Growth studies of m-GaN layers on LiAlO2 by MOCVD

This paper reports that the m-plane GaN layer is grown on （200）-plane LiAlO2 substrate by metal-organic chemical wpour deposition （MOCVD） method. Tetragonal-shaped crystallites appear at the smooth surface. Raman measurement illuminates the compressive stress in the layer which is released with increasing the layer＇s thickness. The high transmittance （80%）, sharp band edge and excitonic absorption peak show that the GaN layer has good optical quality. The donor acceptor pair emission peak located at -3.41 eV with full-width at half maximum of 120 meV and no yellow peaks in the photoluminescence spectra partially show that no Li incorporated into GaN layer from the LiAlO2 substrate.     

Nano-tribological study on a super-hydrophobic film formed on rough aluminium substrates

A novel super-hydrophobic stearic acid (STA) film with a water contact angle of 166^o was prepared by chemical adsorption on aluminum wafer coated with polyethyleneimine (PEI) film. The micro-tribological behavior of the super-hydrophobic STA monolayer was compared with that of the polished and PEI-coated Al surfaces. The effect of relative humidity on the adhesion and friction was investigated as well. It was found that the STA monolayer showed decreased friction, while the adhesive force was greatly decreased by increasing the surface roughness of the Al wafer to reduce the contact area between the atomic force microscope (AFM) tip and the sample surface to be tested. Thus the friction and adhesion of the Al wafer was effectively decreased by generating the STA monolayer, which indicated that it could be feasible and rational to prepare a surface with good adhesion resistance and lubricity by properly controlling the surface morphology and the chemical composition. Both the adhesion and friction decreased as the relative humidity was lowered from 65% to 10%, though the decrease extent became insignificant for the STA monolayer. The project supported by the National Natural Science Foundation of China (50375151, 50323007, 10225209) and the Chinese Academy of Sciences (KJCX-SW-L2)     

Effects of Substrate Temperature on Helium Content and Microstructure of Nanocrystalline Titanium Films

Helium-charged nanocrystalline titanium films have been deposited by HeAr magnetron co-sputtering. The effects of substrate temperature on the helium content and microstructure of the nanocrystalline titanium films have been studied. The results indicate that helium atoms with a high concentration are evenly incorporated in the deposited titanium films. When the substrate temperature increases from 60℃ to 350℃ while the other deposition＇parameters are fixed, the helium content decreases gradually from 38.6 at.% to 9.2at.%, which proves that nanocrystalline Ti films have a great helium storage capacity. The 20 angle of the Bragg peak of （002） crystal planes of the He-charged Ti film shifts to a lower angle and that of （100） crystal plane is unchanged as compared with that of the pure Ti film, which indicates that the lattice parameter c increases and a keeps at the primitive value. The grain refining and helium damage result in the diffraction peak broadening.     

Pt-SDB疏水催化剂的研制

基于液相水-氢同位素催化交换的疏水催化剂研究已有近30年历史。从所报道的资料来看，目前用于重水提氚工艺中相转移的疏水催化剂主要集中在Pt-C-PTFE和Pt-SDB两类材料上。前者疏水性好，耐辐照稳定性好，后者催化活性好，但催化剂耐辐照稳定性稍差。拟在特制的SDB疏水材料上制备出催化活性好，性能稳定，满足使用要求的Pt-SDB疏水催化剂。     

疏水吸附法分离纯化α—淀粉酶

本文报道了一种从发酵液中分离纯化α—淀粉酶的新方法。α—淀粉酶发酵液用两种高分子量的絮凝剂澄清,滤液用一种国产吸附树脂吸附,然后用40％乙醇洗脱,所得酶粉的活性约为60000U/g。产率64.22％。     

利用电泳技术在不锈钢和铁基底上制备MgB2带材

本文首次报道了利用电泳技术在铁和不锈钢基底上制备MgB2超导带材.电阻测量表明,沉积在铁和不锈钢基底上MgB2带材的超导零电阻转变温度分别为37.5K和31K,超导转变宽度分别为0.3K和1K.磁测量表明,(5K,OT)时不锈钢基底上带材的临界电流密度为6×105(A/cm2).X射线衍射谱和扫描电子显微镜图象表明样品结晶良好,晶粒生长致密.本工艺制备MgB2带材时不受系统真空度的限制,生长迅速,成本低廉,并且可以根据不同的需要任意选择基底的形状和大小.     

聚电解质与相反电荷表面活性剂的相互作用

通过透光度测定、电导滴定和粘度法考察了阳离子聚电解质聚苯乙烯 4 乙烯基吡啶硫酸甲酯盐与阴离子表面活性剂十二烷基硫酸钠 (SDS)的相互作用。研究表明 ,在表面活性剂未过量时 ,二者之间的静电作用占主导地位 ,并且当二者电荷总量相等时 ,生成的复合物沉淀最多 ;在表面活性剂过量后 ,复合物可部分溶解 ,溶解的原因是疏水相互作用。本文初步阐述了二者的作用机理     

中性盐对谷氨酸脱羧酶活性的影响机制

通过不同阳离子和不同阴离子对唾液链球菌嗜热亚种(Streptococcus salivariussub sp.thermophilus)谷氨酸脱羧酶活性的影响以及NaNO3对不同蛋白质浓度的谷氨酸脱羧酶活性的影响进行考察,结果表明:中性盐对谷氨酸脱羧酶活性的影响不是由于增加蛋白质亚基间的疏水作用引起的,而可能是由中性盐对谷氨酸脱羧酶活性的弱抑制作用与中性盐增加了谷氨酸脱羧酶的胶体体系稳定性共同作用所致,同时还可能与中性盐降低了反应体系CO2的溶解度有关.     

用高效疏水色谱法对多种脲变α-淀粉酶折叠中间体的研究

用高效疏水色谱法对用脲变性的α-淀粉酶的体外折叠中间体进行了分离，发现脲变α-淀粉酶折叠至少有19个中间体，而且，这些中间体在色谱流出液中可稳定一周．这一结论已由电泳、离子交换色谱和体积排阻色谱法证实．此外，还用紫外吸收光谱和荧光发射光谱研究了这些折叠中间体与天然α-淀粉酶构象之间的差异．