Electron Holography of Barrier Structures in Co／ZrAlOx／Co Magnetic Tunnel Junctions

We investigate the potential profiles and elemental distribution of barriers in Co/ZrAlOx/Co magnetic tunnel junctions (MTJs) using electron holography (EH) and scanning transmission electron microscopy. The MTJ barriers are introduced by oxidizing a bilayer consisting with a uniform 0.45-nm Al layer and a wedge-shaped Zr layer (0-2 nm). From the scanning transmission electron microscopy, AlOx and ZrOx layers are mixed together, indicating that compact AlOx layer cannot be formed in such a bilayer structure of barriers. The Eli results reveal that there are no sharp interfaces between the barrier and magnetic electrodes, which may be responsible for a smaller tunnelling magnetoresistance compared with the MTJs of Co/AlOx/Co.     

非晶Zr—Co的超导转变

测量了非晶态过渡族 Zr_(100-x)Co_x(x=20—41)合金的超导转变温度 T_c、上临界场 B_(c2)(T)和临界电流密度 J_c(H,T).T_c 随着 Co 含量 x 增加而线性地降低.上临界场 B_(c2)(T)的测量数值符合标准的 WHH 理论.电子状态密度和电子比热系数都随着 Co 含量 x 增加而降低.临界电流密度 J_c(H,T)和磁通钉扎力 F_p,相当弱,可以归因于在相干长度尺度上的结构均匀性.     

^95Zr核的高自旋态研究

利用102MeV的^28Si束流，通过^60Ni(^28Si，2pn)熔合蒸发反应布居了^85Zr核的高自旋态，测量了γ-γ符合及DCO比值，建立了一个有43条能级，75条γ跃迁的能级纲图，新增加了36条γ跃迁，25条能级。将能级自旋推高到（49/2^ ），首次观察到了转边带的第二回弯。并确认了一条建立在17/2^-负字称带上的磁转动带。     

溶液中微水的一种检验方法

一般说 ,水分分析 ,特别是微量和痕量水的分析是一项比较困难的课题。水分的定性检出法有钴盐法、铁盐法、四乙酸铅法、碳化钙法和乙醇铝法。比浊法用乙醇铝测有机溶剂水分已非常灵敏 ,但制备乙醇铝步骤多 ,且乙醇铝还需配制溶液。本文介绍制备一种试剂 ,应用于比浊法测试微水。本法制作简单 ,使用方便 ,测试灵敏。1　制备方法采用氨法制备锆醇盐 :ＺｒＣｌ4 +4ＲＯＨ +4ＮＨ3 Ｚｒ(ＲＯ) 4+4ＮＨ4 Ｃｌ↓将氯化锆放到容器中 ,注入异丙醇 ,密封容器。加热并通入氨气 ,搅拌混合 ,反应结束后 ,过滤除去沉淀物氯化铵 ,得到锆醇盐溶液 (由于锆醇…     

纯锆上离子注入钇和镧后的表面分析

用金属蒸汽真空弧源，以40kV加速电压对纯锆样品分别进行了10¹⁶—10¹⁷/cm²的钇、镧离子注入，注入温度约为130℃.然后对注入样品进行表面分析.x射线光电子能谱分析表明，注入的钇以Y₂O₃形式存在，镧以La₂O₃形式存在.俄歇电子能谱表明，纯锆基体表面的氧化膜厚度随着离子注入剂量的增加而增加，当离子注入剂量达到10¹⁷/cm²时，氧化膜的厚度达到了最大值.卢瑟福背散射显示镧层的厚度约为30nm，同时直接观察到当离子注入剂量为(La+Y)10¹⁷/cm²时，纯锆样品表面发生了严重的溅射. 关键词： 纯锆 钇和镧离子共注入 卢瑟福背散射 x射线光电子能谱