主要污染核素为^239Pu，^241Am，^3H和U，其中^239Pu，^241Am属α长寿命极毒核素，很容易产生放射性气溶胶。在手套箱系统退役过程中，手套箱系统的拆除解体前后均应采用行之有效的方法进行去污，最大限度的减少放射性物质对环境的污染。文中根据可剥离膜去污技术、电解去污技术、导电高分子聚合物导电机理以及超声波去污技术，针对镅污染手套箱拆下部件的污染情况和材质特点，采取单独使用和组合使用的方法进行相应的去污技术研究。     

Fabrication of Dendrimer－like PAMAM Based on Silica Nanoparticles

A G 4.0 dendrimer-like poly (amido amine) (PAMAM) based on silica nanoparticles was fabricated via a divergent approach.It was built from γ-aminopropyi silica nanoparfides (APSN) core via repetitive addition of acrylate (MA) and hexylenediamine (HDA). FT-IR and EA were used to monitor the progress of dendrimer during each step. The amino group content of the resulting product increased from 0.49 to 3.72 mmol/g after the 4th generation. In addition, the percentage of grafting increased with increasing generation and reached to 65.9% after 4th generation. It was found that the resulting silica nanoparticles could be dispersed in methanol with a mean hydrodynamic particle diameter of 152.7 nm although the silica nanoparticles had agglomerated during the storage period.     

强场物理与快点火靶的制备

采用本体聚合技术合成全氘代聚苯乙烯（DPS），所得聚合物分子量约250000，分散度约3，氘代率为98．7％。采用热诱导相分离技术制备全氘代聚苯乙烯泡沫。在室温溶解DPS于溶剂中，然后转入轴向冷却模具，进行单向冷却，直到溶剂完全冷冻，最后取出冷冻样置于冷冻干燥仪中进行冷冻干燥，待溶剂完全脱出后即得泡沫。通过对二恶烷／环己烷混合溶剂相图，以及PS一混合溶剂体系的相图的测定，     

Preparation and Selectivity of Molecularly Imprinted Polymer Coating on the Micro Pore Membrane of Polytetrafluoroethylene

In order to obtain mechanically stable membrane for practical application, the imprinted polymer was synthesized in the pores of polyfluoromembrane, the binding and transport ability of the membrane were studied.     

Electron Holography of Barrier Structures in Co／ZrAlOx／Co Magnetic Tunnel Junctions

We investigate the potential profiles and elemental distribution of barriers in Co/ZrAlOx/Co magnetic tunnel junctions (MTJs) using electron holography (EH) and scanning transmission electron microscopy. The MTJ barriers are introduced by oxidizing a bilayer consisting with a uniform 0.45-nm Al layer and a wedge-shaped Zr layer (0-2 nm). From the scanning transmission electron microscopy, AlOx and ZrOx layers are mixed together, indicating that compact AlOx layer cannot be formed in such a bilayer structure of barriers. The Eli results reveal that there are no sharp interfaces between the barrier and magnetic electrodes, which may be responsible for a smaller tunnelling magnetoresistance compared with the MTJs of Co/AlOx/Co.     

(Nd_(1-x)Er_x)_2Co_(15.5)V_(1.5)的结构转变与磁性

利用电弧熔炼制备了 (Nd1 xErx) 2 Co1 5 5V1 5(x=0— 1 0 )化合物样品 .通过x射线衍射分析和磁性测量研究了Er替代Nd2 Co1 5 5V1 5中的Nd时对化合物结构和磁性的影响 .研究结果表明 ,低Er含量 (x <0 4 ) ,化合物为Th2 Zn1 7型结构 ;高Er含量时 (x >0 5 ) ,化合物转变为Th2 Ni1 7结构 ;Er含量为x =0 4和 0 5时 ,两种结构共存 .两种结构的晶胞参数a ,c和晶胞体积V随着Er含量的增加都呈现递减的趋势 .随着Er含量的增加 ,(Nd1 xErx) 2 Co1 5 5V1 5化合物的居里温度和饱和磁化强度都单调下降 .(Nd1 xErx) 2 Co1 5 5V1 5化合物的室温各向异性由低Er含量时的易锥型转变为高Er含量时的易轴型 .x =0— 0 5的化合物在温度升高时发生自旋重取向转变 ,自旋重取向温度Tsr随Er含量的增加而减小