Studies on Structure and Porperties of Water Soluble Polysaccharide from Fruiting Body of Cordyceps Militarvs(L.) Link

A water soluble crude polysaccharide has been isolated from the fruiting body of cultivated Cordyceps militarvs(L.)Link.The GC analysis indicated that it contained the monosaccharides of Gal,Man,Glc and GlcA.Their molar ratio is 1.00:1.58:7.89:0.19.The crude polysaccharide was fractionated with ethanol to get three fractions,which were CM-Ⅰand CM-Ⅲ,CM-Ⅱ was further purified to get one homogeneous fraction named CMB.The molecular weight was estimated to be 6000by means of gel filtration.CMB is a greyish white powder.The GC analysis indicated that it was composed of Gal.Man,Glc and the molar ratio is 1.00:1.38:5.10.Partial hydrolysis with an acid.periodate oxidation.Smith degradation.IR,GC and methylation analyses,GC/MS analyses were used for the structure analyses of CMB.Man,(1→6)-linked-Glc,(1→4)-linked-Glc and (1→4)-linked-Gal.Some of (1→4) -linked-Glc and all(1→4)-linked-Gal residues are substituted at 3-O and 6-O respectively,(1→4)-linked-Glc and minor(1→6)-linked-Gle.The nonreduced end is composed of Gal and Glc.The main glycosidic link of CMB is α configuration.     

Effects of Processing Parameters on Microstructure and Properties of Nanoscale ZrC/ZrB2 Multilayered Coatings

ZrC/ZrB2 multilayered coatings with bilayer periods of 3.5-40nm are synthesized by rf magnetron sputtering. Analyses of x-ray diffraction, scanning electron microscopy and nanoindentation indicate that multilayered coatings possess much higher hardness and greater fracture resistance than monolithic ZrC and ZrB2 coatings. A maximum hardness （41.TCPa） and a critical fracture load （73.7mN） are observed in the multilayer with A = 32 nm deposited at the substrate bias -40 V. Higher residual stress built in the ZrC layer can be released by periodic insertion of ZrB2 into the ZrC layer. A clear multilayered structure with mixed ZrB2（001）, ZrB2 （002） and ZrC （111） orientations should be responsible for the enhanced mechanical properties.     

电感耦合等离子体发射光谱法同时测定涂料中的Pb、Cd、Cr和Hg

研究了电感耦合等离子体发射光谱法测定涂料中的重金属Pb，Cd，Cr和Hg，确定了测定涂料中的重金属Pb，Cd，Cr和Hg的最佳条件。加标回收试验和实际样品测定结果表明，方法的回收率和精密度分别在99.5％-110．0％和0．95％-1．98％范围，该方法快速、准确、可靠，各元素的检出限能满足涂料安全标准，适用于涂料的日常检验。     

水溶性席夫碱型锰配合物的合成、表征及其模拟超氧化物歧化酶活性研究

以水杨醛为母体, 与胺类化合物缩合形成席夫碱配体, 用分子自组装法合成了一系列水溶性席夫碱型金属锰单核、双核配合物. 通过元素分析、红外光谱对配合物进行了表征, 采用邻苯三酚自氧化法测定了配合物的超氧化物歧化酶(SOD)活性. 结果表明, 这些水溶性锰配合物具有良好的SOD活性.     

三七水溶性化学成分及其药理研究新进展

综述了近年来三七水溶性化学成分及其药理作用特别是对神经生理活性研究的进展，对三七与人参展其它植物植物进行了比较，阐明了三七所含多肽哆肽成分研究的意义及可行性。     

水性涂料用聚丙烯酸酯微乳液的合成及其表征

低污染、低能耗的乳液涂料在建筑涂料中得到了广泛应用,具有核壳结构的聚合物乳液对胶膜的力学性能有较大的改善[1],微米(或纳米)级乳液具有优异的成膜性能,两者均是近年来高分子材料科学中发展十分迅速的新领域[2]。但微乳液聚合时乳化剂用量大,单体含量少。本文采用阴非离子复合乳化剂体系,单体预乳化工艺,种子乳液聚合法,通过正交实验优化聚合工艺参数及体系配方,合成了纳米级聚丙烯酸酯微乳液。并对乳液聚合物的粒径及分布、热性能、分子量及分布、结构等进行了表征。1　实验部分1 1　主要原料及乳液表征苯乙烯(St)、甲基丙烯酸甲…     

水溶性聚酯的结构和性能

由对苯二甲酸二甲酯、间苯二甲酸、间苯二甲酸二甲酯５－磺酸钠与乙二醇等共缩聚合成的ＰＥＴ型水溶性聚酯（ＷＳＰ）是一种新型的水溶性聚合物，在化纤、纺织、涂料、粘合剂、电子、油墨等领域有着广泛的应用前景．化纤领域超细纤维新材料的研究、开发和生产，迫切需要一...     

PrCl3催化漆酚干燥成膜的研究

Pr原子特殊的电子层结构使其具有多方面的催化特性．实验发现质量分数为0．7％的PrCl3就可使漆酚(U)于110℃固化成膜的时间从5h降低到1h．用可见分光光度法、电子能谱、紫外和红外光谱等方法研究U在PrCl3作用下的固化成膜历程．结果表明，在Pr(Ⅲ)催化U聚合的过程中首先是U与PrCl3发生配位作用，生成U镨配合物(UPr)，然后该配合物分子中的Pr(Ⅲ)催化U聚合成体形结构的高分子化合物．     

有机硅耐磨透明涂层的固化分析

ＦＴＩＲ、ＴＧ、ＴＢＡ等对有机硅耐磨涂料（有机硅溶胶）的热固化过程研究表明有机硅胶体中缔合羟基间的脱水缩合速率很高；羟基脱水程度与固化温度有关，温度越高，达平衡时羟基的浓度越低，在１０５～１３０℃间羟基的浓度变化最大，加入适当的固化剂，对羟基的脱水交联有促进作用，在较高的固化温度下，反应体系中出现了环氧环异构化产生的酮羰基的吸收峰     

乳液聚合法制备水分散有机硅聚合物

乳液聚合法是制备水性有机硅聚合物的最有效、最常用的方法。本文从乳液聚合所采用的有机硅单体或预聚物、乳液聚合工艺、乳液体系的稳定性等方面，论述了采用乳液聚合法合成水性有机硅聚合物领域所面临的问题及所取得的研究进展。